To obtain a product which has no casting defects such as shrinkage cavity, misrun, cold shut, gas defect, etc., when a casting is produced.例文帳に追加

鋳物を製造するにあたり引け巣、不廻り、湯境い、ガス欠陥等の鋳造欠陥が無い製品を得る。 - 特許庁

To allow molding of a high-quality engine cylinder block by preventing misrun of molten metal when casting the cylinder block of an engine.例文帳に追加

エンジンのシリンダブロックを鋳造成形する場合に、湯回り不良が生じないようにして高品質のものが成形されるようにする。 - 特許庁

To provide a technique in which a cast product composed of a metal- ceramics composite material having no defect can be obtained at high yield by preventing invasion of bubble developed in molten metal into the product and further, preventing misrun.例文帳に追加

溶湯に発生した泡が製品内に入るのを防止し、さらに、湯廻り不良を防いで、欠陥のない金属−セラミックス複合材料からなる鋳造品を高歩留りで得られる技術を提供する。 - 特許庁

To provide a process of manufacturing a mold for vulcanizing and molding a tyre which can assure air leakage by a good casting patch section by preventing a misrun at the time of a first shot and a second shot casting from occurring.例文帳に追加

第１ショット，第２ショットの鋳造時における湯回り不良を防止し、良好な鋳継ぎ部によるエアーリークを確保することが出来るタイヤ加硫成形用金型の製造方法を提供することを目的とする。 - 特許庁

To provide a mold wash for metal molds which insures casting in a manner as not to give rise to casting defects, such as a casting surface defect, chill and misrun, at the time of casting cast iron castings and cast steel castings by a low-pressure casting method.例文帳に追加

低圧鋳造法によって鋳鉄鋳物や鋳鋼鋳物を鋳造するにあたり、鋳物に鋳肌不良、チル及び湯廻り不良などの鋳物欠陥が発生しないようにすることの可能な金型用塗型剤を提供する。 - 特許庁

To provide a metallic mold for casting with which the rate of cast defect, such as misrun, is reduced compared with the conventional mold and a casting excellent in mechanical strength can be obtained when a wheel for vehicle having thinner thickness is formed by casting.例文帳に追加

より薄肉化した車両用ホイールを鋳造成形するに際し、湯まわり不良等の鋳造欠陥発生率が従来より少なく、機械的強度に優れたものを得られる鋳造用金型を提供すること。 - 特許庁

Cooling speed of the molten metal is reduced with the heat and the lowering of fluidity of the molten metal is delayed and the development of misrun in the thin part is prevented and also, the brittleness on the surface part of the casting can be prevented.例文帳に追加

この熱で溶融金属の冷却速度を小さくし、溶融金属の流動性が低下するのを遅らせ、また薄肉部の湯廻り不良の発生を防止すると共に鋳物表面部の脆性を防ぐことができる。 - 特許庁