JPH0678476B2 - Polybutylene terephthalate resin composition - Google Patents
Polybutylene terephthalate resin compositionInfo
- Publication number
- JPH0678476B2 JPH0678476B2 JP1335411A JP33541189A JPH0678476B2 JP H0678476 B2 JPH0678476 B2 JP H0678476B2 JP 1335411 A JP1335411 A JP 1335411A JP 33541189 A JP33541189 A JP 33541189A JP H0678476 B2 JPH0678476 B2 JP H0678476B2
- Authority
- JP
- Japan
- Prior art keywords
- flame retardant
- polybutylene terephthalate
- resin composition
- terephthalate resin
- antimony trioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は、エンジニアリングプラスチックとして多用さ
れているポリブチレンテレフタレート樹脂組成物に関す
るものである。The present invention relates to a polybutylene terephthalate resin composition which is widely used as an engineering plastic.
ポリブチレンテレフタレート樹脂は、機械的性質や電気
的性質、成形性等が優れているために、機械部品や電気
部品、自動車部品等に広く使用されている。 そしてこのポリブチレンテレフタレート樹脂を難燃化す
るために、従来から塩素系脂環族化合物などの有機ハロ
ゲン化合物と三酸化アンチモンとを配合することがおこ
なわれている。Since polybutylene terephthalate resin has excellent mechanical properties, electrical properties, moldability, etc., it is widely used for mechanical parts, electric parts, automobile parts and the like. In order to make the polybutylene terephthalate resin flame-retardant, it has been conventionally practiced to blend an organic halogen compound such as a chlorine-based alicyclic compound with antimony trioxide.
しかし有機ハロゲン化合物や三酸化アンチモンは多量に
配合しないと難燃効果を十分に得ることができないもの
であり、これらの難燃剤で成形金型が腐食されて金型寿
命が短くなるという問題があると共に、また電気部品の
成形に用いる場合には銀接点に変色をおこして接点不良
が発生するおそれがあるという問題があった。 本発明は上記の点に鑑みて為されたものであり、金型を
腐食するおそれがなく、また銀接点を変色させるおそれ
もないポリブチレンテレフタレート樹脂組成物を提供す
ることを目的とするものである。However, unless a large amount of organic halogen compound or antimony trioxide is added, the flame retardant effect cannot be sufficiently obtained, and there is a problem that the molding die is corroded by these flame retardants and the die life is shortened. In addition, there is a problem that when it is used for molding an electric part, the silver contact may be discolored to cause contact failure. The present invention has been made in view of the above points, and an object thereof is to provide a polybutylene terephthalate resin composition that does not have a risk of corroding a mold and a risk of discoloring a silver contact. is there.
【課題を解決するための手段】 本発明に係るポリブチレンテレフタレート樹脂組成物
は、ポリブチレンテレフタレートに、ブロム系難燃剤
と、三酸化アンチモンと、メチロールメラミン樹脂とを
配合して成ることを特徴とするものである。 以下、本発明を詳細に説明する。 本発明においてブロム系難燃剤としては、ブロム系脂環
族化合物や、その他臭素化スチレン、臭素化ポリカーボ
ネートなどを用いることができ、ブロム系脂環族化合物
としては例えばテトラブロムビスフェノールＡ型エポキ
シ樹脂オリゴマーを用いることができる。 そして、ポリブチレンテレフタレート（PBT）に主たる
難燃成分としてブロム系難燃剤及び三酸化アンチモン
を、難燃助剤としてメチロールメラミン樹脂をそれぞれ
配合することによって、本発明に係る難燃化したポリブ
チレンテレフタレート樹脂組成物を得ることができるも
のである。ブロム系難燃剤と三酸化アンチモンの配合量
は、両者の原子の構成比においてBr/Sb＝0.5〜３（重量
比）となるように配合比率を調整し、且つ組成物全量に
対してブロム系難燃剤と三酸化アンチモンとの合計量が
５〜20重量％となるように設定するのが好ましい。また
メチロールメラミン樹脂の配合量は組成物全量に対して
５〜15重量％になるように設定するのが好ましく、ブロ
ム系難燃剤と三酸化アンチモンの配合の合計量をＡ、メ
チロールメラミン樹脂の配合量をＢとするとA/B＝0.5〜
３の重量比になるようにメチロールメラミン樹脂の配合
量を設定するのが好ましい。 上記のように難燃助剤として配合するメチロールメラミ
ン樹脂によって、主たる難燃剤として配合するブロム系
難燃剤や三酸化アンチモンの配合量を低減することがで
きるものであり、難燃剤の影響による金型の腐食を防止
することができると共に銀接点に変色が発生することを
防止することができ、また難燃剤による毒性を低くする
ことができるものである。さらには難燃剤の低減によっ
てコストダウンを図ることができるものである。特に、
ブロム系脂環族化合物は従来から用いられている塩素系
脂環族化合物に比較して配合量を少なくして高い難燃効
果を得ることができるものであり、ブロム系難燃剤とし
