JPH0818111B2 - Continuous casting method for thin slabs - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a moving mold, for example, a twin drum system using a pair of cooling drums having a water cooling mechanism inside, a single drum system using one cooling drum,
Alternatively, the present invention relates to a method of casting a thin-walled slab with a drum-belt type casting device in which a molten metal pool is formed between a cooling drum and a belt.

[0002]

2. Description of the Related Art In recent years, in the field of continuous casting of metals, a thin cast piece having a plate thickness (thickness of 2 to 10 mm) close to the shape of the final product has been used as a cooling mechanism for the purpose of reducing casting cost and creating new materials. Various techniques for casting by a continuous casting apparatus using a cooling drum provided with are proposed.

In such a casting technique, it is an important task to maintain the surface quality of the slab at a high level in a stable manner. Therefore, as a means for achieving uniform production of a solidified shell, for example, a cooling drum. Japanese Unexamined Patent Publication No. 60-184449 discloses a technique in which a large number of depressions are provided on the peripheral surface of the cooling drum so as to form an air gap as a heat insulating layer between the solidified shell and the solidified shell.

As an improved version of such technology,
Japanese Unexamined Patent Publication No. 64-83342 discloses a technique that specifies the depth, diameter, separation distance, and motif of the depression.
Further, as a method for processing the depression, means such as shot blasting, electrolytic method, electric discharge processing method, electron beam processing method and the like are disclosed.
It is disclosed in Japanese Patent Publication No. 62-254953.

[0005]

In order to continuously obtain a preferable thin cast piece using a moving mold type continuous casting machine, the outer peripheral surface of the cooling drum as the mold is cleaned and the outer peripheral surface is subjected to cleaning. Maintaining the shape of the depression (specified depth, diameter,
And maintaining the area ratio). On the outer peripheral surface of the cooling drum in contact with the molten metal, the solidified shell is repeatedly generated and released,
The initial favorable depression wears out. Further, even when brushing the surface of the drum used to keep the outer peripheral surface of the cooling drum clean, scraping of the tips of the brush causes abrasion of the depression.

In order to reduce the effect of such abrasion, if the depth of the initial depression is made larger than necessary, foreign matters such as oxides will be deposited on the bottom of the depression and cannot be removed even by cleaning the drum.
Not only the effect of the depression is reduced, but also the heat flux of the drum is reduced. Therefore, if such abrasion progresses without making the depth of the recess unnecessarily large, it is necessary to reprocess the recess. However, none of the above-mentioned prior arts suggests such reprocessing of the cooling drum recess. Absent.

The present invention solves the problems of the prior art in the continuous casting of thin cast slabs, especially in the surface rework of the cooling drum.

[0008]

The present invention has a diameter on its surface.
0.1 to 1.2 mm, average depth 50 to 100 mu m, the area ratio 20
Before continuously casting a thin cast piece with a continuous casting machine having a cooling drum having an initial depression having a circular or oval opening of -60%, before the average depth of the initial depression is 30 μm or less. The surface of the cooling drum is shot-blasted so that the average depth of the initial depression is 50 to 100 μm.
The main idea is to restart the casting after the m is formed into m , which makes it possible to obtain a sound slab extremely easily.

In the present invention, the initial depression is a depression formed on the surface of a smooth cooling drum in which the depression is not formed. The initial depressions have a diameter of 0.1 to 1.2 mm, an average depth of 30 to 100 μm , and an area ratio of 20 to 60% .
When casting is performed using a cooling drum having one or more of the numerical values deviated, cracks occur on the surface of the slab. Therefore, the flat Hitoshifuka of the average depth of the depression when subjected to shot blasting to a surface of the cooling drum is required to be 30μm or more depressions early is to reduce by casting, in view of the reduced cost It was 50 to 100 μm.

The area ratio of the initial depression in the present invention is
It is defined by the following equation (1).

[0011]

[Equation 1]

Where S is the peripheral area of the cooling drum, Si is the area surrounded by the periphery of the initial depression i, di is the diameter of the initial depression i (the oblong depression is the average value of the major axis and the minor axis) of the present invention. The closest distance L between adjacent initial depressions is 0.
1 to 2 mm, and the ratio of the minor axis to the major axis of the initial depression of the ellipse shape is 0.6 or more, both of which are preferable for preventing the surface crack of the slab.

In the present invention, when the shot blasting is performed to form a required depression on the surface of the cooling drum, in the case of processing an area wider than one projection width, 1/3 to 1 of one projection width. / 2 is piled up and processed sequentially. When a cast piece is cast with a cooling drum having a recess thus repaired (hereinafter referred to as a repair recess), fine cracks on the surface of the cast piece and uneven luster can be prevented.

