JPH0694064B2 - Sliding gate plate brick - Google Patents
Sliding gate plate brickInfo
- Publication number
- JPH0694064B2 JPH0694064B2 JP25979789A JP25979789A JPH0694064B2 JP H0694064 B2 JPH0694064 B2 JP H0694064B2 JP 25979789 A JP25979789 A JP 25979789A JP 25979789 A JP25979789 A JP 25979789A JP H0694064 B2 JPH0694064 B2 JP H0694064B2
- Authority
- JP
- Japan
- Prior art keywords
- plate
- molten metal
- metal contact
- sliding gate
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、モールドに溶湯金属を連続注入し鋳造する際
に、溶湯金属の流量を制御するスライディングゲートの
プレートれんがに関する。The present invention relates to a sliding gate plate brick for controlling the flow rate of molten metal when continuously pouring the molten metal into a mold for casting.
従来、この種のスライディングゲートにおけるプレート
れんがは、補修又は耐食性の向上を目的として、溶湯流
通孔の周囲又は溶湯流通孔の周囲とその周辺部の摺動面
を、プレート本体と同等あるいはそれ以上の耐食性を有
する不定形耐火物、耐食性セラミックス等によって形成
されている（実開昭60−5764号公報参照）。Conventionally, a plate brick in a sliding gate of this type has a sliding surface around the molten metal flow hole or around the molten metal flow hole and its peripheral part, which is equal to or more than the plate body, for the purpose of repair or improving corrosion resistance. It is formed of an irregular shaped refractory material having corrosion resistance, corrosion resistant ceramics, etc. (see Japanese Utility Model Laid-Open No. 605764).
しかしながら、上記従来のスライディングゲートのプレ
ートれんがによれば、次のような問題があった。However, the conventional sliding gate plate brick has the following problems.
（１）溶湯流通孔を設けたリングをプレート本体の孔に
嵌着したものは、溶損部がリング部から摺動面に及んだ
場合、再生不可能であり、又リングの一部が損傷した場
合、リングがプレート本体に対し相対的に移動し、湯漏
れ等のおそれがあった。(1) When the ring provided with the molten metal flow hole is fitted in the hole of the plate body, it cannot be regenerated when the melted part extends from the ring part to the sliding surface, and part of the ring is When it was damaged, the ring moved relative to the plate body and there was a risk of hot water leaks.
（２）溶湯流通孔を設けたリングと、その周辺部の摺動
面の一部をなす円形若しくは長円形のプレートとを一体
にしてプレート本体に装着したものは、リング及びプレ
ートの一部が損傷した場合、同様にリング及びプレート
がプレート本体に対し相対的に移動し、湯漏れ等のおそ
れがあり、又、リング及びプレートを交換する際に、こ
れらをプレート本体から分離するのが困難であった。(2) When the ring provided with the molten metal flow hole and the circular or elliptical plate forming a part of the sliding surface of the peripheral portion are integrally attached to the plate body, If damaged, the ring and plate will also move relative to the plate body, which may lead to hot water leaks, etc., and it is difficult to separate them from the plate body when replacing the ring and plate. there were.
そこで、本発明は、リングやプレート等の溶湯接触部材
の一部損傷による湯漏れを防止し得、かつ補修を容易に
なし得るスライディングゲートのプレートれんがの提供
を目的とする。Therefore, an object of the present invention is to provide a sliding gate plate brick that can prevent leakage of molten metal due to partial damage of a molten metal contact member such as a ring or a plate and that can be easily repaired.
前記課題を解決するため、本発明のスライディングゲー
トのプレートれんがは、溶湯流通孔を設けた適宜大径の
円輪板部と、摺動ストロークより適宜大径の円板部とを
一部重畳するようにしてなるダルマ形状の溶湯接触プレ
ートを、このプレートの外形とほぼ同形状に貫設したプ
レート本体の切欠き部に嵌着したものである。In order to solve the above problems, the sliding gate plate brick of the present invention partially overlaps an appropriately large-diameter circular disk portion provided with a molten metal flow hole and an appropriately large-diameter circular disk portion than a sliding stroke. The molten metal contact plate having the dulma shape thus formed is fitted into the notch portion of the plate main body which penetrates in substantially the same shape as the outer shape of the plate.
上記手段においては、溶湯接触プレートの一部が損傷し
ても、そのプレート本体に対する相対的な移動、ずれが
ダルマ形状のくびれ部によって防止される。In the above means, even if a part of the molten metal contact plate is damaged, relative movement and displacement of the molten metal contact plate with respect to the plate body are prevented by the dulled constricted portion.
