JP3146806B2 - Electric brush - Google Patents
Electric brushInfo
- Publication number
- JP3146806B2 JP3146806B2 JP27941193A JP27941193A JP3146806B2 JP 3146806 B2 JP3146806 B2 JP 3146806B2 JP 27941193 A JP27941193 A JP 27941193A JP 27941193 A JP27941193 A JP 27941193A JP 3146806 B2 JP3146806 B2 JP 3146806B2
- Authority
- JP
- Japan
- Prior art keywords
- brush
- porous
- graphite
- metal body
- pigtail
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、発電機、或いは電動機
などの回転電機に使用される電機ブラシに関するもので
ある。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an electric brush used for a rotating electric machine such as a generator or an electric motor.
【０００２】[0002]
【従来の技術】従来より電機ブラシは、導電性を得るこ
とを目的とした金属粉（主に銅粉が使用されてきてい
る）と、潤滑性を得ることを目的とした黒鉛粉と、該黒
鉛粉を結合することを目的とした結合剤（主に有機物が
使用されてきている）とからなる原材料で構成されて焼
結された金属体であるものが広く普及してきている。2. Description of the Related Art Conventionally, electric brushes include metal powder (mainly copper powder has been used) for obtaining conductivity, graphite powder for obtaining lubricity, and graphite powder. 2. Description of the Related Art A sintered metal body made of a raw material including a binder (mainly an organic substance has been used) for the purpose of binding graphite powder has been widely used.
【０００３】しかしながら、上記の如き構成から成る前
記電機ブラシは、前記導電性を向上させるために前記金
属粉を増量すると耐磨耗性に悪影響を及ぼす。そのため
に、前記耐磨耗性を維持しつつ、即ち寿命を維持しつつ
前記導電性を向上させることは、極めて困難な状況にあ
った。本発明者は、上記の如き状況を鑑みて鋭意研究を
積み重ね、前記導電性と前記寿命の向上を図るための技
術を提案してきている（特願平３−１４２１７１号）。
該提案は、多孔質金属体と、該金属体の多孔質部分をな
す空隙部分に充填された黒鉛とからなる電機ブラシの構
成と、該電機ブラシの製造方法を開示したものである
が、上記の如き構成によって、即ち、金属自体を、連続
した構造を有した発泡金属とすることで、前記導電性を
向上し、さらに上記の従来の構成よりも前記金属粉の含
有量の低下が図れるために寿命を向上することができる
技術を開示したものである。[0003] However, in the electric brush having the above-described configuration, when the amount of the metal powder is increased in order to improve the conductivity, the abrasion resistance is adversely affected. Therefore, it has been extremely difficult to improve the conductivity while maintaining the wear resistance, that is, maintaining the life. In view of the above-mentioned situation, the present inventor has earnestly studied and proposed a technique for improving the conductivity and the life (Japanese Patent Application No. 3-142171).
The proposal discloses a configuration of an electric brush made of a porous metal body and graphite filled in a void portion forming a porous portion of the metal body, and a method of manufacturing the electric brush. By such a configuration, that is, by forming the metal itself as a foamed metal having a continuous structure, the conductivity is improved, and the content of the metal powder can be further reduced as compared with the conventional configuration described above. A technique capable of improving the life is disclosed.
【０００４】ところが、前記電機ブラシに電流を伝達す
るために、電圧が印加される端子電極に結線されるとと
もに前記電機ブラシに結合して備えられているピグテ−
ルと、前記電機ブラシとの間の電気抵抗が大きくなるた
めに、電動機などの性能である回転数が低下してしまう
という問題点が顕在化してきている。However, in order to transmit a current to the electric brush, a pigtail connected to a terminal electrode to which a voltage is applied and coupled to the electric brush is provided.
The problem that the rotation speed, which is the performance of an electric motor or the like, decreases due to an increase in the electrical resistance between the motor and the electric brush has become apparent.
【０００５】[0005]
【発明が解決しようとする課題】したがって、本発明は
上記の如き問題点、即ち回転数の低下を引き起こすこと
のない電機ブラシを提供することを課題とする。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide an electric brush which does not cause the above-mentioned problems, that is, does not cause a decrease in the number of revolutions.
