JP2837460B2 - Composite film for vertical pillow packaging - Google Patents
Composite film for vertical pillow packagingInfo
- Publication number
- JP2837460B2 JP2837460B2 JP24858889A JP24858889A JP2837460B2 JP 2837460 B2 JP2837460 B2 JP 2837460B2 JP 24858889 A JP24858889 A JP 24858889A JP 24858889 A JP24858889 A JP 24858889A JP 2837460 B2 JP2837460 B2 JP 2837460B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- composite film
- resin layer
- film
- polyamide resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は複合フイルムであって、特にあんこ、みそ、
接着剤等の粘稠物を包装するのに好適な縦ピロー包装用
複合フイルムに関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial application field) The present invention relates to a composite film, and particularly to bean paste, miso,
The present invention relates to a composite film for vertical pillow packaging suitable for packaging a viscous material such as an adhesive.
（従来の技術及びその課題） 平坦なフイルムから背貼りシールと底部シールを行な
い製袋すると同時または直後に内容物を充填する、いわ
ゆる縦ピロー包装は、粉流体、固形体等各種形態の内容
物を包装する方法として広く行われている。この縦ピロ
ー包装でその内容物として、あんこ、みそ、接着剤等の
粘稠物を包装する場合は、特に優れたフイルム強度や内
容物を容易に絞り出せることが要求されている。(Prior art and its problems) The so-called vertical pillow packaging, in which a back film seal and a bottom seal are made from a flat film and the contents are filled at the same time as or immediately after bag making, so-called vertical pillow packaging is a type of contents such as powdered fluids and solids. It is widely used as a packaging method. When packaging viscous materials such as red bean paste, miso, and adhesive as the contents in this vertical pillow packaging, it is required that the film be particularly excellent in film strength and that the contents be easily squeezed out.
上記縦ピロー包装用として従来から使用されているフ
イルムの例として、延伸した６ナイロン等のポリアミド
樹脂フイルムと低密度ポリエチレンフイルムとをドライ
ラミネートしてなる複合フイルムがある。しかしなが
ら、この複合フイルムでは外層のポリアミド樹脂層に傷
が入り易く、フイルムにピンホールが発生し、またフイ
ルムが硬いために充填包装された粘稠物を絞り出しにく
いという問題があった。An example of a film conventionally used for the vertical pillow packaging is a composite film obtained by dry laminating a stretched polyamide resin film such as nylon 6 and a low-density polyethylene film. However, in this composite film, there is a problem that the outer polyamide resin layer is easily damaged, a pinhole is generated in the film, and the viscous material packed and packaged is difficult to be squeezed out because the film is hard.
（課題を解決するための手段） 本発明はポリアミド樹脂層を２層に分け１層を外層、
他層を中間層とした層構成の複合フイルムであって特定
の物性を有する複合フイルムを使用することにより上記
問題点を解消できることを見出したものであってその要
旨とするところは、 両最外層がポリアミド樹脂層１及びポリオレフィン樹
脂層４であり、中間層としてポリオレフィン樹脂層２及
びポリアミド樹脂層３をポリアミド樹脂層３がポリオレ
フィン樹脂層４側になるように積層してなる複合フイル
ムであって、上記最外層のポリアミド樹脂層１の厚さが
中間層のポリアミド樹脂層３の厚さ以下であり、かつ複
合フイルム全体の３％引張弾性率（縦方向、23℃）が30
〜60Kg/cm2、及びテーバー曲げこわさが９〜20g・cmの
範囲であることを特徴とする縦ピロー包装用複合フイル
ムにある。(Means for Solving the Problems) The present invention divides the polyamide resin layer into two layers, one layer as an outer layer,
It has been found that the above problems can be solved by using a composite film having a specific physical property, which is a composite film having another layer as an intermediate layer. Is a polyamide resin layer 1 and a polyolefin resin layer 4, a composite film obtained by laminating a polyolefin resin layer 2 and a polyamide resin layer 3 as intermediate layers such that the polyamide resin layer 3 is on the polyolefin resin layer 4 side, The thickness of the outermost polyamide resin layer 1 is equal to or less than the thickness of the intermediate polyamide resin layer 3 and the 3% tensile elastic modulus (vertical direction, 23 ° C.) of the entire composite film is 30.
