The fiber sheet is composed of a solubilized collagen fiber having ≤5 mass% ash by ash measuring method and having an isoionic point of ≤5.0 pH and has a basis weight of ≤50 g/m^2.例文帳に追加

繊維シートは、灰分測定法による灰分が５質量％以下で等イオン点がｐＨ５．０以下である可溶化コラーゲン繊維からなり、目付が５０ｇ／ｍ^２以下である。 - 特許庁

In the blending, the unit cement quantity is controlled to 190 to 220 kg/m^3, the unit paper sludge ash quantity is controlled to 80 to 120 kg/m^3, the unit pearlite quantity is controlled to 100 to 125 kg/m^3, and alkali resistant natural cellulose short fiber is mixed in amount of 4 to 6 kg/m^3.例文帳に追加

配合における単位セメント量を１９０〜２２０ｋｇ／ｃｍ^3、単位ペーパースラッジ灰量を８０〜１２０ｋｇ／ｃｍ^3、単位パーライト量を１００〜１２５ｋｇ／ｃｍ^3とし、耐アルカリ性天然セルロースの短繊維を４〜６ｋｇ／ｃｍ^3混合する。 - 特許庁

In the application for a hollow block product, the super stiff-consistency concrete instantly releasable from the form and having high product strength is obtained by blending PS ash to be 280-320 kg/m^3 in unit cement quantity and 160-240 kg/m^3 in unit PS ash quantity.例文帳に追加

中空ブロック製品への適用においては、超硬練りの即脱可能なコンクリートとして、単位セメント量が２８０〜３２０ｋｇ／ｍ^3、かつ単位ＰＳ灰量が１６０〜２４０ｋｇ／ｍ^3となるようにＰＳ灰を配合することにより、高い製品強度が得られる。 - 特許庁

To continuously collect metal M such as a can satisfactory in quality by classifying refuse incineration ash A from contained metal M by a trommel 2, and peeling contaminants, coating, or rust or the like on the surface of the metal M.例文帳に追加

本発明はトロンメル２によってごみ焼却灰Ａと含有金属類Ｍとを分級し、該金属類Ｍの表面の附着汚物、塗装又は錆等を剥落して品質良好な缶等の金属類Ｍを連続的に回収することを目的とする。 - 特許庁

The hydraulic coating material having sulfuric acid-resistance comprises a slag having a BET specific surface area of 0.75-3.3 m^2/g and/or a fly ash having a BET specific surface area of 1.5-3.3 m^2/g, an aggregate, cement and a water reducing agent.例文帳に追加

ＢＥＴ比表面積０．７５〜３．３ｍ^2／ｇのスラグ及び／又はＢＥＴ比表面積１．５〜３．３ｍ^2／ｇのフライアッシュ、骨材、セメント及び減水剤を含有してなる耐硫酸性水硬塗材。 - 特許庁

Coal ash and soft earth are mixed together to form flake-like solidified soil having a bulk density of 8.5 kN/m^3 or less, which is pneumatically pumped onto the soft ground.例文帳に追加

石炭灰と軟弱土とを混合してかさ密度が８．５ｋＮ／ｍ^３以下のフレーク状の固化処理土を形成し、これを軟弱地盤上へ空気圧送する。 - 特許庁

A newsprint paper having 38-48 g/m^2 basis weight is provided, wherein the newsprint paper contains at least starch and polyvinyl alcohol and the ash based on JIS P 8251 is 7.5-12.0% which ash at least comprises ≥50 mass% clay and <5 mass% calcium carbonate (CaCO_3).例文帳に追加

坪量３８〜４８ｇ／ｍ^2の新聞用紙において、少なくとも澱粉及びポリビニルアルコールを含有し、ＪＩＳ Ｐ ８２５１に基づく灰分が７．５〜１２．０％で、この灰分は、少なくともクレーが５０質量％以上、炭酸カルシウム（ＣａＣＯ_3）が５質量％未満である。 - 特許庁

The method for selecting a fly ash is characterized by selecting from one or more kinds of fly ashes containing α-quartz, a fly ash having a BET specific surface area of 5.0 m^2/g or less and a lattice constant b of the α-quartz obtained by Rietveld analysis of 0.4935 nm or less as a cement admixture.例文帳に追加

α−石英を含有する１種以上のフライアッシュから、セメント混合材として、ＢＥＴ比表面積が５．０ｍ^２／ｇ以下であり、且つリートベルト解析法で求められる前記α−石英の格子定数ｂが０．４９３５ｎｍ以下である、フライアッシュを選定することを特徴とするフライアッシュの選定方法。 - 特許庁