solution orientedとは 意味・読み方・使い方

In addition, this manufacturing method of a sample used for the determination is characterized by manufacturing the oriented solid film by drying the solution prepared by mixing an aqueous solution containing DNAs with molecules bonded to the DNAs in a magnetic field by disposing the solution on a substrate.例文帳に追加

また、前記判定に使用する試料の作製方法において、ＤＮＡを含む水溶液とＤＮＡに結合する分子を混ぜた溶液を基板上に置いて磁場中で乾燥させることにより配向した固体膜を作製することを特徴とする。 - 特許庁

To provide a method for manufacturing a perfect solid solution nitriding magnetic flux density grain-oriented silicon steel sheet having satisfactory glass film formation and excellent magnetic characteristics.例文帳に追加

良好なグラス皮膜形成と優れた磁気特性を有する完全固溶窒化型高磁束密度方向性電磁鋼板の製造方法を提供する。 - 特許庁

The ferromagnetic oxide semiconductor thin film of the present invention has desired conductivity and is composed of a c-axially oriented ilmenite-hematite solid solution orderly phase thin film.例文帳に追加

本発明に係る強磁性酸化物半導体薄膜は、所望の伝導性を有し、かつｃ軸配向したイルメナイト・ヘマタイト固溶体秩序相薄膜からなる。 - 特許庁

In manufacturing of a liquid crystal device 100, after forming inorganic oriented films 16, 26 by oblique deposition in an inorganic oriented film forming step, surface insulator films 17, 27 are formed on the surface side of the inorganic oriented films 16, 26 by liquid phase deposition utilizing deposition from a saturated solution in a surface insulator film forming step.例文帳に追加

液晶装置１００を製造するにあたって、無機配向膜形成工程において斜方蒸着により無機配向膜１６、２６を形成した後、表面絶縁膜形成工程では、無機配向膜１６、２６の表面側に、飽和溶液からの析出を利用した液相析出法により、表面絶縁膜１７、２７を形成する。 - 特許庁

The grain oriented silicon steel sheet having the exposed base iron is brought into contact with an aqueous acidic solution containing hydrochloric acid of 0.1 to 5% in mass ratio and after the mass of the grain oriented silicon steel sheet is decreased in a range of 0.5 to 50 g/m2 on both surfaces of the steel sheet, following which the insulating layer film is formed.例文帳に追加

地鉄面が露出した方向性電磁鋼板を、質量比で0.1〜5%の塩酸を含む酸性水溶液に接触させ、該方向性電磁鋼板の質量を鋼板両面で0.5〜50g/m^2の範囲で減少させた後、絶縁被膜を形成する。 - 特許庁

In the particulate deposition method, a particulate dispersion solution 30 is applied to the surface of the substrate 10 to form a particulate dispersion solution layer, and then a state with a meniscus-forming means 20 brought into contact with the particulate dispersion solution layer is formed, to obtain a particulate deposition layer 32 in which particulates 31 are oriented with respect to the surface of the substrate 10.例文帳に追加

微粒子堆積方法は、微粒子分散溶液３０を基体１０上に塗布して微粒子分散溶液層を形成した後、メニスカス形成手段２０を該微粒子分散溶液層に接触した状態とし、以て、基体１０表面に対して微粒子３１が配向した状態の微粒子堆積層３２を得る。 - 特許庁

To provide a manufacturing method in which a coating solution containing a lyotropic liquid crystal compound and a solvent is applied on a base material and the orientation direction of the compound is parallel (parallel-oriented) to the application direction.例文帳に追加

リオトロピック液晶化合物と溶媒を含むコーティング液を、基材に塗布し、該化合物の配向方向を、塗布方向に平行（平行配向）する製造方法を提供する。 - 特許庁

The ITO film strongly oriented in the (400) plane can be manufactured, by forming the film using a spray pyrolysis method by using a starting material solution having a concentration of 0.3-1 mol/l.例文帳に追加

濃度が０．３ｍｏｌ／ｌ〜１ｍｏｌ／ｌの出発原料液を用いてスプレー熱分解法により成膜することにより、（４００）面に強配向したＩＴＯ膜を製造することができる。 - 特許庁