JP3483589B2 - A method for producing a laminated polymer cement concrete having a rubber base layer and a laminated polymer cement concrete structural material. - Google Patents
A method for producing a laminated polymer cement concrete having a rubber base layer and a laminated polymer cement concrete structural material.Info
- Publication number
- JP3483589B2 JP3483589B2 JP14510793A JP14510793A JP3483589B2 JP 3483589 B2 JP3483589 B2 JP 3483589B2 JP 14510793 A JP14510793 A JP 14510793A JP 14510793 A JP14510793 A JP 14510793A JP 3483589 B2 JP3483589 B2 JP 3483589B2
- Authority
- JP
- Japan
- Prior art keywords
- polymer cement
- concrete
- laminated
- rubber
- cement concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、防振ゴムを一体に積層
したコンクリート製品、電波吸収機能を有する金属酸化
物を含有する機能層を積層したコンクリート製品、又、
ポリマーセメントモルタルに配合する材料を適宜選択す
ることにより多様な機能を発揮させる積層コンクリート
製品等を形成するためのゴム基材層を備えた積層ポリマ
ーセメントコンクリートおよびその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a concrete product in which anti-vibration rubber is integrally laminated, a concrete product in which a functional layer containing a metal oxide having a radio wave absorbing function is laminated, and
TECHNICAL FIELD The present invention relates to a laminated polymer cement concrete provided with a rubber base layer for forming a laminated concrete product or the like which exhibits various functions by appropriately selecting materials to be mixed with the polymer cement mortar, and a method for producing the same.
【０００２】[0002]
【従来の技術】鉄道・道路のコンクリート製の橋梁・高
架、舗装、枕木等における振動騒音を軽減防止するた
め、防振ゴムをコンクリートの構造物や部材に敷設した
り接着している。この方法の材料・工法はコストが高
く、かつ、施工も繁雑である。これを解決するために
は、構造物または部材の施工のためのコンクリート施工
において、防振ゴムと同様な機能、すなわち、ゴム弾性
を発現させることのできるコンクリート、例えば防振ゴ
ムを一体に積層したコンクリートが製造できるような、
新たなコンクリートの製造方法の開発が最良である。2. Description of the Related Art In order to prevent vibration noise from concrete bridges, overpasses, pavements, sleepers, etc. of railroads and roads, antivibration rubber is laid or adhered to concrete structures and members. The material / construction method of this method is high in cost, and the construction is complicated. In order to solve this, in concrete construction for construction of a structure or member, concrete having a function similar to that of the vibration isolating rubber, that is, rubber elasticity can be developed, for example, vibration isolating rubber is integrally laminated. To make concrete,
It is best to develop a new concrete manufacturing method.
【０００３】在来のゴム弾性層を備えたコンクリートの
施工は、セメント、骨材、ゴム粉、ラテックス・エマル
ジョン、水等を同時に混練したポリマーセメントコンク
リートを加振して、ゴム粉とラテックス・エマルジョン
のブリージングを促進し、上層をゴム粉とラテックスに
富む層とし、これの硬化によりゴム弾性層を形成する方
法、すなわちポリマーセメントコンクリートの一回打設
工法によっている。Construction of conventional concrete having a rubber elastic layer is carried out by vibrating polymer cement concrete in which cement, aggregate, rubber powder, latex emulsion, water and the like are simultaneously kneaded to obtain rubber powder and latex emulsion. The method of accelerating the breathing, forming an upper layer rich in rubber powder and latex, and curing it to form a rubber elastic layer, that is, a single-casting method of polymer cement concrete.
【０００４】また、ゴム弾性機能をコンクリートに付与
する方法としては、防振ゴムをコンクリートに接着する
方法がある。Further, as a method of imparting a rubber elasticity function to concrete, there is a method of adhering a vibration-proof rubber to the concrete.