After the initial depression is worn away by the above casting, shot blasting can be performed again to perform casting. In this way, after performing shot blasting a plurality of times and casting, initial depressions are formed on the surface of the cooling drum.
In order to form the initial depressions on the surface of the cooling drum, a photoetching method, an electron beam processing method, a laser processing method, and the like, and a combination of these and shot blast processing are used.

In order to increase the depth of the depression by performing shot blasting on the surface of the cooling drum in which the depression is formed, it is necessary for the shot shot to collide with the bottom surface of the depression with a high probability. The probability P that the shot Z shown in FIG. 1 is projected in the circle of the depression A surrounded by the oblique line is determined by the ratio of the depression diameter (D) and the shot diameter (d),
It is defined by the equation (2).

[0016] D: hollow diameter (average value of long diameter and short diameter in case of oval shape) (mm) d: shot diameter (mm) FIG. 2 shows probability P of shot hitting depression A, depression diameter D and shot diameter d. The relationship with the ratio d / D is shown. From Figure 2 d /
When D exceeds 0.5, the probability P decreases significantly. When the shot diameter d is less than 0.15 mm, the kinetic energy of the shot is small and it is difficult to obtain an effective depression. Therefore, the shot diameter d preferably satisfies the expression (3).

0.15 mm ≦ d ≦ 0.5 × D (3)

[0018]

The inventor of the present invention has variously studied the relationship between the depression on the surface of the cooling drum and the surface crack of the cast slab. When a predetermined amount is cast using a cooling drum having an initial depression on the surface, the depression is worn away. It was found that when shot blast was randomly projected on such a surface, a recess having a required depth could be formed due to the effect of the remaining recess.
FIG. 3 shows the cross-sectional shape of the depression A, (A) is the initial depression,
(B) is a dent that has been worn and used in casting, and (C) is a dent that has been repaired after shot blasting is applied to (B). As shown in FIGS. 4A to 4C, when shot blasting is performed, a protrusion t is formed at the peripheral edge of the depression a formed by the shot Z. Therefore, in FIG. 3C, the depression a and the projection t are formed by the shot. The shot a formed in the depression A increases the volume of the depression A, and the amount of air gap formed between the surface of the molten steel and the bottom surface of the depression A increases accordingly. The air gap is also formed by the depression a formed in the flat area S by the shot. The surface cooling of the slab is prevented by the gradual cooling action of the slab by the air gaps, so that the depth of the depression is from L1 in FIG. 3 (B) to L2 in FIG. 3 (C).
It has increased substantially. As a result of casting using a cooling drum provided with a repair depression as shown in FIG.
It was confirmed that cracks on the surface of the slab could be prevented.

The results are shown in FIG. FIG. 5 is obtained under the following conditions. First, cooling drum width: 800m
m, diameter: 1200 mm, surface: Ni-plated twin-drum type continuous casting machine, molten steel of steel type: SUS304 was rapidly solidified, drawn at a casting speed of 80 m / mim, and cast pieces with a casting thickness of 2.3 mm were obtained. . The surface of the cooling drum is photoetched to have an average depth of 50 to 100 μm, a diameter of 0.1 to 1.2 mm, and an average area ratio of 20 to
60% of the initial depression is formed.

After the above casting was repeated, the average depth of the depression was 29 μm, the effect of the depression was reduced, and cracks were generated on the surface of the slab. Therefore, shot blasting was performed on the surface of the cooling drum under the following conditions. That is, using a pneumatic projection type blaster, steel ball shot (diameter 0.15 ~ 0.
6 mm martensite), projection air pressure: 4-7 kg / c
A repair depression was formed by changing the depth and area ratio of the depression as shown in FIG. 5 by m ² and a projection width of 20 mm per time.

A slab is produced under the same casting conditions as above by using the cooling drum whose surface is reworked as described above.
The amount of surface crack generation of the obtained slab was investigated. As shown in FIG. 5, the area without cracks has an average depth of 30 μm or more,
It was found that it was when the repair dents having an average area ratio of 20% or more were formed.

[0022]

EXAMPLE First, the continuous casting machine used in the present invention will be described with reference to FIG. 6. In the continuous casting machine, cooling drums 1, 1 are arranged so as to rotate in parallel and in opposite directions. Side dams 2 and 2 are provided on both end surfaces of the molten metal to form a pool 4, and the molten metal 5 in the pool is cooled by rotating the cooling drums 1 to cast a thin slab S. ing. Further, the side dams 2 and 2 are pressed against both end surfaces of the cooling drums 1 and 1, and maintain a sealed state due to wear due to rotation of the cooling drums to prevent hot water leakage. A is an initial depression. The depression A is formed into the depression shape shown in Table 1 by photo etching or shot blasting.