【０００６】[0006]
【課題を解決するための手段】そのために、請求項１
は、多孔質であり、しかも導電性を有した多孔質金属
体、及び前記多孔質を形成する空隙部に充填された黒鉛
から成るブラシと、多孔質であり、しかも導電性を有し
た多孔質金属体、及び前記多孔質を形成する空隙部に充
填された黒鉛から成る取り付け部、或いは、多孔質であ
り、しかも導電性を有した多孔質金属体から成る取り付
け部のいずれかと、前記取り付け部に結合された導電性
のピグテ−ルとから構成され、前記取り付け部の金属の
含有率が前記ブラシの金属含有率よりも大きく、更に前
記ブラシと前記取り付け部とを一体化結合した構成とす
ることによって課題を解決するものである。To achieve the object, claim 1 is provided.
Is a porous metal body that is porous and conductive, and a brush made of graphite filled in voids that form the porous body, and a porous and conductive porous body. Either a mounting portion made of a metal body and graphite filled in a void portion forming the porous material, or a mounting portion made of a porous and conductive porous metal body, and the mounting portion And a conductive pigtail coupled to the brush, wherein the metal content of the mounting portion is greater than the metal content of the brush, and the brush and the mounting portion are integrally connected. This solves the problem.
【０００７】又、上記の如き電機ブラシを得るために、
請求項２は、黒鉛と結合剤と溶媒とからなるペ−スト状
物をブラシの多孔質金属体の空隙部に充填したものと、
黒鉛と結合剤と溶媒とからなるペ−スト状物を取り付け
部の多孔質金属体の空隙部に充填したものか、若しく
は、黒鉛と結合剤と溶媒とからなるペ−スト状物を前記
取り付け部の多孔質金属体の空隙部に充填していないも
のかのいずれかと、ピグテ−ルとを同時に加圧成形して
一体化し、その後焼結することにより、前記取り付け部
の金属の含有率が前記ブラシの金属含有率よりも大きく
なるように製造するものである。さらに、本発明におい
ては、上記の多孔質金属体として、発泡金属体を採用す
ることが好ましい。 Further, in order to obtain the electric brush as described above,
Claim 2 is a brush in which a paste-like material comprising graphite, a binder and a solvent is filled in a void portion of a porous metal body of a brush.
A paste made of graphite, a binder, and a solvent is filled in the space of the porous metal body of the attachment portion, or a paste made of graphite, a binder, and a solvent is attached to the attachment. The pigtail and any one not filled in the void portion of the porous metal body of the portion and the pigtail are simultaneously pressed and integrated, and then sintered, so that the metal content of the mounting portion is reduced. The brush is manufactured so as to be larger than the metal content of the brush. Further, in the present invention,
In this case, a foamed metal body is used as the porous metal body.
Preferably.
【０００８】[0008]
【作用】請求項１により、前記ピグテ−ルを結合する前
記取り付け部を設け、更に前記取り付け部の金属の含有
率を、前記ブラシの金属含有率よりも大きな値としたこ
とから、前記ピグテ−ルと前記取り付け部との間の電気
抵抗を低減することが出来るようになる。According to the first aspect of the present invention, the mounting portion for connecting the pigtail is provided, and the metal content of the mounting portion is set to a value larger than the metal content of the brush. The electric resistance between the mounting portion and the mounting portion can be reduced.
【０００９】請求項２により、金属含有率の異なった前
記ブラシと前記取り付け部を一体化できる。請求項３に
より、多孔質金属体を発泡金属体にて構成することによ
り、例えば焼結により多孔質金属体を形成した場合に比
して、粒界がなく連続した多孔質金属体とすることがで
きる。 According to the second aspect, the brush and the mounting portion having different metal contents can be integrated. Claim 3
By forming the porous metal body from a foamed metal body,
For example, compared to the case where a porous metal body is formed by sintering,
And a continuous porous metal body without grain boundaries
Wear.
【００１０】[0010]
【発明の効果】上記作用により、請求項１では、前記ピ
グテ−ルと前記取り付け部との間の電気抵抗を低減する
ことが可能となったことで、回転数の低下を引き起こす
ことのない電機ブラシ構成を提供することができ、ま
た、請求項２で前記電機ブラシを供給する製造方法を提
供することができる。さらに、請求項３により、例えブ
ラシの摩擦による熱が発生したとしても、熱が滞留する
ことなく、外部に放熱させることができる。 According to the first aspect of the present invention, the electric resistance between the pigtail and the mounting portion can be reduced, so that the electric motor does not cause a decrease in the number of revolutions. A brush configuration can be provided, and a manufacturing method for supplying the electric brush can be provided. Further, according to claim 3, for example,
Even if heat is generated due to the friction of the brush, the heat stays
The heat can be radiated to the outside without the need.