【０００５】[0005]
【発明が解決しようとする課題】在来のブリージングを
利用するポリマーセメントコンクリートの一回打設工法
においては、ラテックス・エマルジョンとともにセメン
ト粒子、砂、ゴム粉などの粒子の小さいものが浮上し、
ゴム弾性層の品質管理が困難である。また、これらがブ
リージング層の下部に沈降し、ブリージング層が乾燥・
硬化して形成されるラテックス層すなわちゴム弾性層の
厚さが薄く、かつ、下層のコンクリート層との間に脆弱
なセメントリッチなペースト層やゴム粉などを含む移行
層が生ずるという欠点がある。In the one-time construction method of polymer cement concrete utilizing conventional breathing, small particles such as cement particles, sand, and rubber powder float with latex emulsion,
It is difficult to control the quality of the rubber elastic layer. In addition, these settle at the bottom of the breathing layer, and the breathing layer dries.
The latex layer formed by curing, that is, the rubber elastic layer, has a small thickness, and a fragile cement-rich paste layer and a transfer layer containing rubber powder are formed between the layer and the lower concrete layer.
【０００６】さらに、下層のコンクリート層においても
ゴム粉が残り、さらに、ラテックス・エマルジョンの水
分が加えられるため、過剰水分状態が生じてモルタルの
粘性が不足し、骨材分離が生じ易く、さらに、強度不足
のコンクリートになるという欠点がある。その他、防振
ゴムの接着による施工方法では、防振ゴムの形状寸法が
大きくなると、接着作業が繁雑であり、かつ手数が多く
かかり、接着品質の信頼性が低下し易いという欠点があ
る。Further, since rubber powder remains in the lower concrete layer and the water content of the latex emulsion is further added, an excessive water state occurs, the viscosity of the mortar becomes insufficient, and the aggregate separation easily occurs. It has the drawback of becoming concrete with insufficient strength. In addition, in the construction method by bonding the anti-vibration rubber, there is a drawback that the adhering work is complicated and the number of steps is large when the shape size of the anti-vibration rubber is large, and the reliability of the adhesive quality is easily deteriorated.
【０００７】このため、コンクリートの製造・施工の際
にゴム弾性を付与することのできる省力化された簡易な
施工技術の開発が強く要請されている。そこで、上記の
ような欠点の避けられない在来技術に代わる新規技術を
提供する目的で設定する、本発明における技術的課題
は、所要の弾性材層を確実に形成するとともにコンクリ
ート層の強度を向上・確保することのできるゴム基材層
を備えた積層ポリマーセメントコンクリートおよびその
製造方法を提供することである。For this reason, there is a strong demand for the development of a labor-saving and simple construction technique capable of imparting rubber elasticity during the production and construction of concrete. Therefore, set for the purpose of providing a new technology that replaces the conventional technology inevitable of the drawbacks described above, the technical problem in the present invention is to reliably form the required elastic material layer and to improve the strength of the concrete layer. It is an object of the present invention to provide a laminated polymer cement concrete having a rubber base layer that can be improved and ensured, and a method for producing the same.
【０００８】[0008]
【問題点を解決するための手段】このような課題を解決
するための本発明の技術手段は、ゴム基材を備えた積層
ポリマーセメントコンクリートの製造方法として、ゴ
ム、プラスチック、木材、金属等の粉粒体または繊維を
混練したラテックス・エマルジョンを配合したポリマー
セメントモルタルを表層部形成側に打設し、このポリマ
ーセメントモルタルに配合したものと同一のラテックス
・エマルジョンを配合したポリマーセメントコンクリー
トを前記ポリマーセメントモルタル打設個所の内側に打
設して、表層にゴム基材層を備えた積層ポリマーセメン
トコンクリートを製造することを特徴とする。The technical means of the present invention for solving such a problem is to produce rubber, plastic, wood, metal, etc. as a method for producing a laminated polymer cement concrete having a rubber base material. A polymer cement mortar containing a latex emulsion prepared by kneading powders or fibers is placed on the surface layer forming side, and the same polymer cement concrete containing the same latex emulsion as the polymer cement mortar is added to the polymer The invention is characterized in that it is cast inside a cement mortar casting site to produce a laminated polymer cement concrete having a rubber base layer on the surface layer.
