JPH0726072B2 - Adhesive composition - Google Patents
Adhesive compositionInfo
- Publication number
- JPH0726072B2 JPH0726072B2 JP1312431A JP31243189A JPH0726072B2 JP H0726072 B2 JPH0726072 B2 JP H0726072B2 JP 1312431 A JP1312431 A JP 1312431A JP 31243189 A JP31243189 A JP 31243189A JP H0726072 B2 JPH0726072 B2 JP H0726072B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- vinyl acetate
- emulsion
- ethylene
- ethylene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、新規な接着剤組成物に関し、特に、ポリ塩化
ビニルあるいは撥水紙のように疎水性を有する被着材に
対して優れた接着性能を有する接着剤組成物に関する。TECHNICAL FIELD The present invention relates to a novel adhesive composition, and in particular, it is excellent for an adherend having a hydrophobic property such as polyvinyl chloride or water repellent paper. The present invention relates to an adhesive composition having adhesive performance.
従来より、ポリ塩化ビニルまたは撥水紙のように疎水性
を有する被着材に対して用いる接着剤としては、エチレ
ン−酢酸ビニル共重合体またはアクリル酸エステル−酢
酸ビニル共重合体エマルジョン系のものが用いられてい
る。Conventionally, as an adhesive used for an adherend having a hydrophobic property such as polyvinyl chloride or water repellent paper, an ethylene-vinyl acetate copolymer or an acrylic ester-vinyl acetate copolymer emulsion type adhesive is used. Is used.
しかしながら、上記のようなエマルジョン接着剤では、
密着性及び耐熱クリープ特性が十分でないという問題が
あった。そこで、密着性及び耐熱クリープ性を改善する
ために、ウレタン樹脂と水性ラテックスとを混合してな
る主剤に、使用前にエポキシ化合物、メラミン化合物ま
たはアジリジン環化合物等の架橋剤を添加する２液タイ
プの接着剤が提案されている（例えば、特公昭63−3351
8号）。However, with the emulsion adhesive as described above,
There is a problem that the adhesiveness and the heat-resistant creep property are not sufficient. Therefore, in order to improve the adhesiveness and the heat-resistant creep resistance, a two-pack type in which a crosslinking agent such as an epoxy compound, a melamine compound or an aziridine ring compound is added before use to a main agent obtained by mixing a urethane resin and an aqueous latex. Have been proposed (for example, Japanese Patent Publication No. 63-3351).
No. 8).
しかしながら、２液タイプの接着剤組成物では、使用す
る前に主剤と硬化剤とを混合しなければならない。ま
た、混合後の粘度上昇により塗工が行い難くなり、使用
可能時間に制限があった。However, in a two-pack type adhesive composition, the main agent and the curing agent must be mixed before use. In addition, the increase in viscosity after mixing made it difficult to apply the coating, and the usable time was limited.
従って、本発明の目的は、ポリ塩化ビニルあるいは撥水
紙のような疎水性を有する被着材の接着に好適であり、
かつ取扱作業性に優れた１液タイプの接着剤を構成し得
る新規な接着剤組成物を提供することにある。Therefore, the object of the present invention is suitable for adhesion of an adherend having a hydrophobic property such as polyvinyl chloride or water repellent paper,
Another object of the present invention is to provide a novel adhesive composition capable of forming a one-pack type adhesive having excellent handling workability.
本願発明者らは、疎水性被着材の接着に適しており、さ
らに、１液タイプの接着剤として構成し得る接着剤組成
物を開発すべく鋭意検討した結果、酢酸ビニル−エチレ
ン共重合体エマルジョン、塩化ビニル−酢酸ビニル−エ
チレン共重合体またはその変性物のエマルジョン及び水
溶性もしくは水分散性ウレタン樹脂を配合すれば、本発
明の目的を達成し得ることを見出し、該知見に基づき本
発明をなすに至った。The inventors of the present application have made earnest studies to develop an adhesive composition suitable for adhering a hydrophobic adherend and capable of being configured as a one-pack type adhesive, and as a result, a vinyl acetate-ethylene copolymer. It was found that the object of the present invention can be achieved by blending an emulsion, an emulsion of a vinyl chloride-vinyl acetate-ethylene copolymer or a modified product thereof, and a water-soluble or water-dispersible urethane resin, and the present invention was based on this finding. Came to make.