【００１１】[0011]
（実施例１）以下、本発明を具体的な実施例を記した図
でもって説明する。図１は、本発明の一実施例である電
機ブラシ１を電動機に組付けた状態を示す斜視図であ
る。図において、前記電機ブラシ１は、直方体形状であ
り、図示されていないスプリングによってコンミュテ−
タ５に対して押しつけられて配置される。前記電機ブラ
シ１は、ブラシ２と取り付け部３とピグテ−ルとから一
体化されて構成され、そして前記ブラシ２は、前記コン
ミュテ−タ５の回転に伴い前記コンミュテ−タ５の表面
を摺動しつつ、該コンミュテ−タ５とピグテ−ル４との
導通状態を保持している。(Embodiment 1) Hereinafter, the present invention will be described with reference to the drawings showing specific embodiments. FIG. 1 is a perspective view showing a state in which an electric brush 1 according to one embodiment of the present invention is assembled to an electric motor. In the figure, the electric brush 1 has a rectangular parallelepiped shape, and is connected by a spring (not shown).
And is pressed against the table 5. The electric brush 1 is integrally formed of a brush 2, a mounting portion 3, and a pigtail, and the brush 2 slides on the surface of the computer 5 as the computer 5 rotates. While the electrical connection between the computer 5 and the pigtail 4 is maintained.
【００１２】前記ブラシ２は、金属が３次元に連なった
多孔質金属体２１である発泡金属（例えば、住友電工
（株）製セルメット）の空隙部２３に後述の処理黒鉛２
２を備えており、また前記取り付け部３も多孔質金属体
３１である発泡金属（例えば、住友電工（株）製セルメ
ット）の空隙部３３に後述の処理黒鉛３２を備えたもの
である。そして、銅線からなる前記ピグテ−ル４は前記
ピグテ−ル取り付け穴５に固定されて備えられている。The brush 2 is formed in a void 23 of a foamed metal (for example, Celmet manufactured by Sumitomo Electric Industries, Ltd.) which is a porous metal body 21 in which metal is three-dimensionally connected.
The mounting portion 3 is also provided with a treated graphite 32 described later in a void portion 33 of a foamed metal (for example, Celmet manufactured by Sumitomo Electric Industries, Ltd.) which is a porous metal body 31. The pigtail 4 made of a copper wire is fixed to the pigtail mounting hole 5 and provided.
【００１３】次に前記電機ブラシ１の製造方法について
説明する。黒鉛粉末（日本黒鉛製：ＣＢ１５０）９５重
量％と結合剤（住友デュレズ（株）製フェノ−ル217K）
５重量％からなる混合物１００％に対して、外からエタ
ノ−ル１５重量％を加えて混合し、その後前記エタノ−
ルを揮発させて前記混合物を乾燥した。その後、前記混
合物を粉砕し、又篩分級することによって整粒し、顆粒
状物とした処理黒鉛を作製した。次いで、前記処理黒鉛
に対してエタノ−ル６０重量％を加えて混練することに
よってペ−スト状黒鉛を作製した。そして、該ペ−スト
状黒鉛をエア−ガンによって、前記ブラシ２用及び前記
取り付け部３用の各々の前記発泡金属に吹きつけて、該
発泡金属の前記空隙部に充填した。その後、再びエタノ
−ルを揮発させて以下に記すような成形を行った。Next, a method of manufacturing the electric brush 1 will be described. 95% by weight of graphite powder (CB150 made by Nippon Graphite) and binder (Phenol 217K manufactured by Sumitomo Durez Co., Ltd.)
To 100% of the mixture consisting of 5% by weight, 15% by weight of ethanol was added from the outside and mixed, and then the ethanol was added.
And the mixture was dried. Thereafter, the mixture was pulverized and classified by sieving to obtain a granulated material, thereby producing treated graphite. Next, paste-like graphite was prepared by adding 60% by weight of ethanol to the treated graphite and kneading the mixture. Then, the paste-like graphite was sprayed on each of the foamed metal for the brush 2 and the mounting portion 3 by an air gun to fill the voids of the foamed metal. Thereafter, the ethanol was volatilized again, and molding as described below was performed.