Casting was started with such an apparatus, and the casting was continued based on the above-mentioned casting conditions. Test No. 1 in Table 1
It is 1,1-2,2-1,4-1,5-1. Further, thereafter, shot blasting with a projection width of 20 mm was performed online on the surface of the cooling drum having the worn out initial depressions to form repaired depressions shown in Table 1 and restart casting. Test No. 1-3, 1-4, 2-2, 3-2, 4- in Table 1
It is 2,4-3,4-4,4-5. Test No. 1
-5 shows the casting result after performing the shot blasting again on the cooling roll of Test No. 1-4 to repair the depression.
As an example, FIG. 7 shows the surface sectional shape of the cooling drums of Test Nos. 2-1 and 2-2. (A) is an initial depression (before shot blasting) (2-1), and (b) is a repairing depression (after shot blasting) (2-2).

[0024]

[Table 1]

The presence of fine cracks on the surface of the slab thus obtained and the presence of uneven gloss were observed. Table 1 shows the results. As shown in Table 1, there were no fine cracks on the surface of the cast piece cast by the method of the present invention, and no uneven gloss. That is, even if cracks occur on the surface of the slab due to lack of the depth of the initial dent due to casting (Test No. 1-2, 2
-1, 4-1), by subjecting this to shot blasting to deepen the depth of the depression (Test No. 1-3, 2-).
2,3-2,4-2,4-3; 50μm or more deep)
It was possible to eliminate the occurrence of cracks.

In addition, when the depth of the repair dent cannot be ensured in the casting due to the casting, it is not possible to secure a region where cracks do not occur (Test No. 1-
Even in 4), it was possible to increase the depth and eliminate fine cracks by performing shot blasting again (Test No. 1).
-5). Further, by overlapping the projection width in shot blasting at least one-third of the projection width at least once, no light and shade stripes were generated, and uneven gloss and cracks could be completely eliminated (Test No. 4-2, 4). -3). Test No. 4-4
In No. 4-5, since the overlapping amount was insufficient, unevenness of gloss was caused by unevenness of the depression caused by the shot, and slight cracks were generated at that portion.

Test No. 5-1 is a case where only shot blasting is performed, but in order to make the recess depth to be the required depth (the shot diameter must be increased, the recesses due to the shots overlap, and As a result, the diameter of the dents became excessively large, which caused uneven gloss, and in this case, it was difficult to achieve both sufficient pit depth and prevention of uneven gloss.

[0028]

As described above, according to the present invention, the depressions on the surface of the cooling drum can be easily formed on-line (above or to the side of the casting machine) at the depth and area ratio of the region where cracks do not occur. Since it is possible to reduce the reprocessing period and cost, the industrial effect is great.

[Brief description of drawings]

FIG. 1 shows how a shot is projected onto the bottom surface of a depression.

FIG. 2 shows the probability that a shot collides with the bottom surface of a depression.

FIG. 3 shows a situation in which the depth of the depression is increased by the method of the present invention.

FIG. 4 shows a situation in which the surface of the cooling drum is deformed by performing shot blasting.

FIG. 5 shows the relationship between the depth of depression and the area ratio of depression obtained by the method of the present invention, and the amount of cracking on the surface of the slab.

FIG. 6 is a perspective view of a twin-drum type continuous casting machine for carrying out the present invention.

FIG. 7 is an enlarged cross-sectional view of the surface of the cooling drum, in which (a) shows the state of the drum surface before carrying out the present invention and (b) shows the state of the drum surface after carrying out the present invention.

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 ... Cooling drum 2 ... Side dam 3 ... Molten discharge nozzle 4 ... Molten pool part 5 ... Molten metal A ... Dimple D ... Dotted diameter S ... Thin cast piece a ... Dotted by shot d ... Dotted diameter by shot t ... Projection by shot z ... shot

─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. ⁶ Identification number Internal reference number FI Technical display location B24C 1/04 Z (72) Inventor Kensuke Shimomura 3434 Shimada, Hikari City, Yamaguchi Prefecture Nippon Steel shares (72) Inventor Mizuchi Isao 3434 Shimada, Hikari City, Yamaguchi Prefecture Nippon Steel Corporation Hikari Steel Co., Ltd.

Claims (3)

[Claims] 1. A cooling drum having on its surface an initial depression having a circular or oval opening having a diameter of 0.1 to 1.2 mm, an average depth of 50 to 100 μm , and an area ratio of 20 to 60%. Thin cast piece is continuously cast by a continuous casting machine having, and before the average depth of the initial depression is 30 μm or less, the surface of the cooling drum is subjected to shot blasting to reduce the average depth of the initial depression. after forming the 50 to 100 mu m, the thin cast strip method continuous casting, characterized in that to resume the casting. 2. The method according to claim 1, wherein when performing shot blasting on the surface of the cooling drum, the projections are sequentially performed while overlapping one-third to one-half of a single projection width. 3. The surface processing for forming an initial depression on the surface of the cooling drum is performed by any one of a photoetching method, an electron beam processing method and a laser processing method.
The described method.