すなわち、本発明は、 樹脂中にエチレンを10〜25重量％含有する酢酸ビニル−
エチレン共重合体のエマルジョン（Ｉ）と、 樹脂中に塩化ビニルを20〜70重量％含有し、さらにエチ
レンを10〜25重量％含有する塩化ビニル−酢酸ビニル−
エチレン共重合体またはその変性物のエマルジョン（I
I）と、 芳香族もしくは脂肪族イソシアネート系ポリエステル型
水溶性もしくは水分散性ウレタン樹脂（III）とを配合
してなる接着剤組成物である。That is, the present invention relates to vinyl acetate containing 10 to 25% by weight of ethylene in the resin.
Emulsion (I) of ethylene copolymer and vinyl chloride containing 20 to 70% by weight of vinyl chloride in the resin and further containing 10 to 25% by weight of ethylene-vinyl acetate-
Emulsion of ethylene copolymer or its modified product (I
An adhesive composition comprising I) and an aromatic or aliphatic isocyanate polyester type water-soluble or water-dispersible urethane resin (III).
配合量 塩化ビニル−酢酸ビニル−エチレンまたはその変性物の
共重合体エマルジョン（II）は、酢酸ビニル−エチレン
共重合体エマルジョン（Ｉ）100重量部（固形分換算）
に対し、固形分換算で５〜50重量部配合される。５重量
部未満では、塩化ビニルとの密着性が低下し、かつ耐熱
性も劣化するからであり、他方、50重量部を越えて配合
した場合には耐寒性が低下するからである。好ましく
は、塩化ビニル−酢酸ビニル−エチレン共重合体または
その変性物のエマルジョン（II）は、酢酸ビニル−エチ
レン共重合体エマルジョン（Ｉ）100重量部（固形分換
算）に対し、15〜30重量部（固形分換算）配合される。Amount to be blended Vinyl chloride-vinyl acetate-ethylene or a modified product thereof copolymer emulsion (II) is 100 parts by weight of vinyl acetate-ethylene copolymer emulsion (I) (solid content conversion).
On the other hand, 5 to 50 parts by weight in terms of solid content is blended. This is because if the amount is less than 5 parts by weight, the adhesion to vinyl chloride will deteriorate and the heat resistance will also deteriorate, while if it is compounded in an amount exceeding 50 parts by weight, the cold resistance will decrease. Preferably, the emulsion (II) of vinyl chloride-vinyl acetate-ethylene copolymer or a modified product thereof is 15 to 30 parts by weight based on 100 parts by weight of vinyl acetate-ethylene copolymer emulsion (I) (solid content conversion). Parts (solid content conversion).
また、水溶性もしくは水分散性のウレタン樹脂（III）
は、酢酸ビニル−エチレン共重合体エマルジョン（Ｉ）
100重量部（固形分換算）に対し、固形分換算で２〜50
重量部配合される。２重量部未満では、塩化ビニルとの
密着性が悪くなり、かつ耐熱性が低下するからである。
他方、50重量部を超えて配合した場合には、エマルジョ
ンの安定性及び塗工性が低下し、かつウレタン樹脂（II
I）の凝集力が弱いので接着強度が低下するからであ
る。好ましくは、水溶性もしくは水分散性ウレタン樹脂
（III）は、酢酸ビニル−エチレン共重合体エマルジョ
ン（Ｉ）100重量部に対し、５〜30重量部配合される。In addition, water-soluble or water-dispersible urethane resin (III)
Is a vinyl acetate-ethylene copolymer emulsion (I)
2 to 50 in terms of solid content for 100 parts by weight (in terms of solid content)
It is compounded in parts by weight. This is because if it is less than 2 parts by weight, the adhesion to vinyl chloride will deteriorate and the heat resistance will decrease.
On the other hand, when the amount is more than 50 parts by weight, the emulsion stability and coatability are deteriorated, and the urethane resin (II
This is because the cohesive force of I) is weak and the adhesive strength is reduced. Preferably, the water-soluble or water-dispersible urethane resin (III) is blended in an amount of 5 to 30 parts by weight with respect to 100 parts by weight of the vinyl acetate-ethylene copolymer emulsion (I).
エマルジョン（Ｉ） 本発明において用いる酢酸ビニル−エチレン共重合体エ
マルジョン（Ｉ）としては、樹脂中にエチレンを10〜25
重量％含有するものが用いられる。エチレン含有量が10
重量％未満では造膜温度が高くなり使用することができ
ないからである。また、25重量％を超える場合には接着
力が低下するからである。Emulsion (I) The vinyl acetate-ethylene copolymer emulsion (I) used in the present invention contains 10 to 25 ethylene in the resin.