て用いて好ましい。A polybutylene terephthalate resin composition according to the present invention is characterized by comprising polybutylene terephthalate blended with a brominated flame retardant, antimony trioxide, and a methylol melamine resin. To do. Hereinafter, the present invention will be described in detail. In the present invention, as the bromine-based flame retardant, a bromine-based alicyclic compound or other brominated styrene or brominated polycarbonate can be used. Examples of the bromine-based alicyclic compound include tetrabromobisphenol A type epoxy resin oligomer. Can be used. And, by blending a bromine-based flame retardant and antimony trioxide as a main flame retardant component in polybutylene terephthalate (PBT) and a methylol melamine resin as a flame retardant aid, the flame retarded polybutylene terephthalate according to the present invention is added. A resin composition can be obtained. The blending amount of the brominated flame retardant and antimony trioxide is adjusted so that the composition ratio of both atoms is Br / Sb = 0.5 to 3 (weight ratio), and the brominated amount is based on the total amount of the composition. It is preferable to set the total amount of the flame retardant and antimony trioxide to be 5 to 20% by weight. The amount of the methylol melamine resin is preferably set to be 5 to 15% by weight based on the total amount of the composition, and the total amount of the brominated flame retardant and antimony trioxide is A, and the methylol melamine resin is added. If the quantity is B, A / B = 0.5〜
It is preferable to set the compounding amount of the methylolmelamine resin so that the weight ratio is 3. By the methylol melamine resin to be blended as a flame retardant aid as described above, it is possible to reduce the blending amount of the brominated flame retardant or antimony trioxide to be blended as the main flame retardant, and the mold due to the influence of the flame retardant. It is possible to prevent the corrosion of the silver contact, prevent the discoloration of the silver contact from occurring, and reduce the toxicity of the flame retardant. Furthermore, the cost can be reduced by reducing the flame retardant. In particular,
Brominated alicyclic compounds are those which can obtain a high flame retardant effect by reducing the compounding amount as compared with conventionally used chlorine based alicyclic compounds, and are preferably used as brominated flame retardants. .
以下本発明を実施例によって詳述する。 実施例１ 融点が225℃、極限粘度（フェノール／テトラクロルエ
タン＝1/1,30℃）が0.9のポリブチレンテレフタレート
に、次表の配合でブロム系難燃剤と三酸化アンチモンと
メチロールメラミン樹脂とを配合して混合し、これを押
し出し機にて押し出し造粒することによって、ペレット
状にポリブチレンテレフタレート樹脂組成物を調製し
た。 尚、ブロム系難燃剤としてはブロム系脂環族化合物のテ
トラブロムビスフェノールＡ型エポキシ樹脂オリゴマー
（マラック株式会社製EBR107;重合度約15）を用いた。 比較例１ 難燃助剤としてメチロールメラミン樹脂を配合せず、ブ
ロム系難燃剤と三酸化アンチモンの配合量を増量するこ
とによって難燃効果を維持するようにした他は、上記実
施例１と同様にしてポリブチレンテレフタレート樹脂組
成物を得た。 比較例２ 難燃剤として塩素系脂環族化合物であるパークロルペン
タシクロデカンと三酸化アンチモンとを配合するように
した他は、上記実施例１と同様にしてポリブチレンテレ
フタレート樹脂組成物を得た。 上記のようにして得られた実施例１、比較例1,2のポリ
ブチレンテレフタレート樹脂組成物を射出成形機を用い
て成形して、UL94燃焼試験用試験片（1/16インチ厚）を
作成し、UL94燃焼試験をおこなった。結果を次表に示
す。また実施例１、比較例1,2で得たポリブチレンテレ
フタレート樹脂組成物のペレットについて、金型腐食
製、銀接点変色性を調べた。試験は、30ml容器のバイア
ル瓶にペレットを5g入れ、この上に金型から切断した金
型片及び銀接点をそれぞれ載置して密閉し、150℃の条
件で７日間放置した後の金型片や銀接点の外観を観察す
ることによっておこなった。結果を次表に示す。 実施例１のものと比較例１との比較によって明らかなよ
うに、メチロールメラミン樹脂を配合することによって
ブロム系難燃剤や三酸化アンチモンの配合量を低減して
も優れた難燃効果を維持できることが確認され、金型腐
食や銀接点の変色を低減できることが確認される。また
比較例２のように難燃剤として塩素系脂環族化合物を用
いると配合量を多量にする必要があるために金型腐食や