又、溶湯接触プレートの損傷による交換補修に際して
は、例えばホールソー等の工具によってプレートれんが
に２つの円形の透孔を設けることにより、溶湯接触部の
プレートが除去される。Further, in the case of replacement and repair due to damage to the molten metal contact plate, the plate at the molten metal contact portion is removed by providing two circular through holes in the plate brick with a tool such as a hole saw.
円輪板部の直径は、溶湯流通孔の1.5〜3.0倍、円板部の
直径は、摺動ストロークの0.5〜2.0倍であることが好ま
しい。The diameter of the circular plate portion is preferably 1.5 to 3.0 times the diameter of the molten metal flow hole, and the diameter of the circular plate portion is preferably 0.5 to 2.0 times the sliding stroke.
以下、本発明の一実施例を図面と共に説明する。 An embodiment of the present invention will be described below with reference to the drawings.
第１図、第２図は３枚プレートのスライディングゲート
における中間のプレートれんがの平面図、縦断面図であ
る。1 and 2 are a plan view and a vertical sectional view of an intermediate plate brick in a sliding gate having three plates.
図中１はアルミナ質、マグネシア質、ムライト質又はア
ルミナ・ムライト質等の耐火物からなる長円板状のプレ
ート本体で、その外周には、帯板材からなるリング状の
鉄皮２が嵌着されている。又、プレート本体１には、後
述する溶湯流通孔と対応する位置に、この溶湯流通孔よ
り適宜大径（溶湯流通孔の1.5〜3.0倍）の円と、プレー
ト本体１の摺動ストロークより適宜大径（摺動ストロー
クの0.5〜2.0倍）の円とを一部重畳するようにしてなる
ダルマ形状の切欠き部３が貫設されている。切欠き部３
の両円は、実施例では、同一径に設けられている。In the figure, 1 is an elliptical plate body made of a refractory material such as alumina, magnesia, mullite, or alumina-mullite, and a ring-shaped iron skin 2 made of a strip material is attached to the outer periphery thereof. Has been done. Further, in the plate body 1, at a position corresponding to a later-described molten metal flow hole, a circle having an appropriately larger diameter than the molten metal flow hole (1.5 to 3.0 times the molten metal flow hole) and a sliding stroke of the plate body 1 are appropriately used. A daruma-shaped notch 3 is formed so as to partially overlap a circle having a large diameter (0.5 to 2.0 times the sliding stroke). Notch 3
Both circles are provided with the same diameter in the embodiment.
そして、プレート本体１の切欠き部３には、溶湯流通孔
４を設けた適宜大径（溶湯流通孔の1.5〜3.0倍）の円輪
板部5aと、プレート本体１の摺動ストロークより適宜大
径（摺動ストロークの1.5〜2.0倍）の円板部5bとを一部
重畳するようにし、切欠き部３とほぼ同様のダルマ形状
の溶湯接触プレート５がモルタル６を介在して嵌着され
ている。溶湯接触プレート５は、プレート本体１と同
様、アルミナ質、マグネシア質、ムライト質又はアルミ
ナ・ムライト質等の耐火物からなり、その外周面には、
プレート本体１との接合強度を高めるため、周溝７が形
成されている。Further, the notch 3 of the plate body 1 is provided with a molten metal flow hole 4 and an appropriately large-diameter ring plate portion 5a (1.5 to 3.0 times the molten metal flow hole) and a sliding stroke of the plate body 1 as appropriate. A large-diameter (1.5 to 2.0 times the sliding stroke) disk part 5b is partially overlapped, and a duller-shaped molten metal contact plate 5 similar to the cutout part 3 is fitted with a mortar 6 interposed. Has been done. Like the plate body 1, the molten metal contact plate 5 is made of a refractory material such as alumina, magnesia, mullite, or alumina-mullite, and the outer peripheral surface thereof is
A circumferential groove 7 is formed in order to increase the bonding strength with the plate body 1.
上記構成のプレートれんがにおいては、溶湯接触プレー
ト５の一部が損傷しても、そのプレート本体１に対する
相対的な移動、ずれがダルマ形状のくびれ部によって防
止されるので、溶湯の湯洩等が生じない。In the plate brick having the above structure, even if a part of the molten metal contact plate 5 is damaged, relative movement and displacement of the molten metal contact plate 5 with respect to the plate main body 1 are prevented by the daruma-shaped necked portion, so that molten metal leakage or the like does not occur. Does not happen.