Those containing wt% are used. Ethylene content 10
This is because if it is less than wt%, the film forming temperature becomes too high to be used. Also, if it exceeds 25% by weight, the adhesive strength will decrease.
エマルジョン（II） 塩化ビニル−酢酸ビニル−エチレン共重合体またはその
変性物のエマルジョン（II）としては、樹脂中に塩化ビ
ニルを20〜70重量％含有し、さらにエチレンを10〜25重
量％含有するものが用いられる。塩化ビニル含有量が20
重量％未満では、十分な密着性及び耐熱性が得られない
からであり、70重量％を超える場合には接着力が低下す
るからである。また、エチレン含有量が10重量％未満の
場合には造膜温度が高くなり使用できないからであり、
25重量％を超える場合には接着力が低下するからであ
る。Emulsion (II) Emulsion (II) of vinyl chloride-vinyl acetate-ethylene copolymer or its modified product contains 20 to 70% by weight of vinyl chloride in the resin and further contains 10 to 25% by weight of ethylene. Things are used. Vinyl chloride content is 20
This is because if it is less than wt%, sufficient adhesiveness and heat resistance cannot be obtained, and if it exceeds 70 wt%, the adhesive strength is reduced. Also, if the ethylene content is less than 10% by weight, the film forming temperature becomes too high to use,
This is because if the amount exceeds 25% by weight, the adhesive strength will decrease.
ウレタン樹脂（III） 芳香族もしくは脂肪族イソシアネート系ポリエステル型
水溶性もしくは水分散性のウレタン樹脂（III）として
は、公知のものを広く用いることができる。例えば、脂
肪族イソシアネート系ポリエステル型水溶性もしくは水
分散性ウレタン樹脂や、特公昭42−24192号公報及び特
公昭53−38760号公報に記載のようなカルボキシル基含
有芳香族イソシアネート系ポリエステル型水溶性もしく
は水分散性のウレタン樹脂を適宜用いることができる。
より具体的には、UXA−3004（商品名；三洋化成社製）
のような芳香族イソシアネート系ポリエステル型水分散
液を用いることができる。Urethane Resin (III) As the aromatic or aliphatic isocyanate polyester type water-soluble or water-dispersible urethane resin (III), widely known ones can be used. For example, an aliphatic isocyanate-based polyester type water-soluble or water-dispersible urethane resin, a carboxyl group-containing aromatic isocyanate-based polyester type water-soluble or as described in JP-B-42-24192 and JP-B-53-38760. A water-dispersible urethane resin can be used as appropriate.
More specifically, UXA-3004 (trade name; manufactured by Sanyo Kasei Co., Ltd.)
Aromatic isocyanate type polyester type aqueous dispersions such as the above can be used.
製造方法 本発明の接着剤組成物の製造方法は特に限定されない。
すなわち、この分野で慣用されている方法を広く用いる
ことがてのる。例えば、上記酢酸ビニル−エチレン共重
合体エマルジョン（Ｉ）、塩化ビニル−酢酸ビニル−エ
チレン共重合体またはその変性物のエマルジョン（II）
及び水溶性もしくは水分散性ウレタン樹脂（III）を単
に混合することにより製造することができる。Production Method The production method of the adhesive composition of the present invention is not particularly limited.
That is, the method commonly used in this field can be widely used. For example, the above vinyl acetate-ethylene copolymer emulsion (I), vinyl chloride-vinyl acetate-ethylene copolymer or its modified emulsion (II).
And a water-soluble or water-dispersible urethane resin (III) can be simply mixed.
なお、配合された接着剤組成物は、固形分濃度が30〜70
重量％となるように調整することが好ましい。30重量％
未満では、樹脂部分がかなり少ないので乾燥に長時間を
要し、作業性が低下するからである。他方、70重量％を
超えると、樹脂分が高くなり過ぎ、配合物の安定性（貯
蔵安定性及び機械的安定性等）が低下するからである。
同様の観点から固形分濃度のより好ましい範囲は、40〜
60重量％である。In addition, the blended adhesive composition has a solid content concentration of 30 to 70.
