Advanced microstructural characterization of the intergranular oxidation of Alloy 600Bertali et al., 2015
View PDF- Document ID
- 17914287969667532379
- Author
- Bertali G
- Scenini F
- Burke M
- Publication year
- Publication venue
- Corrosion Science
External Links
Snippet
Oxidation of solution-annealed Alloy 600 has been performed in a hydrogenated steam environment, which is considered to simulate PWR primary water exposure. FIB and analytical TEM characterization, coupled with detailed SEM analyses, provided unequivocal …
- 230000003647 oxidation 0 title abstract description 71
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N23/00—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons
- G01N23/22—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons by measuring secondary emission
- G01N23/225—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons by measuring secondary emission using electron or ion microprobe or incident electron or ion beam
- G01N23/2251—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons by measuring secondary emission using electron or ion microprobe or incident electron or ion beam with incident electron beam
- G01N23/2252—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons by measuring secondary emission using electron or ion microprobe or incident electron or ion beam with incident electron beam and measuring excited X-rays
-
- G—PHYSICS
- G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
- G21C—NUCLEAR REACTORS
- G21C17/00—Monitoring; Testing ; Maintaining
- G21C17/02—Devices or arrangements for monitoring coolant or moderator
- G21C17/022—Devices or arrangements for monitoring coolant or moderator for monitoring liquid coolants or moderators
- G21C17/0225—Chemical surface treatment, e.g. corrosion
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Bertali et al. | Advanced microstructural characterization of the intergranular oxidation of Alloy 600 | |
| Bertali et al. | The intergranular oxidation susceptibility of thermally–treated Alloy 600 | |
| Lozano-Perez et al. | Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content | |
| Bertali et al. | The effect of residual stress on the Preferential Intergranular Oxidation of Alloy 600 | |
| Kumar et al. | Microstructural stability and mechanical behavior of FeNiMnCr high entropy alloy under ion irradiation | |
| Lim et al. | Intergranular oxidation of Ni-based Alloy 600 in a simulated PWR primary water environment | |
| Kuang et al. | A high-resolution characterization of irradiation-assisted stress corrosion cracking of proton-irradiated 316L stainless steel in simulated pressurized water reactor primary water | |
| Bruemmer et al. | Linking grain boundary microstructure to stress corrosion cracking of cold-rolled alloy 690 in pressurized water reactor primary water | |
| Hou et al. | The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead | |
| Hémery et al. | Effect of oxygen on liquid sodium embrittlement of T91 martensitic steel | |
| Burke et al. | The application of in situ analytical transmission electron microscopy to the study of preferential intergranular oxidation in Alloy 600 | |
| Persaud et al. | Characterization of initial intergranular oxidation processes in alloy 600 at a sub-nanometer scale | |
| Xie et al. | Characterization of stress corrosion cracks in Ni-based weld alloys 52, 52M and 152 grown in high-temperature water | |
| Lozano-Perez et al. | TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions | |
| Shen et al. | The effects of intergranular carbides on the grain boundary oxidation and cracking in a cold-worked Alloy 600 | |
| Persaud et al. | High resolution characterization of Pb-SCC in Alloy 800 exposed to 330° C mildly caustic environments | |
| Kuang et al. | Insights into the roles of intergranular carbides in the initiation of intergranular stress corrosion cracking of alloy 690 in simulated PWR primary water | |
| Behnamian et al. | Characterization of oxide layer and micro-crack initiation in alloy 316L stainless steel after 20,000 h exposure to supercritical water at 500° C | |
| Du et al. | IASCC of neutron irradiated 316 stainless steel to 125 dpa | |
| Persaud et al. | High resolution characterization of sulfur-assisted degradation in alloy 800 | |
| Persaud et al. | The influence of the high Fe and Cr contents of Alloy 800 on its inter-and intragranular oxidation tendency in 480 C hydrogenated steam | |
| Chen et al. | A study on the surface and crack tip oxidation of alloy 600 through high-resolution characterization | |
| Carter et al. | On the influence of microstructure on the neutron irradiation response of HIPed SA508 steel for nuclear applications | |
| Coghlan et al. | The effect of microstructure on the oxidation and carburisation of 9Cr-1Mo steel exposed to CO2 | |
| Jiang et al. | Effect of Mn addition on the tellurium embrittlement resistance of GH3535 alloy |