polymerization terminatorとは 意味・読み方・使い方

To provide such an effectively terminating method of a polymerization reaction using a complex-based catalyst as has a little influence on the catalyst activity even when carrying out the next reaction in the remaining condition of a terminator.例文帳に追加

錯体系触媒を使用する重合反応における効果的な停止方法であって、停止剤が残存した状態で次の反応を行っても触媒活性への影響が小さい停止方法を提供すること。 - 特許庁

A cyclic olefin compound is subjected to continuous metathesis polymerization in the presence of a ruthenium carbene catalyst and a tertiary phosphorus compound for a residence time of 10-300 seconds, and a reaction terminator is continuously added to the resulting reaction solution.例文帳に追加

環状オレフィン化合物をルテニウムカルベン触媒と第三級りん化合物の存在下に滞留時間１０秒〜３００秒で連続的にメタセシス重合し、得られた反応液に連続的に反応停止剤を添加する。 - 特許庁

To provide a method for producing a straight-chain polycarbonate having improved washability in the washing step in producing the polycarbonate having improved flowability by interfacial polymerization with the use of a long-chain monoalkylphenol as the chain-end terminator.例文帳に追加

末端停止剤として長鎖モノアルキルフェノールを用い、流動性が改良された直鎖状ポリカーボネートを界面重縮合法により製造するに際し、洗浄工程における洗浄性が向上した該ポリカーボネートの製造方法を提供すること。 - 特許庁

The aqueous dispersion of polyurethane resin is obtained by dispersing a polyurethane resin in water which polyurethane resin is obtained by reacting polymerization components comprising a polyol having 500-10,000 number average molecular weight, a polyisocyanate compound, a chain extender and a chain length terminator, wherein the chain length terminator comprises a compound having an active hydrogen-containing functional group and an oxazolidine skeleton.例文帳に追加

数平均分子量が５００〜１００００のポリオール、ポリイソシアネート化合物、鎖伸長剤および鎖長停止剤を含有した重合成分を反応させて得られるポリウレタン樹脂であって、前記鎖長停止剤が活性水素を有する官能基とオキサゾリジン骨格とを有する化合物を含有することを特徴とするポリウレタン樹脂を、水に分散させてなる、ポリウレタン樹脂の水分散液を用いる。 - 特許庁

Preferably, in the method for producing the block copolymer, after the reaction, a reaction terminator is further added to the polymerization reaction, and catalytically active sites originated from (C) the metal carbene complex catalyst bound to one end of the polymer and halogen atoms or the like coordinated on the central metal are removed, respectively.例文帳に追加

このとき、上記反応のあとに更に、反応停止剤を加えて重合反応を停止させ、重合体の一端に結合した金属カルベン錯体触媒（Ｃ）由来の触媒活性部位を除くとともに、その中心金属に配位したハロゲン原子等も除くことが好ましい。 - 特許庁

The reduction of hysteresis in a silica-filled vulcanized elastomeric compound is achieved through the steps of: mixing a diene monomer and optionally a monovinyl aromatic monomer with a lithium amine initiator and, optionally, a modifier; effecting polymerization conditions; terminating polymerization with an amino group-producing terminator to form an amine-functionalized diene elastomer; compounding the amine-functionalized diene elastomer with an amorphous silica filler and a vulcanizing agent; and effecting vulcanization.例文帳に追加

リチウムアミン開始剤とジエン単量体と任意にモノビニル芳香族単量体と任意に修飾剤を混合し；重合条件を確立し；重合をアミノ基産生停止剤で停止させることでアミン官能化ジエンエラストマーを生じさせ；このアミン官能化ジエンエラストマーを非晶質シリカ充填材および加硫剤と一緒にしてコンパウンドにし；そして加硫を達成することを通して、シリカ充填加硫エラストマーコンパウンドのヒステリシスを低下させる。 - 特許庁

The method for producing a modified conjugated diene polymer is provided, which includes (1) addition of water or 5C or less alcohol as a reaction terminator immediately after polymerization of a conjugated diene polymer, (2) subsequent cooling of the reaction system, and (3) subsequent hydrosilylation of the modified conjugated diene polymer by an organosilane compound.例文帳に追加

変性共役ジエン重合体の製造方法において、（１）共役ジエン重合体を重合直後に、反応停止剤として水あるいは炭素数が５以下のアルコールを投入、（２）次いで反応系を冷却、（３）次いで前記変性共役ジエン重合体を有機シラン化合物によりヒドロシリル化することを特徴とする変性共役ジエン重合体の製造方法を提供する。 - 特許庁