A composite film for vertical pillow packaging, characterized in that the composite film has a thickness of こ 60 kg / cm 2 and a Taber bending stiffness of 9-20 g · cm.
最外層には、シール温度を高くして高速シールを可能
にするため比較的高融点のポリアミド樹脂層１を用いる
ものであり、中間層であるポリオレフィン層２は、もう
一方のポリオレフィン層４とともに中間のポリアミド樹
脂層３をはさんで耐ピンホール性を付与するものであ
る。このポリオレフィン層２はポリアミド樹脂層1,3の
接着層を兼ねるのが好ましい。中間のポリアミド樹脂層
３は引張り強度やガスバリヤー性を付与するが、ポリオ
レフィン層でサンドイッチされているのでたとえ外層に
傷がついてもこのポリアミド樹脂層まで伝播しない。For the outermost layer, a polyamide resin layer 1 having a relatively high melting point is used in order to enable high-speed sealing by increasing the sealing temperature, and the polyolefin layer 2 which is an intermediate layer, together with the other polyolefin layer 4, has an intermediate layer. The pinhole resistance is provided between the polyamide resin layers 3. It is preferable that the polyolefin layer 2 also serves as an adhesive layer for the polyamide resin layers 1 and 3. The intermediate polyamide resin layer 3 imparts tensile strength and gas barrier properties, but does not propagate to the polyamide resin layer even if the outer layer is damaged because it is sandwiched by the polyolefin layer.
また他の最外層のポリオレフィン層４はヒートシール
層である。ここで最外層のポリアミド樹脂層１の厚さを
中間層のポリアミド樹脂層３の厚さ以下とする必要があ
り、厚さが中間層を越えるものでは、複合フイルムにカ
ールが発生し易いという問題がある。The other outermost polyolefin layer 4 is a heat seal layer. Here, it is necessary that the thickness of the outermost polyamide resin layer 1 be equal to or less than the thickness of the intermediate polyamide resin layer 3, and if the thickness exceeds the intermediate layer, the composite film is likely to be curled. There is.
なお、中間層として、他の樹脂層（例えばポリオレフ
ィン層２とポリアミド樹脂層３との間にエチレン−ビニ
ルアルコール共重合樹脂層、ポリアミド樹脂層３とポリ
オレフィン層４との間に接着性樹脂層）を加えてもよ
い。As an intermediate layer, another resin layer (for example, an ethylene-vinyl alcohol copolymer resin layer between the polyolefin layer 2 and the polyamide resin layer 3, an adhesive resin layer between the polyamide resin layer 3 and the polyolefin layer 4) May be added.
本発明におけるポリアミド樹脂としては、６−ナイロ
ン、または６−ナイロンを主体とするコポリアミドが好
適である。As the polyamide resin in the present invention, 6-nylon or a copolyamide mainly composed of 6-nylon is preferable.
また、ポリオレフィン層２としては、低密度ポリエチ
レン、エチレン−酢酸ビニル共重合樹脂等が用いられる
が、直接ポリアミド樹脂層1,3を接着する場合には、不
飽和カルボン酸をグラフトした変性ポリオレフィン樹脂
が好適に用いられる。As the polyolefin layer 2, low-density polyethylene, ethylene-vinyl acetate copolymer resin, or the like is used. When the polyamide resin layers 1 and 3 are directly bonded, a modified polyolefin resin grafted with an unsaturated carboxylic acid is used. It is preferably used.
また、ポリオレフィン層４としては、ヒートシール性
のよいエチレン−ビニル共重合樹脂、低密度ポリエチレ
ン、線状低密度ポリエチレン、アイオノマー等を用い
る。Further, as the polyolefin layer 4, an ethylene-vinyl copolymer resin having good heat sealing properties, low density polyethylene, linear low density polyethylene, ionomer, or the like is used.
