Improvement of surface roughness for 4H-SiC epilayers grown on 4 off-axis substrates

Aigo et al., 2010

Document ID
4494773958080732197
Author
Aigo T
Tsuge H
Yashiro H
Fujimoto T
Katsuno M
Nakabayashi M
Hoshino T
Ohashi W
Publication year
Publication venue
Materials Science Forum

External Links

Snippet

The epitaxial growth process was optimized in order to obtain good surface morphology for epilayers grown on 4˚ off-axis substrates. The optimization was carried out from growth temperatures and gas chemistry including C/Si ratio. Step-bunching was significantly …
Continue reading at www.scientific.net (other versions)

Classifications

    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02524—Group 14 semiconducting materials
    • H01L21/02529—Silicon carbide
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02367—Substrates
    • H01L21/0237—Materials
    • H01L21/02373—Group 14 semiconducting materials
    • H01L21/02381—Silicon, silicon germanium, germanium
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02612—Formation types
    • H01L21/02617—Deposition types
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic System or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
    • H01L21/302—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to change their surface-physical characteristics or shape, e.g. etching, polishing, cutting
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L29/00—Semiconductor devices adapted for rectifying, amplifying, oscillating or switching, or capacitors or resistors with at least one potential-jump barrier or surface barrier, e.g. PN junction depletion layer or carrier concentration layer; Details of semiconductor bodies or of electrodes thereof; Multistep manufacturing processes therefor
    • H01L29/02—Semiconductor bodies; Multistep manufacturing processes therefor
    • H01L29/12—Semiconductor bodies; Multistep manufacturing processes therefor characterised by the materials of which they are formed
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/10—Inorganic compounds or compositions
    • C30B29/40—AIIIBV compounds wherein A is B, Al, Ga, In or Tl and B is N, P, As, Sb or Bi
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/02—Elements
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B33/00—After-treatment of single crystals or homogeneous polycrystalline material with defined structure

Similar Documents

Publication Publication Date Title
US9337277B2 (en) High voltage power semiconductor device on SiC
Burk et al. SiC Epitaxial Layer Growth in a 6x150 mm Warm-Wall Planetary Reactor
Mao et al. Surface defects in 4H-SiC: Properties, characterizations and passivation schemes
Li et al. Reduction of morphological defects in 4H-SiC epitaxial layers
Lee et al. Properties of GaN epitaxial layers grown on 6H-SiC (0001) by plasma-assisted molecular beam epitaxy
Kojima et al. 4H-SiC homoepitaxial growth on substrate with vicinal off-angle lower than 1
Kimoto et al. Homoepitaxial growth of 4H–SiC (033̄8) and nitrogen doping by chemical vapor deposition
Miyazawa et al. Thick 4h-sic epitaxial growth and defect reduction for very high voltage bipolar devices
Dojima et al. Macro Step Bunching/Debunching Engineering on 4 off 4H-SiC (0001) to Control the BPD-TED Conversion Ratio by Dynamic AGE-ing®
Bogumilowicz et al. Realization and characterization of thin single crystal Ge films on sapphire
Ogawa et al. Realization of cathodoluminescence in the 180 nm spectral range by suppressing thermal stress in mist chemical vapor deposition of rocksalt-structured MgZnO films
Aigo et al. Improvement of surface roughness for 4H-SiC epilayers grown on 4 off-axis substrates
Tsuchida et al. Low-pressure fast growth and characterization of 4H-SiC epilayers
Lee et al. Comparative study of 4H-SiC epitaxial layers grown on 4° off-axis Si-and C-face substrates using bistrimethylsilylmethane precursor
Hassan et al. On-axis homoepitaxial growth of 4H-SiC PiN structure for high power applications
Sudoh et al. BPD-TED Conversion in the SiC Substrate after High-Temperature Si-VE
Tamura et al. Starting point of step-bunching defects on 4H-SiC Si-face substrates
Wu et al. Characterization of dislocations and micropipes in 4H n+ SiC substrates
Lilja et al. Influence of growth temperature on carrier lifetime in 4H-SiC epilayers
Sun et al. Formation and reduction of large growth pits on 100 mm 4° 4H-SiC
Krishnan et al. Vanadium doping using VCl4 source during the chloro-carbon epitaxial growth of 4H-SiC
Zhang et al. High Growth Rate (up to 20 µm/h) SiC epitaxy in a horizontal hot-wall reactor
Zhang et al. Defect reduction paths in SiC Epitaxy
Lilja et al. The Effect of Growth Conditions on Carrier Lifetime in N-Type 4H-SiC Epitaxial Layers
Kojima et al. Improvement of Homoepitaxial Layer Quality Grown on 4H-SiС Si-Face Substrate Lower than 1 Degree Off Angle