銀接点の変色が発生し易くなることが確認される。Hereinafter, the present invention will be described in detail with reference to examples. Example 1 Polybutylene terephthalate having a melting point of 225 ° C. and an intrinsic viscosity (phenol / tetrachloroethane = 1 / 1,30 ° C.) of 0.9 was mixed with a bromine-based flame retardant, antimony trioxide, and methylol melamine resin in the formulations shown in the following table. Were mixed and mixed, and the mixture was extruded and granulated by an extruder to prepare a polybutylene terephthalate resin composition in the form of pellets. As the bromine-based flame retardant, a tetrabrom bisphenol A type epoxy resin oligomer of a bromine-based alicyclic compound (EBR107 manufactured by Malak Co .; polymerization degree: about 15) was used. Comparative Example 1 Similar to Example 1 above, except that the methylol melamine resin was not blended as a flame retardant aid, and the flame retardant effect was maintained by increasing the blending amounts of the brominated flame retardant and antimony trioxide. Then, a polybutylene terephthalate resin composition was obtained. Comparative Example 2 A polybutylene terephthalate resin composition was obtained in the same manner as in Example 1 except that perchlorpentacyclodecane, which is a chlorine-based alicyclic compound, and antimony trioxide were blended as a flame retardant. . The polybutylene terephthalate resin compositions of Example 1 and Comparative Examples 1 and 2 obtained as described above were molded using an injection molding machine to prepare a test piece (1/16 inch thick) for UL94 combustion test. Then, the UL94 combustion test was performed. The results are shown in the table below. The pellets of the polybutylene terephthalate resin composition obtained in Example 1 and Comparative Examples 1 and 2 were examined for mold corrosion and silver contact discoloration. For the test, put 5g of pellets in a vial of 30ml container, put the mold piece cut from the mold and the silver contact on it, seal each, and leave the mold at 150 ° C for 7 days. This was done by observing the appearance of the piece and the silver contact. The results are shown in the table below. As is clear from the comparison between Example 1 and Comparative Example 1, it is possible to maintain an excellent flame retardant effect even if the amount of the brominated flame retardant or antimony trioxide is reduced by adding the methylolmelamine resin. It is confirmed that the mold corrosion and the discoloration of the silver contact can be reduced. It is also confirmed that when a chlorine-based alicyclic compound is used as the flame retardant as in Comparative Example 2, it is necessary to increase the blending amount, and therefore mold corrosion and silver contact discoloration are likely to occur.
上述のように本発明にあっては、ポリブチレンテレフタ
レートに、ブロム系難燃剤と、三酸化アンチモンと、メ
チロールメラミン樹脂とを配合するようにしたので、メ
チロールメラミン樹脂を配合することによってブロム系
難燃剤や三酸化アンチモンの配合量を低減しても優れた
難燃効果を維持できるものであり、難燃剤による金型腐
食や銀接点の変色を低減することができるものである。As described above, in the present invention, the polybutylene terephthalate is blended with a bromine flame retardant, antimony trioxide, and a methylol melamine resin. The excellent flame retardant effect can be maintained even if the blending amount of the flame retardant or antimony trioxide is reduced, and the mold corrosion and the discoloration of the silver contact due to the flame retardant can be reduced.
Claims (1)
難燃剤と、三酸化アンチモンと、メチロールメラミン樹
脂とを配合して成ることを特徴とするポリブチレンテレ
フタレート樹脂組成物。1. A polybutylene terephthalate resin composition comprising polybutylene terephthalate mixed with a bromine flame retardant, antimony trioxide and a methylol melamine resin.