本発明の複合フイルムは通常の共押出法により製膜す
ればよく複合フイルム全体の３％引張弾性率（縦方向、
23℃）が30〜60Kg/cm2、及びテーバー曲げこわさが９〜
20g・cmの範囲となるようにする必要がある。ここで上
記引張弾性率はASTMD−638に準拠して測定し試料幅5mm
で３％伸び時の数値であり、テーバー曲げこわさはASTM
D−747に準拠した測定値である（試料3.8cm×1.27c
m）。The composite film of the present invention may be formed into a film by an ordinary co-extrusion method.
23 ℃) is 30 ~ 60Kg / cm 2 , and Taber bending stiffness is 9 ~
It must be in the range of 20 g · cm. Here, the tensile modulus is measured according to ASTM D-638, and the sample width is 5 mm.
Is the value at 3% elongation, and the Taber bending stiffness is ASTM.
It is a measured value based on D-747 (sample 3.8cm x 1.27c
m).
ここで上記３％引張弾性率が30Kg/cm2未満のものでは
充填する粘稠物の重量が大きい場合、フイルムが伸びて
変形するという問題があり、60Kg/cm2を越すものでは、
充填した粘稠物を絞り出しにくいという問題がある。ま
た、同様にテーバー曲げこわさが9g・cm未満のもので
は、フイルムの腰が弱いため取り扱いにくく、20g・cm
を越すものでは、充填した粘稠物を絞り出しにくいとい
う問題がある。In the case where the above 3% tensile modulus is less than 30 kg / cm 2, if the weight of the viscous material to be filled is large, there is a problem that the film is stretched and deformed, and if it exceeds 60 kg / cm 2 ,
There is a problem that it is difficult to squeeze the filled viscous material. Also, if the Taber bending stiffness is less than 9 gcm, it is difficult to handle because the film is weak
In the case of exceeding, there is a problem that it is difficult to squeeze the filled viscous material.
上記引張弾性率とテーバー曲げこわさの範囲を満足し
た複合フイルムを得るには、使用するポリアミド樹脂層
の総厚みを15〜60μｍの範囲とすることが好ましく、15
μｍ未満では引張弾性率が低くなりフイルムが変形し易
く、60μｍを越えるものではテーバー曲げこわさが大き
過ぎるためフイルムが硬くなり充填した粘稠物を絞り出
しにくいという問題がある。同様に複合フイルム全体の
総厚みは70〜100μｍの範囲が好ましく、70μｍ未満で
はピンホールが発生し易く、100μｍを越えるものでは
テーバー曲げこわさが大きくなりフイルムが硬すぎると
いう問題がある。以下本発明を実施例により説明する。In order to obtain a composite film that satisfies the above ranges of tensile modulus and Taber bending stiffness, the total thickness of the polyamide resin layer used is preferably in the range of 15 to 60 μm,
If it is less than μm, the tensile modulus is low and the film tends to be deformed. If it exceeds 60 μm, the Taber bending stiffness is too large, so that the film becomes hard and it is difficult to squeeze out the filled viscous material. Similarly, the total thickness of the entire composite film is preferably in the range of 70 to 100 μm. If it is less than 70 μm, pinholes are likely to occur, and if it exceeds 100 μm, the Taber bending stiffness increases and the film becomes too hard. Hereinafter, the present invention will be described with reference to examples.