【００１４】図２は、本実施例の前記電機ブラシ１の成
形工程を記したものである。前記の如きペ−スト状黒鉛
を充填した前記取り付け部３用発泡金属３ａを複数枚重
ねてダイ８内の下パンチ７ａ上に配置し、更にその横に
前記の如きペ−スト状黒鉛を充填した前記ブラシ２用発
泡金属２ａを複数枚重ねて配置した（図２(ア)）。次い
で、成形圧0.5Ton/ cm2 でもって仮成形をおこない（図
２(イ））、上パンチ７ｂを取り除いて、仮成形した取り
付け部３用発泡金属３ｂに前記ピグテ−ル４を備えるた
めのピグテ−ル取り付け穴５を設け、該穴５に前記ピグ
テ−ル４を差し込み（図２(ウ）），該ピグテ−ル４を外
部に取り出すための穴を備えた前記上パンチ７ｃの前記
穴から前記ピグテ−ルを引き出して設置して、成形圧3.
5Ton/ cm2 でもって本成形し（図２(エ））、前記ダイ８
から、一体化した本成形したブラシ２ｃと本成形した取
り付け部３ｃとを取り出して前記電機ブラシ１形状を得
た。そして、最後に750 ℃にて焼成を行い前記電機ブラ
シ１とした。尚、従来と同等の寿命を確保するために前
記ブラシ２の銅含有量を３２重量％とし（黒鉛含有量６
８重量％）、又、前記取り付け部３については、前記ピ
グテ−ル４と前記取り付け部３とのあいだに形成される
電気抵抗値のレベルを検討するために銅の含有量を種々
変化して作製した。FIG. 2 shows a step of forming the electric brush 1 of this embodiment. A plurality of the foamed metal pieces 3a for the mounting portion 3 filled with the above-mentioned paste-like graphite are stacked and arranged on the lower punch 7a in the die 8, and the side thereof is further filled with the above-mentioned paste-like graphite. A plurality of the foamed metal pieces 2a for the brush 2 were placed one on another (FIG. 2A). Next, temporary molding is performed at a molding pressure of 0.5 Ton / cm 2 (FIG. 2A), the upper punch 7b is removed, and the pigtail 4 is provided on the temporarily molded foam metal 3b for the mounting portion 3. A pigtail mounting hole 5 is provided, the pigtail 4 is inserted into the hole 5 (FIG. 2C), and the hole of the upper punch 7c provided with a hole for taking out the pigtail 4 to the outside. Pull out the pigtail from the table and install it.
The main molding is performed with 5 Ton / cm 2 (FIG. 2 (D)),
Then, the integrated brush 2c and the mounting portion 3c that were integrally formed were taken out of the apparatus to obtain the electric brush 1 shape. Finally, firing was performed at 750 ° C. to obtain the electric brush 1. The copper content of the brush 2 was set to 32% by weight (graphite content 6
8% by weight). The copper content of the mounting portion 3 was changed variously in order to examine the level of the electric resistance value formed between the pigtail 4 and the mounting portion 3. Produced.
【００１５】次に評価結果について記す。前記ピグテ−
ル４の取り付けによる電気抵抗値は前記ピグテ−ル４と
前記ブラシ２とのあいだに１アンペアの電流を流すこと
によって発生する電圧降下を測定することによって求め
た。図３は、前記取り付け部３の銅含有量に対する前記
電圧降下のレベルをピグテ−ル取り付け抵抗として表し
たものであり、銅の含有量が増えるに連れてピグテ−ル
取り付け抵抗は低下する。このグラフから銅の含有量
が、４５重量％以上であればピグテ−ル取り付け抵抗は
従来レベルよりも小さくなり、発電機の回転数を向上で
きるようになる。尚、図中の符号は、ピグテ−ル取りつ
け抵抗の（平均値±標準偏差の３倍値）を表したもので
ある。更には、銅の含有量を７０重量％以上とすること
によってピグテ−ル取り付け抵抗をほぼ無視できる程度
にまで改善できる。Next, the evaluation results will be described. The pigtee
The electric resistance value due to the attachment of the brush 4 was determined by measuring a voltage drop caused by flowing a current of 1 amp between the pigtail 4 and the brush 2. FIG. 3 shows the level of the voltage drop with respect to the copper content of the mounting portion 3 as a pigtail mounting resistance. As the copper content increases, the pigtail mounting resistance decreases. According to this graph, when the copper content is 45% by weight or more, the pigtail mounting resistance becomes smaller than the conventional level, and the rotation speed of the generator can be improved. The symbols in the figure represent the pigtail mounting resistance (mean value ± 3 times the standard deviation). Further, by setting the content of copper to 70% by weight or more, the pigtail mounting resistance can be improved to an almost negligible level.