【０００９】 また、前記製造方法において、ラテック
ス・エマルジョンを配合したポリマーセメントモルタル
と、同一のラテックス・エマルジョンを配合したポリマ
ーセメントコンクリートとを、上下方向に重ねて打設し
たことを特徴とする。さらにまた、前記製造方法におい
て、ラテックス・エマルジョンを配合したポリマーセメ
ントモルタルと、同一のラテックス・エマルジョンを配
合したポリマーセメントコンクリートとを、側面方向に
積層させたことを特徴とする。Further, in the above-mentioned manufacturing method, a polymer cement mortar containing a latex emulsion and a polymer cement concrete containing the same latex emulsion are piled up and down in a vertical direction. Furthermore, in the above-mentioned manufacturing method, a polymer cement mortar containing a latex emulsion and a polymer cement concrete containing the same latex emulsion are laminated in a lateral direction.
【００１０】 また、積層ポリマーセメントコンクリー
ト構造材としては、前記請求項１乃至３記載の製造方法
によって製造された積層ポリマーセメントコンクリート
構造材であって、ゴム、プラスチック、その他の有機
系、無機系の微粒体または繊維を混練したラテックス・
エマルジョンが配合されたゴム基材層を形成し、表層側
に配設されたポリマーセメントモルタルと、このポリマ
ーセメントモルタルに配合されたラテックス・エマルジ
ョンと同一のラテックス・エマルジョンが配合され、ポ
リマーセメントモルタル打設個所の内側に配設されたポ
リマーセメントコンクリートとからなることを特徴とす
る。The laminated polymer cement concrete structural material is a laminated polymer cement concrete structural material manufactured by the manufacturing method according to any one of claims 1 to 3, and is made of rubber, plastic, other organic type or inorganic type. Latex mixed with fine particles or fibers
A rubber base layer containing an emulsion is formed, and a polymer cement mortar arranged on the surface layer side and a latex emulsion identical to the latex emulsion blended with this polymer cement mortar are blended to form a polymer cement mortar. It is characterized in that it is made of polymer cement concrete arranged inside the setting place.
【００１１】[0011]
【作用】本発明のゴム基材層を備えた積層ポリマーセメ
ントコンクリートの製造方法は、ラテックス・エマルジ
ョンを配合したポリマーセメントモルタルと、ラテック
ス・エマルジョンを配合したポリマーセメントコンクリ
ートとに、同一のラテックス・エマルジョンを配合した
ことによって、ポリマーセメントモルタルとポリマーセ
メントコンクリートとが接合する界面の相溶・混和がよ
く、両積層材のラテックスによる結合すなわち接着が促
進される。このため、在来のゴム弾性層を備えたコンク
リートよりも信頼性が高く、良質かつ多様な機能を発現
するゴム基材層が形成される。The method for producing a laminated polymer cement concrete provided with a rubber substrate layer of the present invention is the same latex emulsion for polymer cement mortar containing a latex emulsion and polymer cement concrete containing a latex emulsion. By blending, the compatibility and mixing of the interface between the polymer cement mortar and the polymer cement concrete are good, and the bonding of the both laminated materials by latex, that is, the adhesion is promoted. For this reason, a rubber base material layer which is more reliable than the conventional concrete having a rubber elastic layer, has high quality, and exhibits various functions is formed.
【００１２】 また、ポリマーセメントモルタルとポリ
マーセメントコンクリートとのそれぞれを、順に型枠内
に、上下方向に前後して打設し、または、左右方法に並
列かつ隣接して形成させる等の方法によって、所要のゴ
ム弾性層を表層に有する積層ポリマーセメントコンクリ
ート構造材が製造される。製造された積層ポリマーセメ
ントコンクリート構造材は、信頼性が高く良質かつ多様
な機能を発現するゴム基材層を表層に形成し、ポリマー
セメントモルタルとポリマーセメントコンクリートとが
接合する界面の相溶・混和がよく、両積層材のラテック
スによる結合すなわち接着が促進され、ゴム基材層とコ
ンクリート層とが強固に一体化された積層ポリマーセメ
ントコンクリート構造材となり、コンクリート層の強度
を向上・確保する。Further, each of the polymer-cement mortar and the polymer-cement concrete is sequentially placed in the mold in the vertical direction, or by a method such as forming them in parallel and adjacent to each other by the left-right method. A laminated polymer cement concrete structural material having the required rubber elastic layer on the surface layer is manufactured. The manufactured laminated polymer cement concrete structural material has a rubber base layer that has high reliability and high quality and expresses various functions on the surface layer, and the compatibility and mixing of the interface where polymer cement mortar and polymer cement concrete are joined. Therefore, the bonding of the two laminated materials by the latex, that is, the adhesion is promoted, and a laminated polymer cement concrete structural material in which the rubber base material layer and the concrete layer are firmly integrated is obtained, and the strength of the concrete layer is improved and secured.