It is preferable to adjust the content to be wt%. 30% by weight
If it is less than the above range, the resin portion is considerably small, so that it takes a long time to dry and the workability is deteriorated. On the other hand, if it exceeds 70% by weight, the resin content becomes too high, and the stability of the compound (storage stability, mechanical stability, etc.) is reduced.
From the same viewpoint, the more preferable range of the solid content concentration is 40 to
60% by weight.
また、必要に応じて、溶剤、可塑剤、充填剤、増粘剤、
防黴剤及び／または防錆剤等を適宜添加してもよい。Also, if necessary, a solvent, a plasticizer, a filler, a thickener,
A mildew-proofing agent and / or a rust preventive agent may be added as appropriate.
本発明の接着剤組成物による接着 本発明の接着剤組成物は、１液タイプの接着剤として好
適に用いられる。すなわち、酢酸ビニル−エチレン共重
合体エマルジョン（Ｉ）、塩化ビニル−酢酸ビニル−エ
チレン共重合体またはその変性物のエマルジョン（II）
及び水溶性もしくは水分散性のウレタン樹脂（III）の
すべてを、上記のように混合することにより、１液タイ
プの接着剤として用意される。そして、使用に際して
は、ロールコーター、刷毛塗りまたはスプレー等の通常
の接着方法により接着剤を塗布すればよい。Adhesion by Adhesive Composition of the Present Invention The adhesive composition of the present invention is suitably used as a one-pack type adhesive. That is, a vinyl acetate-ethylene copolymer emulsion (I), a vinyl chloride-vinyl acetate-ethylene copolymer or its modified emulsion (II).
All of the water-soluble or water-dispersible urethane resin (III) are mixed as described above to prepare a one-liquid type adhesive. Then, at the time of use, the adhesive may be applied by a usual adhesion method such as a roll coater, brush coating or spraying.
本発明の接着剤組成物が優れた耐熱性及び塗工作業性を
示すのは以下の理由によると考えられる。すなわち、酢
酸ビニル−エチレン共重合体エマルジョン（Ｉ）に水溶
性もしくは水分散性のウレタン樹脂（III）をある程度
混合すれば、耐熱性は向上される。しかしながら、接着
力及び塗工作業性が低下する。これに対して、本発明で
配合される塩化ビニル−酢酸ビニル−エチレン共重合体
またはその変性物のエマルジョン（II）は、この接着力
及び塗工性を改善する機能を果たし、それによって接着
剤組成物全体の接着力、耐熱性及び塗工作業性のバラン
スをとっているものと考えられる。It is considered that the adhesive composition of the present invention exhibits excellent heat resistance and coating workability for the following reasons. That is, the heat resistance is improved by mixing the vinyl acetate-ethylene copolymer emulsion (I) with the water-soluble or water-dispersible urethane resin (III) to some extent. However, the adhesive strength and coating workability are reduced. On the other hand, the emulsion (II) of the vinyl chloride-vinyl acetate-ethylene copolymer or a modified product thereof, which is blended in the present invention, has a function of improving this adhesive force and coatability, whereby the adhesive agent It is considered that the adhesive strength, heat resistance and coating workability of the entire composition are balanced.
以上のように、本発明によれば、樹脂中にエチレンを10
〜25重量％含有する酢酸ビニル−エチレン共重合体エマ
ルジョン（Ｉ）及び芳香族もしくは脂肪族イソシアネー
ト系ポリエステル型の水溶性もしくは水分散性ウレタン
樹脂（III）に、樹脂中に塩化ビニルを20〜70重量％、
エチレンを10〜25重量％含有する塩化ビニル−酢酸ビニ
ル−エチレン共重合体またはその変性物のエマルジョン
（II）が配合されているため、ポリ塩化ビニルあるいは
撥水紙のような疎水性を有する接着し難い被着材の接着
に好適であり、耐熱クリープ特性に優れた接着剤組成物
を提供することが可能となる。しかも、本発明の接着剤
組成物は、１液タイプの接着剤として使用することがで
き、経時的な粘度上昇も生じ難いため、使用に際して混
合作業を省略することができ、かつ塗工作業性も大幅に
改善される。As described above, according to the present invention, ethylene in the resin 10
Vinyl acetate-ethylene copolymer emulsion (I) and aromatic or aliphatic isocyanate polyester type water-soluble or water-dispersible urethane resin (III) containing 20 to 70% by weight of vinyl chloride. weight%,
Emulsion (II) of vinyl chloride-vinyl acetate-ethylene copolymer containing ethylene in an amount of 10 to 25% by weight or its modified emulsion (II) is blended so that it has adhesive properties such as polyvinyl chloride or water repellent paper. It is possible to provide an adhesive composition that is suitable for adhering adherends that are difficult to perform and has excellent heat-resistant creep properties. Moreover, since the adhesive composition of the present invention can be used as a one-pack type adhesive and the viscosity does not easily increase over time, the mixing operation can be omitted during use, and the coating workability can be improved. Is also greatly improved.
