JPH0773728B2 - Rolling work roll surface care device and method of using the same - Google Patents
Rolling work roll surface care device and method of using the sameInfo
- Publication number
- JPH0773728B2 JPH0773728B2 JP2155083A JP15508390A JPH0773728B2 JP H0773728 B2 JPH0773728 B2 JP H0773728B2 JP 2155083 A JP2155083 A JP 2155083A JP 15508390 A JP15508390 A JP 15508390A JP H0773728 B2 JPH0773728 B2 JP H0773728B2
- Authority
- JP
- Japan
- Prior art keywords
- work roll
- doctor blade
- roll
- rolling
- care device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ＜産業上の利用分野＞ 本発明は、鋼帯等を圧延するワークロール表面に付着し
た異物を除去するドクターブレード式ロール表面の手入
れ装置及びその使用方法に関するものである。Description: TECHNICAL FIELD The present invention relates to a doctor blade type roll surface care device for removing foreign matters adhering to the work roll surface for rolling a steel strip and the like and a method for using the same. .
＜従来の技術＞ 鋼帯やステンレス鋼帯を圧延する際に、ワークロールの
表面に異物が付着していると、鋼帯の表面が凹み状に形
成されて、いわゆる押込疵が発生する。そこで、一般に
ワークロールには、表面の異物を除去するロール手入れ
装置が使用される。<Prior Art> When rolling a steel strip or a stainless steel strip, if a foreign material adheres to the surface of the work roll, the surface of the steel strip is formed in a concave shape, and so-called indentation flaws occur. Therefore, a roll care device that removes foreign matter on the surface is generally used for the work roll.
ロール手入れ装置としては、実公昭56−26881号公報や
実公昭63−50005号公報、あるいは実開平２−28304号公
報のように、第４図に示すような金属製のカミソリ刃状
ドクターブレード５を直接ワークロール２に押し当てる
方法が知られている。As a roll maintenance device, a metal razor blade-shaped doctor blade 5 as shown in FIG. 4 is used, as in JP-B-56-26881, JP-B-63-5005, or JP-B-2-28304. There is known a method of directly pressing the work roll 2 against the work roll 2.
＜発明が解決しようとする課題＞ しかし、上記の従来の方法では、ドクターブレード５は
ワークロール２に対して固定されているため、ドクター
ブレード５の先端に引っ掛かった異物14は同一場所に残
り、第４図に示すように、ワークロール２にスジ状疵15
を発生させる。<Problems to be Solved by the Invention> However, in the above-mentioned conventional method, since the doctor blade 5 is fixed to the work roll 2, the foreign matter 14 caught at the tip of the doctor blade 5 remains at the same place, As shown in FIG. 4, the work roll 2 has streak-like flaws 15.
Generate.
なお、この対策としては、ドクターブレード５の上部に
集塵回路を設置し、すみやかに異物14を除去することも
考えられ、乾式調質圧延では効果がある。しかし、圧延
油を使用する冷間圧延や調質圧延油を使用する湿式調質
圧延では、異物14は容易に除去されないため、この手段
では不十分である。As a countermeasure against this, a dust collecting circuit may be installed above the doctor blade 5 to quickly remove the foreign matter 14, which is effective in dry temper rolling. However, in cold rolling using rolling oil and wet temper rolling using temper rolling oil, the foreign matter 14 is not easily removed, and this means is insufficient.
また、ワークロール２としては、粗度Ra＝0.1〜0.4μｍ
程度のブライトロールや、Ra＝1.0〜3.0μｍのダルロー
ルが使用されるが、ダルロールの場合、ドクターブレー
ド５のワークロール２への押付力が高いと短時間でロー
ル粗度が低下するという問題がある。The work roll 2 has a roughness Ra = 0.1 to 0.4 μm.
Bright rolls of a certain degree or dull rolls of Ra = 1.0 to 3.0 μm are used. However, in the case of dull rolls, there is a problem that the roll roughness decreases in a short time if the pressing force of the doctor blade 5 against the work roll 2 is high. is there.
本発明は、このような問題を解決した圧延ワークロール
表面の手入れ装置及びその使用方法を提供することを目
的とする。An object of the present invention is to provide a rolling work roll surface care device and a method of using the same, which solves the above problems.
＜課題を解決するための手段＞ 本発明の圧延用ワークロール表面の手入れ装置は、圧延
用ワークロールの表面に付着した異物を除去するドクタ
ーブレード式ロール手入れ装置において、前記ドクター
ブレードを厚みが0.05〜0.3mmのカミソリ刃状とすると
ともに、このドクターブレードをロール胴長方向に往復
摺動させる摺動機構を設けたことを特徴とするものであ
る。<Means for Solving the Problems> A rolling work roll surface care device of the present invention is a doctor blade type roll care device for removing foreign matter adhering to the surface of a rolling work roll, wherein the doctor blade has a thickness of 0.05. It is characterized in that it has a razor blade shape of up to 0.3 mm and is provided with a sliding mechanism for sliding the doctor blade back and forth in the length direction of the roll body.