【００１３】そして、このように製造された積層ポリマ
ーセメントコンクリート構造材の施工後には、所要のゴ
ム弾性層を所定位置に確実に形成するとともに、コンク
リート層の強度を向上・確保し、希望する弾性機能を発
揮するコンクリート構造物が形成される。また、ポリマ
ーセメントモルタルのゴム粉の代わりに、コルク、プラ
スチック・ビーズ、石粉、金属粉等の粒子、あるいは化
学繊維のモノフィラメント、チョップ、テキスタイル、
不織布等の無機系、有機系の材料をフィラーあるいは強
化材として応用すれば、物理的化学的な機能を発現する
高度化多様化したコンクリート構造材として用途が拡大
する。After the laminated polymer cement concrete structural material manufactured in this manner is installed, a required rubber elastic layer is surely formed at a predetermined position, and the strength of the concrete layer is improved and ensured to obtain a desired elasticity. A concrete structure that exerts its function is formed. Instead of rubber powder of polymer cement mortar, particles such as cork, plastic beads, stone powder, metal powder, or monofilament of chemical fiber, chop, textile,
If inorganic or organic materials such as non-woven fabric are applied as a filler or a reinforcing material, the application will be expanded as a highly diversified concrete structural material that exhibits physical and chemical functions.
【００１４】[0014]
（実施例１）図１に示すように、型枠１にカチオン系の
ネオプレンラテックスの４５±０．５％エマルジョンに
エマルジョン重量の１．０〜３．０倍のＳＢＲ（スチレ
ン・ブタジエン・ラバー）の直径５ｍｍ以下のゴム粉を
混練したポリマーセメントモルタル２を厚さ２０〜５０
ｍｍに打設した後、直ちに前記ネオプレンラテックス・
エマルジョンをセメント重量に対して１０％以下の割合
で配合したポリマーセメントコンクリート３を高さ２０
０〜４５０ｍｍ打設し、６０℃以上の雰囲気温度におい
て養生した。(Example 1) As shown in FIG. 1, a 45 ± 0.5% emulsion of a cationic neoprene latex was added to a mold 1 and 1.0 to 3.0 times the weight of the emulsion was added to the SBR (styrene-butadiene rubber). The thickness of the polymer cement mortar 2 kneaded with rubber powder having a diameter of 5 mm or less is 20 to 50
Immediately after being placed in mm, the neoprene latex
The height of the polymer cement concrete 3 containing the emulsion in an amount of 10% or less based on the weight of the cement is 20
It was cast from 0 to 450 mm and cured at an ambient temperature of 60 ° C or higher.