（実施例） 実施例１ 第１層（６ナイロン、５μｍ）、第２層（酸変性ポリ
オレフィン、10μｍ）、第３層（６ナイロン、15μ
ｍ）、第４層（酸変性ポリオレフィン）／第５層（線状
低密度ポリエチレン）、第４層と５層の合計厚さは50μ
ｍ。上記第１層乃至第５層を順次配してなる複合フイル
ム（全体の厚み80μ）を共押出し法により製膜した。(Example) Example 1 First layer (6 nylon, 5 μm), second layer (acid-modified polyolefin, 10 μm), third layer (6 nylon, 15 μm)
m), fourth layer (acid-modified polyolefin) / fifth layer (linear low-density polyethylene), total thickness of the fourth and fifth layers is 50 μm
m. A composite film (total thickness: 80 μm) in which the first to fifth layers were sequentially arranged was formed into a film by a co-extrusion method.
得られた上記複合フイルムの３％引張弾性率は44Kg/c
m2、テーバー曲げこわさは12g・cmであった。また、こ
の複合フイルムを使用し、第５層がヒートシール層とな
るように、縦ピロー包装機（オリヒロ社製TNPACK250L
L）に供給してエマルジョンタイプ接着剤3Kgを充填した
後、開口部をシールし包装体を得た。The 3% tensile elastic modulus of the obtained composite film is 44 kg / c.
m 2 , and Taber bending stiffness was 12 g · cm. Also, using this composite film, a vertical pillow packaging machine (TNPACK250L manufactured by Orihiro Co., Ltd.) so that the fifth layer becomes a heat sealing layer.
L), the emulsion type adhesive was filled with 3 kg, and the opening was sealed to obtain a package.
得られた包装体にはカールやフイルムの伸びはなく、
また内容物の絞り出しも容易であり問題なかった。There is no curl or film elongation in the obtained package,
Also, it was easy to squeeze out the contents and there was no problem.
実施例２ 第１層（６ナイロン、８μｍ）、第２層（酸変性ポリ
オレフィン、10μｍ）、第３層（６ナイロン、10μ
ｍ）、第４層（酸変性ポリオレフィン）／第５層（線状
低密度ポリエチレン）、第４層と５層の合計厚さは50μ
ｍ。上記第１層乃至第５層を順次配してなる複合フイル
ムを実施例１と同様の方法で製膜した。得られた複合フ
イルムの３％引張弾性率は46Kg/cm2、テーバー曲げこわ
さは12g・cmであった。また、この複合フイルムを使用
し、実施例１と同様の方法で接着剤を充填して包装体と
しての性能を評価したが問題を生じなかった。Example 2 First layer (6 nylon, 8 μm), second layer (acid-modified polyolefin, 10 μm), third layer (6 nylon, 10 μm)
m), fourth layer (acid-modified polyolefin) / fifth layer (linear low-density polyethylene), total thickness of the fourth and fifth layers is 50 μm
m. A composite film in which the first to fifth layers were sequentially arranged was formed in the same manner as in Example 1. The 3% tensile modulus of the obtained composite film was 46 kg / cm 2 , and the Taber flexural stiffness was 12 g · cm. Using this composite film, an adhesive was filled in the same manner as in Example 1 to evaluate the performance as a package, but no problem occurred.
比較例１ 実施例１に使用した複合フイルムと同一樹脂の組合せ
であって、第１層の厚みが15μｍ、第３層の厚みが５μ
ｍであり、最外層のポリアミド樹脂層が中間層のポリア
ミド樹脂層より大きい以外は実施例１と同一内容で複合
フイルムを得た。３％引張弾性率は44Kg/cm2、テーバー
曲げこわさは11g・cmであった。得られた複合フイルム
について実施例１と同様の評価を行なったところ、包装
体の伸びはなく、また内容物の絞り出しは容易であった
が、フイルムがカールしており作業性が劣っていた。Comparative Example 1 A combination of the composite film and the same resin used in Example 1, wherein the thickness of the first layer was 15 μm and the thickness of the third layer was 5 μm.
m, and the composite film was obtained in the same manner as in Example 1 except that the outermost polyamide resin layer was larger than the intermediate polyamide resin layer. The 3% tensile modulus was 44 kg / cm 2 , and the Taber flexural stiffness was 11 g · cm. When the obtained composite film was evaluated in the same manner as in Example 1, there was no elongation of the package, and the contents were easily squeezed out, but the film was curled and workability was poor.