そして、本発明の圧延用ワークロール表面の手入れ装置
の使用方法は、前記装置を使用するに際し、ドクターブ
レードの押付力を線圧0.5〜3.0kg/mとすることを特徴と
するものである。The method of using the apparatus for cleaning the surface of the work roll for rolling according to the present invention is characterized in that the pressing force of the doctor blade is set to a linear pressure of 0.5 to 3.0 kg / m when the apparatus is used.
＜作 用＞ 本発明では、ドクターブレードを厚みが0.05〜0.3mmの
カミソリ刃状とするとともにワークロールの胴長方向に
往復摺動させるので、異物が同一場所に残ることを防止
でき、ワークロールにスジ状疵が発生するのを防止でき
る。<Operation> In the present invention, since the doctor blade has a razor blade shape with a thickness of 0.05 to 0.3 mm and slides back and forth in the longitudinal direction of the work roll, it is possible to prevent foreign matter from remaining in the same place, and It is possible to prevent streak-like defects from being generated.
また、本発明によれば、第３図に示したように（詳細は
後記の第３図の説明を参照）、ワークロールの粗度低下
によるロール寿命の低下の問題が生じない。Further, according to the present invention, as shown in FIG. 3 (for details, see the description of FIG. 3 below), the problem of roll life shortening due to work roll roughness reduction does not occur.
＜実施例＞ 本発明の実施例を図面に基づいて説明する。<Example> An example of the present invention will be described with reference to the drawings.
第１図は、本発明の装置の一実施例を示し、装置の片側
の説明図である。第２図は第１図のＩ−Ｉ線断面図であ
る。FIG. 1 shows an embodiment of the device of the present invention, and is an illustration of one side of the device. FIG. 2 is a sectional view taken along line II of FIG.
第１、２図において、ドクターブレード５はブレードホ
ルダー３に、ブレード押え６で固定され、軸４と軸受８
により回転自在に支持されている。ドクターブレード５
のワークロール２への押付力Ｆは、自重Ｗで与えられる
が、カウンターウェイト７により、押付力Ｆの調整を可
能としてある。1 and 2, the doctor blade 5 is fixed to the blade holder 3 by a blade retainer 6, and the shaft 4 and the bearing 8 are attached.
It is rotatably supported by. Doctor blade 5
The pressing force F on the work roll 2 is given by its own weight W, but the pressing force F can be adjusted by the counterweight 7.
また、軸受８の下部には、スライドライナー９とアクチ
ュエータ10があり、電磁切換弁13、スピードコントロー
ラ12の操作により、ドクターブレード５はワークロール
２胴長方向に往復摺動可能としてある。A slide liner 9 and an actuator 10 are provided below the bearing 8, and the doctor blade 5 can be slid back and forth in the longitudinal direction of the work roll 2 by operating an electromagnetic switching valve 13 and a speed controller 12.
11は、スライドライナー９及びアクチュエータ10を支持
するブラケットである。また、１は鋼帯である。Reference numeral 11 is a bracket that supports the slide liner 9 and the actuator 10. Further, 1 is a steel strip.
次に、具体的実施例について説明する。Next, specific examples will be described.
610mmφの３％Cr鋼製で、粗度Ra＝2.5μｍのワークロー
ル２に対して、材質SK5、厚み0.2mmのドクターブレード
５を用いた本発明の装置を、押付力Ｆを線圧2.0kg/m、
摺動ストロークを±20mm（頻度１回/3秒）として使用し
た。その結果は、ロールスジ状疵15の発生がなく、ロー
ル粗度の低下の問題もなかった。The apparatus of the present invention using the material SK5 and the doctor blade 5 having the thickness of 0.2 mm is applied to the work roll 2 made of 610 mmφ 3% Cr steel and having the roughness Ra = 2.5 μm. / m,
The sliding stroke was ± 20 mm (frequency: 1/3 seconds). As a result, there was no occurrence of roll streaks 15 and there was no problem of deterioration of roll roughness.
続いて、ドクターブレード５の厚み及び押付力Ｆを変え
て実験を行った。その結果は、第３図に示すように、押
付力Ｆが線圧3.0kg/mを超えると、ワークロール２の粗
度の低下が表れ、また、ドクターブレード５の厚みが0.