【００１６】以上に記したように、前記電機ブラシ１
を、銅含有量が３２重量％以上で残部が黒鉛であるよう
な発泡金属、望ましくは銅含有量が４５重量％以上で残
部が黒鉛であるような発泡金属から構成された取り付け
部３と、銅含有量が従来レベルである３２重量％程度で
残部が黒鉛であるような発泡金属から構成されたブラシ
２と、取り付け部３に設けられた穴に固定されたピグテ
ール４とから構成することによって、ピグテール取り付
け抵抗を従来レベルよりも小さくすることができ、電動
機の回転数を向上できるようになる。これにより回転数
の低下を引き起こすことなく、しかもブラシ２の銅含有
量を従来と同等にしていることから寿命を従来よりも低
減することのない電機ブラシの構成と該ブラシの製造方
法を提供することができる。[0016] As noted above, the Electric brush 1
A mounting made of a foamed metal having a copper content of at least 32% by weight and the balance being graphite, preferably a foamed metal having a copper content of at least 45% by weight and the balance being graphite
Part 3 and a brush made of a foamed metal having a copper content of about 32% by weight, which is a conventional level, and a balance of graphite
2, by configuring the pigtail 4 which is fixed in a hole provided in the Attach section 3, can be made smaller than the conventional level pigtail attachment resistance, it becomes possible to improve the rotational speed of the electric motor . Accordingly, the present invention provides a configuration of an electric brush and a method for manufacturing the brush, which do not cause a reduction in the number of revolutions, and further reduce the life of the brush 2 than before because the copper content of the brush 2 is equal to that of the conventional brush. be able to.
【００１７】また、上記実施例では銅の含有量の異なる
２つの発泡金属を用いたが、銅含有量が３２重量％以上
で残部がグラファイトになるような多孔質発泡金属のピ
グテ−ル取り付け部分をマスキングしたのちに、上記例
の如きペ−スト状黒鉛をエア−ガンによって、マスキン
グしてない発泡金属部分に吹きつけて、該発泡金属の前
記空隙部に充填し、その後、再びエタノ−ルを揮発させ
てから上記例に記したような成形を行って、焼結したも
のでも同様の効果が得られる。さらに、上記実施例の構
成において、コンミュテータ５の表面とブラシ２との摺
動による摩擦により、熱が発生したとしても、熱がブラ
シ２自体に滞留することなく、外部に容易に放熱させる
ことができるという効果を有する。 In the above embodiment, two foamed metals having different copper contents were used. However, a pigtail mounting portion of a porous foamed metal having a copper content of 32% by weight or more and the remainder being graphite. After the masking, the paste-like graphite as in the above example is sprayed by an air gun onto the unmasked foamed metal portion to fill the voids of the foamed metal, and then ethanol again. The same effect can be obtained even if the material is volatilized and then molded as described in the above example and sintered. Further, the configuration of the above embodiment
In the formation, the sliding between the surface of the commutator 5 and the brush 2
Even if heat is generated due to friction caused by dynamics,
Dissipates heat easily to the outside without staying in the fabric 2 itself
It has the effect of being able to.
【００１８】また、上記の実施例では銅を例にとった
が、他の金属でも同様の効果が得られる。Although copper is used as an example in the above embodiment, the same effect can be obtained with other metals.
【図１】本発明の電気ブラシを説明するための斜視図で
ある。FIG. 1 is a perspective view for explaining an electric brush of the present invention.
【図２】本発明の電気ブラシの成形工程を説明するため
の図である。・・・FIG. 2 is a view for explaining a forming step of the electric brush of the present invention. ...
【図３】本発明の電気ブラシのピグテ−ル取り付け抵抗
を表したグラフである。FIG. 3 is a graph showing pigtail mounting resistance of the electric brush of the present invention.