比較例２ 実施例１に使用した複合フイルムと同一樹脂の組合せ
であって、第１層の厚みが15μｍ、第３層の厚みが20μ
ｍ、第４と５層の総厚みが60μ以外は実施例１と同一内
容で複合フイルム（全体の総厚み105μｍ）を得た。３
％引張弾性率が60Kg/cm2、テーバー曲げこわさが25g・c
mであった。得られた複合フイルムについて実施例と同
様の評価を行なったところ、包装体の伸びやフイルムの
カールはなかったが、フイルムが硬く内容物の絞り出し
が困難という問題があった。Comparative Example 2 A combination of the composite film and the same resin used in Example 1, wherein the thickness of the first layer was 15 μm and the thickness of the third layer was 20 μm.
m, and a composite film (total thickness 105 μm) was obtained in the same manner as in Example 1 except that the total thickness of the fourth and fifth layers was 60 μm. 3
% Tensile modulus is 60Kg / cm 2 , Taber bending stiffness is 25g ・ c
m. When the obtained composite film was evaluated in the same manner as in the example, there was no elongation of the package and no curl of the film, but there was a problem that the film was hard and it was difficult to squeeze out the contents.
比較例３ 実施例１に使用した複合フイルムと同一樹脂の組合せ
であって、第３層の厚みが８μｍ、第４と５層の総厚み
が70μｍである以外は実施例１と同一内容で複合フイル
ム（総厚み93μｍ）を得た。３％引張弾性率は22Kg/c
m2、テーバー曲げこわさは9g・cmであった。得られた複
合フイルムについて実施例１と同様の評価を行なったと
ころ、フイルムのカールはなく、また内容物の絞り出し
は容易であったが、包装体が伸び易いという問題があっ
た。Comparative Example 3 The same composite as Example 1 except that the combination of the composite film and the same resin used in Example 1 was the same resin, and the thickness of the third layer was 8 μm and the total thickness of the fourth and fifth layers was 70 μm. A film (93 μm in total thickness) was obtained. 3% tensile modulus is 22Kg / c
m 2 , Taber bending stiffness was 9 g · cm. The obtained composite film was evaluated in the same manner as in Example 1. As a result, there was no curl of the film and the contents were easily squeezed out, but there was a problem that the package was easily stretched.
（発明の効果） 上述したように本発明の複合フイルムによれば、特に
縦ピロー包装方法によりあんこ、みそ、接着剤等の粘稠
物を包装するのに好適である。(Effect of the Invention) As described above, the composite film of the present invention is particularly suitable for packaging viscous materials such as anko, miso, and adhesive by a vertical pillow packaging method.
Claims (1)
リオレフィン樹脂層（４）であり、中間層としてポリオ
レフィン樹脂層（２）及びポリアミド樹脂層（３）をポ
リアミド樹脂層（３）がポリオレフィン樹脂層（４）側
になるように積層してなる複合フイルムであって、上記
最外層のポリアミド樹脂層（１）の厚さが中間層のポリ
アミド樹脂層（３）の厚さ以下であり、かつ複合フイル
ム全体の３％引張弾性率（縦方向、23℃）が30〜60Kg/c
m2、及びテーバー曲げこわさが９〜20g・cmの範囲であ
ることを特徴とする縦ピロー包装用複合フイルム。The outermost layers are a polyamide resin layer (1) and a polyolefin resin layer (4), and a polyolefin resin layer (2) and a polyamide resin layer (3) are used as an intermediate layer. A composite film laminated so as to be on the resin layer (4) side, wherein the thickness of the outermost polyamide resin layer (1) is equal to or less than the thickness of the intermediate polyamide resin layer (3); And 3% tensile elastic modulus (longitudinal direction, 23 ° C) of the whole composite film is 30-60kg / c
A composite film for vertical pillow packaging, characterized in that m 2 and Taber bending stiffness are in the range of 9 to 20 g · cm.