又、溶湯による損傷がプレート本体１まで及ばないと共
に、溶湯接触プレート５の損傷による交換補修に際して
は、例えばダイヤモンドチップ付きのホールソー等の工
具によって、プレート本体１と溶湯接触プレート５との
接合部のモルタル７を切削することにより、溶湯接触プ
レート５が容易に除去され、新しい溶湯接触プレート５
をモルタル７を介して切欠き部３に嵌着、かつ摺動面に
研削加工を施すと、プレートれんがの再使用が可能とな
る。Further, the damage due to the molten metal does not reach the plate body 1, and at the time of replacement and repair due to the damage to the molten metal contact plate 5, the joining portion between the plate body 1 and the molten metal contact plate 5 is repaired with a tool such as a hole saw with a diamond tip. The molten metal contact plate 5 is easily removed by cutting the mortar 7, and a new molten metal contact plate 5 is obtained.
The plate brick can be reused by fitting it into the notch 3 through the mortar 7 and grinding the sliding surface.
なお、ダルマ形状の溶湯接触プレート５によるプレート
れんがの再生は、上述したように損傷した溶湯接触プレ
ート５の交換補修に限らず、溶湯接触プレート５を有し
ない従来のプレートれんがにも、ダルマ形状の切欠き部
を設け、この切欠き部に溶湯接触プレート５を嵌着する
ことによっても行うことができる。Regeneration of the plate bricks by the dharma-shaped molten metal contact plate 5 is not limited to replacement and repair of the molten metal contact plate 5 damaged as described above, and conventional plate bricks that do not have the molten metal contact plate 5 also have It can also be performed by providing a notch and fitting the molten metal contact plate 5 into the notch.
以上のように本発明よれば、溶湯接触プレートの一部が
損傷しても、そのプレート本体に対する相対的な移動、
ずれがダルマ形状のくびれ部によって防止されるので、
溶湯の漏洩等を防止することができる。As described above, according to the present invention, even if a part of the molten metal contact plate is damaged, relative movement with respect to the plate body,
Since the slippage is prevented by the dharma-shaped constriction,
It is possible to prevent leakage of molten metal.
又、溶湯接触プレートの損傷による交換補修に際して
は、例えばホールソー等の工具によってプレートれんが
に溶湯接触プレートの輪郭に沿った２つの円形の透孔を
設けることにより、溶湯接触プレートが除去されるの
で、従来の長円形の溶湯接触部材のようにその除去が困
難となることがなく、補修作業を容易に行うことができ
る。In addition, at the time of replacement and repair due to damage to the molten metal contact plate, the molten metal contact plate is removed by providing two circular through holes along the contour of the molten metal contact plate in the plate brick with a tool such as a hole saw. Unlike the conventional elliptical molten metal contact member, it is not difficult to remove the member, and the repair work can be easily performed.
第１図は本発明の一実施例を示すスライディングゲート
のプレートれんがの平面図、第２図は第１図におけるII
−II線断面図である。 １……プレート本体、３……切欠き部 ４……溶湯流通孔、５……溶湯接触プレート 5a……円輪板部、5b……円板部FIG. 1 is a plan view of a plate brick of a sliding gate showing one embodiment of the present invention, and FIG. 2 is a II in FIG.
It is a II sectional view. 1 ... Plate body, 3 ... Notch portion 4 ... Molten metal flow hole, 5 ... Molten metal contact plate 5a ... Ring plate portion, 5b ... Disc portion
───────────────────────────────────────────────────── フロントページの続き (72)発明者 西尾 内匠 愛知県刈谷市小垣江町南藤１番地 東芝セ ラミックス株式会社刈谷製造所内 (72)発明者 浅井 正道 愛知県刈谷市小垣江町南藤１番地 東芝セ ラミックス株式会社刈谷製造所内 (72)発明者 平山 清衛 茨城県鹿島郡鹿島町大字光３番地 住友金 属工業株式会社鹿島製鉄所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Nishio Takumi, 1st Nanto, Ogakie-cho, Kariya city, Aichi Toshiba Ceramics Co., Ltd. inside Kariya factory (72) Masamichi Asai 1st, Nanto, Ogakie-cho, Kariya city, Aichi prefecture Lamix Co., Ltd. Kariya Works (72) Inventor, Kiyoe Hirayama, Kashima-machi, Kashima-gun, Ibaraki Prefecture, Sumitomo Metal Industries, Ltd. Kashima Works
Claims (1)
と、摺動ストロークより適宜大径の円板部とを一部重畳
するようにしてなるダルマ形状の溶湯接触プレートを、
このプレートの外径とほぼ同形状に貫設したプレート本
体の切欠き部に嵌着したことを特徴とするスライディン
グゲートのプレートれんが。1. A dulma-shaped molten metal contact plate in which an appropriately large-diameter circular disk portion provided with a molten metal flow hole and a circular disk portion having an appropriately large diameter than a sliding stroke partially overlap each other,
A plate brick for a sliding gate, characterized in that the plate brick is fitted into a notch portion of a plate body which is formed to have a shape substantially the same as the outer diameter of the plate.