【００１５】この結果、ポリマーセメントモルタルの硬
化物、すなわちゴム弾性を有するゴム基材層（２）は、
３〜５ｔｏｎｆ／ｃｍ（１０×１０ｃｍ2 ）のばね係数
を示す。また、このゴム基材層（２）と、ポリマーセメ
ントコンクリート３側のコンクリート層との、接着せん
断強度は３〜７ｋｇｆ／ｃｍ2 という所要の物性を示
す。さらに、ポリマーセメントコンクリート３側のコン
クリート層の圧縮強度は２５０ｋｇｆ／ｃｍ2 以上が得
られ、ゴム弾性のあるゴム基材層（２）を備えた十分な
強度を有する積層ポリマー・セメント・コンクリートで
あることが認められた。As a result, the cured product of polymer cement mortar, that is, the rubber base layer (2) having rubber elasticity is
The spring coefficient of 3 to 5 tonf / cm (10 × 10 cm 2 ) is shown. The rubber base layer (2) and the concrete-side concrete-concrete-concrete-side concrete layer 3 have required physical properties of adhesive shear strength of 3 to 7 kgf / cm 2 . Further, the compressive strength of the concrete layer on the side of the polymer-cement concrete 3 is 250 kgf / cm 2 or more, and the laminated polymer-cement-concrete having a sufficient strength is provided with the rubber base layer (2) having rubber elasticity. Was confirmed.
【００１６】（実施例２）ポリマーセメントモルタル２
とポリマーセメントコンクリート３とを、上下方向へ交
互に打設することにより、図２に示すように、多層構造
の積層ポリマーセメントコンクリートが得られ、コンク
リートへの振動、衝撃を緩和し、あるいは、コンクリー
ト防水の機能を強化することができる。
（実施例３）実施例１の打設の順序を逆にして、図３に
示すように、先に、ポリマーセメントコンクリート３を
打設したのち、直ちに、ポリマーセメントモルタル２を
打設して、加熱養生すると、この方法により得られたコ
ンクリートの強度、ゴム弾性層となるゴム基材層（２）
のばね係数、接着せん断強度等は、先の実施例１とほぼ
同等の物性並びに実用性を示した。(Example 2) Polymer cement mortar 2
By alternately pouring the polymer cement concrete 3 and the polymer cement concrete 3 in the vertical direction, a laminated polymer cement concrete having a multi-layer structure can be obtained, as shown in FIG. The waterproof function can be enhanced. (Example 3) By reversing the order of placing in Example 1, as shown in FIG. 3, first, the polymer cement concrete 3 was placed first, and then the polymer cement mortar 2 was placed immediately, The strength of the concrete obtained by this method when heated and cured, and the rubber base layer which becomes the rubber elastic layer (2)
The spring coefficient, adhesive shear strength, and the like of Example 1 showed substantially the same physical properties and practicality as those of Example 1 above.
【００１７】これらの実施例１，２，３において、木
粉、コルク粒子、あるいは、プラスチック・ビーズ等の
粒子を適宜混練したポリマーセメントモルタル２を使用
することにより、ゴム基材層（２）すなわちゴム弾性層
のバネ係数、硬さを調製した積層ポリマーセメントコン
クリートとして利用することができる。さらに、ラテッ
クス・エマルジョンにＰＥＴ（テトロンなどのポリエチ
レン・テレフタレート），ナイロン等の不織布、あるい
は、チョップ等の繊維を含有するポリマーセメントモル
タル２を使用すれば、繊維強化したゴム基材層（２）す
なわちゴム弾性層を備えた積層ポリマーセメントコンク
リートとして利用することができる。In these Examples 1, 2, and 3, by using the polymer cement mortar 2 in which particles such as wood powder, cork particles, or plastic beads are appropriately kneaded, the rubber base layer (2), that is, It can be used as a laminated polymer cement concrete in which the elastic modulus and hardness of the rubber elastic layer are adjusted. Furthermore, if a latex / emulsion is made of non-woven fabric such as PET (polyethylene terephthalate such as Tetron) or nylon, or polymer cement mortar 2 containing fibers such as chops, the fiber-reinforced rubber base layer (2), that is, It can be used as a laminated polymer cement concrete having a rubber elastic layer.