3mmを超えると、3.0kg/mの押付力では、ワークロール２
のクラウン（0.1mmの凸クラウン）になじまなかった。Subsequently, an experiment was conducted by changing the thickness of the doctor blade 5 and the pressing force F. As a result, as shown in FIG. 3, when the pressing force F exceeds a linear pressure of 3.0 kg / m, the roughness of the work roll 2 is lowered, and the thickness of the doctor blade 5 is 0.
Above 3 mm, work roll 2 with a pressing force of 3.0 kg / m
I didn't get used to the crown (0.1mm convex crown).
したがって、ドクターブレード５のワークロール２への
押付力Ｆは線圧3.0kg/m以下とする必要があり、この時
ドクターブレード５の厚みは0.3mm以下とする必要があ
る。Therefore, the pressing force F of the doctor blade 5 against the work roll 2 needs to be set to a linear pressure of 3.0 kg / m or less, and at this time, the thickness of the doctor blade 5 needs to be set to 0.3 mm or less.
なお、厚み0.1mm以下の薄いドクターブレード５を使用
する際には、線圧1.0kg/m以下の押付力でもよいが、押
付力Ｆをあまり小さくすると、振動等でブレードホルダ
ー３が反転することがあるので、0.5kg/m以上が望まし
い。When using a thin doctor blade 5 with a thickness of 0.1 mm or less, a pressing force with a linear pressure of 1.0 kg / m or less may be used, but if the pressing force F is too small, the blade holder 3 may be inverted due to vibrations or the like. Therefore, 0.5kg / m or more is desirable.
また、ドクターブレード５の厚みを0.5mmより薄くする
と、0.5kg/mの線圧で押しつぶされて波打ち状態とな
り、使用不能となるため、ドクターブレード５の厚みは
0.05mm以上が望ましい。Also, if the thickness of the doctor blade 5 is less than 0.5 mm, it will be crushed by a linear pressure of 0.5 kg / m and will be in a wavy state, making it unusable.
0.05mm or more is desirable.
また、摺動については、±10mm程度の短いストロークで
も十分である。Regarding sliding, a short stroke of about ± 10 mm is sufficient.
＜発明の効果＞ 以上説明したように、本発明により、ロール寿命を低下
させることなく、安定的に押し込み疵を防止することが
でき、品質、生産性ともに大幅に向上することができ
る。<Effects of the Invention> As described above, according to the present invention, it is possible to stably prevent indentation flaws without shortening the roll life, and it is possible to significantly improve both quality and productivity.
第１図は本発明の装置の一実施例を示し、装置の片側の
説明図である。第２図は第１図のＩ−Ｉ線断面図であ
る。第３図は押付力を変えたときの通板距離と粗度との
関係を示したグラフである。第４図は従来技術の説明図
である。 １……鋼帯、 ２……ワークロール、 ３……ブレードホルダー、 ４……軸、 ５……ドクターブレード、 ６……ブレード押え、 ７……カウンターウェイト、 ８……軸受、 ９……スライドライナー、 10……アクチュエータ、 11……ブラケット、 12……スピードコントローラ、 13……電磁切換弁、 14……異物、 15……スジ状疵。FIG. 1 shows an embodiment of the device of the present invention, and is an illustration of one side of the device. FIG. 2 is a sectional view taken along line II of FIG. FIG. 3 is a graph showing the relationship between the passage distance and the roughness when the pressing force is changed. FIG. 4 is an explanatory diagram of a conventional technique. 1 …… Steel strip, 2 …… Work roll, 3 …… Blade holder, 4 …… Shaft, 5 …… Doctor blade, 6 …… Blade retainer, 7 …… Counter weight, 8 …… Bearing, 9 …… Slide Liner, 10 …… actuator, 11 …… bracket, 12 …… speed controller, 13 …… solenoid switching valve, 14 …… foreign matter, 15 …… streak-like flaw.
Claims (2)
を除去するドクターブレード式ロール手入れ装置におい
て、前記ドクターブレードを厚みが0.05〜0.3mmのカミ
ソリ刃状とするとともに、このドクターブレードをロー
ル胴長方向に往復摺動させる摺動機構を設けたことを特
徴とする圧延用ワークロール表面の手入れ装置。1. A doctor blade type roll care device for removing foreign matter adhering to the surface of a work roll for rolling, wherein the doctor blade has a razor blade shape with a thickness of 0.05 to 0.3 mm, and the doctor blade is a roll cylinder. A device for cleaning the surface of a work roll for rolling, which is provided with a sliding mechanism for reciprocally sliding in the long direction.
ーブレードの押付力を線圧0.5〜3.0kg/mとすることを特
徴とする圧延用ワークロール表面の手入れ装置の使用方
法。2. A method of using a device for caring for the surface of a work roll for rolling, characterized in that the pressing force of the doctor blade is set to a linear pressure of 0.5 to 3.0 kg / m when the device of claim 1 is used.