１ 電気ブラシ ２ ブラシ ２１ 多孔質金属 ２２ 黒鉛 ２３ 空隙部 ２ａ ブラシ用発泡金属 ２ｂ 仮成形をしたブラシ用発泡金属 ２ｃ 本成形をしたブラシ用発泡金属 ３ 取り付け部 ３１ 多孔質金属 ３２ 黒鉛 ３３ 空隙部 ３ａ 取り付け部用発泡金属 ３ｂ 仮成形をした取り付け部用発泡金属 ３ｃ 本成形をした取り付け部用発泡金属 ４ ピグテ−ル ５ ピグテ−ル取り付け穴 ６ コンミュテ−タ ７ａ 下パンチ ７ｂ 上パンチ ８ ダイ DESCRIPTION OF SYMBOLS 1 Electric brush 2 Brush 21 Porous metal 22 Graphite 23 Void 2a Foam metal for brush 2b Foam metal for brush formed temporarily 2c Foam metal for brush formed this time 3 Mounting part 31 Porous metal 32 Graphite 33 Void 3a Foamed metal for mounting part 3b Foamed metal for mounting part temporarily molded 3c Foamed metal for mounting part formed permanently 4 Pigtail 5 Pigtail mounting hole 6 Calculator 7a Lower punch 7b Upper punch 8 Die
フロントページの続き (72)発明者 宮田 義雄 愛知県刈谷市昭和町１丁目１番地 日本 電装株式会社内 (56)参考文献 特開 平４−249876（ＪＰ，Ａ) 特開 平２−219438（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) H02K 13/00 Continuation of front page (72) Inventor Yoshio Miyata 1-1-1 Showa-cho, Kariya-shi, Aichi Japan Inside Denso Co., Ltd. (56) References JP-A-4-249876 (JP, A) JP-A-2-219438 (JP) , A) (58) Field surveyed (Int. Cl. 7 , DB name) H02K 13/00
Claims (3)
孔質金属体、及び前記多孔質を形成する空隙部に充填さ
れた黒鉛から成るブラシと、多孔質であり、しかも導電
性を有した多孔質金属体、及び前記多孔質を形成する空
隙部に充填された黒鉛から成る取り付け部、或いは、多
孔質であり、しかも導電性を有した多孔質金属体から成
る取り付け部のいずれかと、前記取り付け部に結合され
た導電性のピグテ−ルとから構成され、前記取り付け部
の金属の含有率が前記ブラシの金属含有率よりも大き
く、更に前記ブラシと前記取り付け部とが一体化結合さ
れていることを特徴とする電機ブラシ。1. A brush made of a porous metal body having electrical conductivity and a graphite filled in voids forming the porous body, and a porous and electrically conductive brush. A porous metal body, and an attachment portion made of graphite filled in a void portion forming the porous material, or an attachment portion made of a porous and conductive porous metal body, A conductive pigtail connected to the mounting portion, wherein the metal content of the mounting portion is greater than the metal content of the brush, and the brush and the mounting portion are integrally connected. An electric brush, characterized in that:
状物をブラシの多孔質金属体の空隙部に充填したもの
と、黒鉛と結合剤と溶媒とからなるペ−スト状物を取り
付け部の多孔質金属体の空隙部に充填したものか、若し
くは、黒鉛と結合剤と溶媒とからなるペ−スト状物を前
記取り付け部の多孔質金属体の空隙部に充填していない
ものかのいずれかと、ピグテ−ルとを同時に加圧成形し
て一体化し、その後焼結することにより、前記取り付け
部の金属の含有率が前記ブラシの金属含有率よりも大き
いことを特徴とする電機ブラシの製造方法。2. A paste made of graphite, a binder and a solvent filled in a void portion of a porous metal body of a brush, and a paste made of graphite, a binder and a solvent. What is filled in the space of the porous metal body of the attachment portion, or the case where the space portion of the porous metal body of the attachment portion is not filled with a paste-like material made of graphite, a binder and a solvent. Wherein the metal content of the mounting portion is greater than the metal content of the brush by simultaneously pressing and integrating any one of the above and the pigtail, and then sintering. Brush manufacturing method.
ことを特徴とする請求項１及び２のいずれか１項記載のThe method according to any one of claims 1 and 2, wherein
電機ブラシの製造方法。Manufacturing method of electric brush.