【００１８】これらの実施例１，２，３における粒子と
してフェライト、ニッケル、銀、銅等の金属粉体を混練
したポリマーセメントモルタルを使用すれば、金属分散
相のゴム基材相（２）を備え、導電性、電波吸収性等の
所要の電気特性を発現するポリマーセメントコンクリー
トとして利用することができる。
（実施例４）これらの実施例に用いたポリマーセメント
モルタル２とポリマーセメントコンクリート３を、着脱
自在な仕切板４を設けた型枠５に、図４に示すように、
左右方向（側面方向）へ並列かつ隣接して打設し、直ち
に仕切板４を取り外すことにより、ポリマーセメントモ
ルタル２とポリマーセメントコンクリート３とが直接接
触し、硬化後、ゴム基材層（２）とポリマーセメントコ
ンクリート層とが並列した積層コンクリートとなり、左
右方向の荷重に対する振動、衝撃の緩和、あるいは、防
水性が要求される、例えば盛土の擁壁などのコンクリー
ト構造物として利用することができる。If polymer cement mortar obtained by kneading metal powders of ferrite, nickel, silver, copper or the like is used as the particles in Examples 1, 2 and 3, the rubber base phase (2) of the metal dispersed phase is obtained. It can be used as a polymer-cement concrete that is provided and exhibits required electrical characteristics such as conductivity and radio wave absorption. (Example 4) The polymer cement mortar 2 and the polymer cement concrete 3 used in these examples were placed in a mold 5 provided with a removable partition plate 4, as shown in FIG.
The polymer cement mortar 2 and the polymer cement concrete 3 are in direct contact with each other by being driven in parallel and adjacently in the left-right direction (side direction) and immediately removing the partition plate 4, and after curing, the rubber base layer (2) It becomes a laminated concrete in which the polymer cement concrete layer and the polymer cement concrete layer are juxtaposed, and can be used as a concrete structure such as a retaining wall for embankment, which requires vibration and impact relaxation against a lateral load, or waterproofness.
【００１９】さらに、この実施例４による積層コンクリ
ートを水平にして使用すれば、実施例１の上下方向に積
層した積層ポリマーセメントコンクリートとしても利用
することができることは自明である。
（実施例５）凹凸のある型枠（図示せず）を用いると、
ポリマーセメントモルタルは液状ないし流動性に富むモ
ルタルであるから、図５に示すように、表面に凹凸のあ
るゴム基材層（２）を備えた積層コンクリートとして成
形される。そのため、例えば、道床抵抗の大きい鉄道枕
木として使用することができるなど、各種の部材・構造
物として活用することができる。Further, it is obvious that if the laminated concrete according to the fourth embodiment is used horizontally, it can be used as the laminated polymer cement concrete laminated in the vertical direction of the first embodiment. (Embodiment 5) Using a mold frame (not shown) having irregularities
Since the polymer cement mortar is a mortar which is liquid or rich in fluidity, it is molded as a laminated concrete provided with a rubber base layer (2) having an uneven surface as shown in FIG. Therefore, it can be utilized as various members and structures, for example, it can be used as a railroad sleeper with high roadbed resistance.
【００２０】[0020]
【発明の効果】以上のように本発明では、ゴム基材層を
備えた積層ポリマーセメントコンクリートの製造方法と
して、ゴム、プラスチック、その他の有機系、無機系の
微粒体または繊維を混練するラテックス・エマルジョン
を配合したポリマーセメントモルタルと、コンクリート
積層物を形成させるために打設する、ラテックス・エマ
ルジョンを配合したポリマーセメントコンクリートとに
同一のラテックス・エマルジョンを配合したことによっ
て、ゴム粉等の粒子または繊維を含むラテックス・エマ
ルジョンを配合したポリマーセメントモルタルと、ラテ
ックス・エマルジョン、セメント、骨材等を配合したポ
リマーセメントコンクリートとが、層状に直接接触して
打設でき、両層に含まれている同一のラテックス・エマ
ルジョンが、両層の相溶性を良くし、両層間の接着を良
好な状態にさせることができる。INDUSTRIAL APPLICABILITY As described above, according to the present invention, as a method for producing a laminated polymer cement concrete provided with a rubber base layer, latex, which is prepared by kneading rubber, plastic, other organic or inorganic fine particles or fibers, Particles or fibers such as rubber powder obtained by mixing the same latex emulsion with polymer cement mortar mixed with emulsion and polymer cement concrete mixed with latex emulsion, which is cast to form a concrete laminate. Polymer cement mortar mixed with latex emulsion containing is and polymer cement concrete mixed with latex emulsion, cement, aggregate, etc. Latex emulsion is both layers To improve the compatibility, it is possible to cause the adhesion between the two layers in a good condition.