酢酸ビニル−エチレン共重合体エマルジョン（Ｉ）とし
て、Ｓ−440（商品名；住友化学工業社製）を、塩化ビ
ニル−酢酸ビニル−エチレン共重合体エマルジョン（I
I）としてＳ−830（商品名；住友化学工業社製）を、芳
香族イソシアネート系ポリエステル型ウレタン樹脂の水
分散液としてUXA−3004（商品名；三洋化成社製）を用
い、第１表に示す割合で配合し、実施例１〜３の接着剤
組成物を得た。As the vinyl acetate-ethylene copolymer emulsion (I), S-440 (trade name; manufactured by Sumitomo Chemical Co., Ltd.) was used as a vinyl chloride-vinyl acetate-ethylene copolymer emulsion (I
S-830 (trade name; manufactured by Sumitomo Chemical Co., Ltd.) is used as I), and UXA-3004 (trade name; manufactured by Sanyo Chemical Co., Ltd.) is used as an aqueous dispersion of an aromatic isocyanate polyester urethane resin. It mixed in the ratio shown and the adhesive composition of Examples 1-3 was obtained.
また、比較のために、第１表に示す割合で１種または２
種以上の上記エマルジョンを混合した接着剤組成物を比
較例１〜３として用意した。In addition, for comparison, one kind or two kinds are used at the ratio shown in Table 1.
Adhesive compositions prepared by mixing one or more of the above emulsions were prepared as Comparative Examples 1 to 3.
なお、Ｓ−440のエチレン及び酢酸ビニルの含有量は、
エチレン18重量％及び酢酸ビニル80重量％である。ま
た、Ｓ−830中の塩化ビニル、酢酸ビニル及びエチレン
の含有量は、それぞれ、エチレン10〜15重量％、酢酸ビ
ニル30〜35重量％及び塩化ビニル55重量％である。ま
た、Ｓ−440、Ｓ−830及びUXA−3004の蒸発残分は、そ
れぞれ、56％（Ｓ−440）、50％（Ｓ−830）及び40％
（UXA−3004）である。The content of ethylene and vinyl acetate in S-440 is
18% by weight of ethylene and 80% by weight of vinyl acetate. The contents of vinyl chloride, vinyl acetate and ethylene in S-830 are ethylene 10 to 15% by weight, vinyl acetate 30 to 35% by weight and vinyl chloride 55% by weight, respectively. The evaporation residues of S-440, S-830 and UXA-3004 are 56% (S-440), 50% (S-830) and 40%, respectively.
(UXA-3004).
第１表に示す割合で上記各エマルジョンを配合して得た
実施例１〜３及び比較例１〜３の各接着剤組成物を、被
着材として軟質塩化ビニルシート及びJAS1類のラワン合
板を用い、下記の接着条件で接着した。Each of the adhesive compositions of Examples 1 to 3 and Comparative Examples 1 to 3 obtained by blending the above emulsions in the proportions shown in Table 1 was used as an adherend using a soft vinyl chloride sheet and a JAS1 class lauan plywood. They were used and bonded under the following bonding conditions.
接着条件 塗布量:110g/m2。Adhesion conditions Coating weight: 110g / m 2 .
圧締条件:1kg/cm2×15時間。Clamping condition: 1kg / cm 2 x 15 hours.
養生条件:20℃,65％RHにて48時間。Curing condition: 48 hours at 20 ℃, 65% RH.
接着した後、常態強度及び耐熱クリープを下記の要領で
測定した。結果を、第１表に併せて示す。After bonding, the normal strength and heat resistant creep were measured as follows. The results are also shown in Table 1.
常態強度： 幅25mmの貼り合わせ試験片について、速度200mm/分で18
0℃剥離試験を行った。Normal strength: 18 at a speed of 200 mm / min for a bonded specimen with a width of 25 mm
A 0 ° C. peel test was performed.