【００２１】また、接着界面には骨材、ゴム粉等の粒
子、繊維等の固形物質が存在し、これら固形物質により
凹凸状となるため、これらの凹凸が両層に対してそれぞ
れ楔効果を出し、すなわち、接着面に作用するせん断外
力に対する抵抗を示して、接着結合を一層安定化し、ゴ
ム基材層とコンクリート層とが強固に一体化した積層コ
ンクリートとなる。Further, since aggregates, particles such as rubber powder, and solid substances such as fibers are present at the adhesive interface, and these solid substances form irregularities, these irregularities exert a wedge effect on both layers. That is, it shows resistance to external shear force acting on the adhesive surface, further stabilizes the adhesive bond, and becomes a laminated concrete in which the rubber base material layer and the concrete layer are firmly integrated.
【００２２】そしてまた、使用されるポリマーセメント
モルタルは、液状ないし流動性に富むモルタルであり、
凹凸のある型枠を用いると、表面に凹凸のあるゴム基材
層を備えた積層コンクリートが形成できるため、例えば
道床抵抗の大きい鉄道枕木として使用することができる
など、各種の部材・構造物としての活用が広がる。そし
てまた、高層ビルなどのコンクリート構造物の電波反射
による電波障害が問題となっているため、電波の吸収機
能を有する金属酸化物を含有する機能層を備えた積層し
たコンクリートが提供でき、防振、歩行快適性のコンク
リート床板としても利用可能な材料を提供することがで
きるものである。Further, the polymer cement mortar used is a liquid or fluid mortar,
By using a formwork with irregularities, it is possible to form laminated concrete with a rubber base layer with irregularities on the surface, so it can be used as a railway sleeper with high roadbed resistance, etc. The utilization of will spread. Also, because radio wave interference due to radio wave reflection of concrete structures such as high-rise buildings has become a problem, it is possible to provide laminated concrete with a functional layer containing a metal oxide having a function of absorbing radio waves, and to prevent vibration. It is possible to provide a material that can also be used as a concrete floor board for walking comfort.
【００２３】そしてまた、ポリマーセメントモルタルに
配合する粒子または繊維の種類を適宜選択して、これら
の粒子、繊維の物性、機能とラテックスとの複合効果に
より、各種の物理的化学的な機能をコンクリートに付与
することができるため、ただ単にゴム弾性を発現した積
層コンクリートができるだけではなく、物理的化学的に
多面的な機能を発現するゴム基材層を備えた積層コンク
リートを実現させ、更なる技術的な発展を期待すること
ができるばかりでなく、生産、応用技術的な効果ばかり
でなく、経済的な効果を高めることができる。Further, the kind of particles or fibers to be mixed in the polymer cement mortar is appropriately selected, and various physical and chemical functions are given to concrete by the combined effect of physical properties and functions of these particles and fibers and latex. Therefore, not only is it possible to obtain laminated concrete that exhibits rubber elasticity, but it is also possible to realize laminated concrete that has a rubber base layer that exhibits multifaceted functions in terms of physicochemical properties. It is possible to expect not only economic development, but also production and applied technical effects as well as economic effects.
【００２４】また、ポリマーセメントコンクリートとポ
リマーセメントモルタルとのそれぞれを、順に型枠内
に、上下方向に前後して打設し、または、側面方向に並
列かつ隣接して形成させる等の方法によって打設するこ
とによって、所要のゴム弾性層を表層に有する積層ポリ
マーセメントコンクリート構造材が製造できる。そして
また、このように製造された積層ポリマーセメントコン
クリート構造材の施工後は、所要のゴム弾性層を所定位
置に確実に形成できるとともに、コンクリート層の強度
を向上・確保することができ、希望する弾性機能を発揮
するコンクリート構造物が形成できる。Further, each of the polymer cement concrete and the polymer cement mortar is sequentially placed in the mold in the vertical direction, or is placed in parallel and adjacent in the lateral direction. By installing, a laminated polymer cement concrete structural material having a required rubber elastic layer on the surface layer can be manufactured. Further, after the laminated polymer cement concrete structural material manufactured in this way is constructed, a desired rubber elastic layer can be reliably formed at a predetermined position, and the strength of the concrete layer can be improved and ensured. A concrete structure that exhibits an elastic function can be formed.