耐熱クリープ試験： 幅25mm×200mmの試験片を軟質塩化ビニルシート側を縦
方向に50mm剥離し、試験片を水平に置き、剥離した軟質
塩化ビニルシートを垂下したまま80℃をギヤオーブンに
１時間静置した後、軟質塩化ビニルシートの剥離されて
いる部分の先端に500gの荷重をかけて放置し、１時間後
の剥離長さを測定した。この場合、剥離長さが短い程耐
熱クリープ性が良好であることを示す。Heat-resistant creep test: A test piece with a width of 25 mm x 200 mm is peeled 50 mm vertically on the soft vinyl chloride sheet side, the test piece is placed horizontally, and the peeled soft vinyl chloride sheet is hung down at 80 ° C in a gear oven for 1 hour. After standing still, a load of 500 g was applied to the tip of the peeled portion of the soft vinyl chloride sheet and left for one hour, and the peel length after 1 hour was measured. In this case, the shorter the peeling length, the better the thermal creep resistance.
第１表から明らかなように、Ｓ−440、Ｓ−830及びUXA
−3004を配合してなる実施例１〜３の接着剤組成物で
は、常態強度及び耐熱クリープの双方において優れた特
性を示すことがわかる。 As is clear from Table 1, S-440, S-830 and UXA
It can be seen that the adhesive compositions of Examples 1 to 3 containing -3004 show excellent characteristics in both normal strength and heat-resistant creep.
これに対して、酢酸ビニル−エチレン共重合体エマルジ
ョン（Ｉ）からなる比較例１の接着剤組成物や、酢酸ビ
ニル−エチレン共重合体エマルジョン（Ｉ）及び塩化ビ
ニル−酢酸ビニル−エチレン共重合体エマルジョン（I
I）を配合した比較例３の接着剤組成物では、常態強度
こそ実施例１〜３と同等であるが、耐熱クリープ試験に
おいて試験片全体が剥がれてしまい、耐熱性においてか
なり劣ることがわかる。On the other hand, the adhesive composition of Comparative Example 1 comprising the vinyl acetate-ethylene copolymer emulsion (I), the vinyl acetate-ethylene copolymer emulsion (I) and the vinyl chloride-vinyl acetate-ethylene copolymer. Emulsion (I
In the adhesive composition of Comparative Example 3 containing I), the normal strength is equivalent to that of Examples 1 to 3, but it can be seen that the entire test piece is peeled off in the heat creep test and the heat resistance is considerably poor.
また、酢酸ビニル−エチレン共重合体エマルジョン
（Ｉ）と芳香族イソシアネート系ポリエステル型ウレタ
ン樹脂（III）の水分散液とを配合した比較例２の接着
剤組成物では、耐熱クリープ試験については、実施例２
と同等の性能を示しているものの、実施例１〜３の何れ
の接着剤組成物に対しても常態強度において劣ることが
わかる。Further, in the adhesive composition of Comparative Example 2 in which the vinyl acetate-ethylene copolymer emulsion (I) and the aqueous dispersion of the aromatic isocyanate polyester urethane resin (III) were blended, the heat-resistant creep test was conducted. Example 2
Although it shows the same performance as, it is found that the normal state strength is inferior to any of the adhesive compositions of Examples 1 to 3.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｌ 23/08 ＬＦＭ 27/06 ＬＥＰ ＬＥＵ 31/04 ＬＤＫ 75/06 ＮＧＧ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display area C08L 23/08 LFM 27/06 LEP LEU 31/04 LDK 75/06 NGG
Claims (1)
酢酸ビニル−エチレン共重合体のエマルジョンン（Ｉ）
と、 樹脂中に塩化ビニルを20〜70重量％含有し、さらにエチ
レンを10〜25重量％含有する塩化ビニル−酢酸ビニル−
エチレン共重合体またはその変性物のエマルジョン（I
I）と、 芳香族もしくは脂肪族イソシアネート系ポリエステル型
の水溶性もしくは水分散性ウレタン樹脂（III）とを配
合してなることを特徴とする接着剤組成物。1. A vinyl acetate-ethylene copolymer emulsion (I) containing 10 to 25% by weight of ethylene in a resin.
And vinyl chloride containing 20 to 70% by weight of vinyl chloride in the resin and 10 to 25% by weight of ethylene-vinyl acetate-
Emulsion of ethylene copolymer or its modified product (I
An adhesive composition comprising I) and an aromatic or aliphatic isocyanate polyester type water-soluble or water-dispersible urethane resin (III).