【図１】本発明における実施例１のゴム基材層を備えた
積層ポリマーセメントコンクリートの製造時における横
断面図である。FIG. 1 is a cross-sectional view of a laminated polymer cement concrete including a rubber base layer of Example 1 of the present invention at the time of production.
【図２】本発明における実施例２のゴム基材層を備えた
積層ポリマーセメントコンクリートの横断面図である。FIG. 2 is a cross-sectional view of a laminated polymer cement concrete provided with a rubber base layer according to Example 2 of the present invention.
【図３】本発明における実施例３のゴム基材層を備えた
積層ポリマーセメントコンクリートの製造時における横
断面図である。FIG. 3 is a cross-sectional view at the time of manufacturing a laminated polymer cement concrete including a rubber base layer of Example 3 of the invention.
【図４】本発明における実施例４のゴム基材層を備えた
積層ポリマーセメントコンクリートの製造時における横
断面図である。FIG. 4 is a transverse cross-sectional view at the time of manufacturing a laminated polymer cement concrete provided with a rubber base layer of Example 4 of the invention.
【図５】本発明における実施例５のゴム基材層を備えた
積層ポリマーセメントコンクリートの横断面図である。FIG. 5 is a cross-sectional view of a laminated polymer cement concrete provided with a rubber base layer according to Example 5 of the present invention.
１ 型枠 ２ ポリマーセメントモルタル （２） ゴム基材層 ３ ポリマーセメントコンクリート ４ 仕切板 ５ 型枠 1 formwork 2 Polymer cement mortar (2) Rubber base material layer 3 Polymer cement concrete 4 partition boards 5 formwork
───────────────────────────────────────────────────── フロントページの続き (72)発明者 丸山 久一 新潟県長岡市花園東２−198−１ (72)発明者 池田 俊雄 神奈川県鎌倉市稲村ケ崎３丁目11番５号 (72)発明者 江本 佑橘 東京都練馬区中村３丁目39番13号 シェ ルロイヤルＭ−206 (72)発明者 安藤 勝敏 東京都国分寺市光町二町目８番38 財団 法人鉄道総合技術研究所内 (72)発明者 原田 修輔 千葉県船橋市豊富町585番地 住友セメ ント株式会社中央研究所内 (56)参考文献 特開 平４−317480（ＪＰ，Ａ) 実開 平５−22742（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 C04B 2/00 - 32/02 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Hisaichi Maruyama 2-198-1 Hanazono Higashi, Nagaoka City, Niigata Prefecture (72) Inventor Toshio Ikeda 3-11-5 Inamuragasaki, Kamakura City, Kanagawa Prefecture (72) Invention Yumoto Emoto 3-39-13 Nakamura, Nerima-ku, Tokyo Sherroyal M-206 (72) Inventor Katsutoshi Ando 8-8 Nimachi-cho, Hikarimachi, Kokubunji-shi, Tokyo Inside the Railway Technical Research Institute (72) Inventor Shusuke Harada, 585, Tomimachi, Funabashi, Chiba, Central Research Laboratory, Sumitomo Cement Co., Ltd. (56) Reference JP-A-4-317480 (JP, A) Fukukaihei 5-22742 (JP, U) (58) Fields investigated (Int.Cl. 7 , DB name) B32B 1/00-35/00 C04B 2/00-32/02
Claims (4)
体または繊維を混練したラテックス・エマルジョンを配
合したポリマーセメントモルタルを表層部形成側に打設
し、このポリマーセメントモルタルに配合したものと同
一のラテックス・エマルジョンを配合したポリマーセメ
ントコンクリートを前記ポリマーセメントモルタル打設
個所の内側に打設して、表層にゴム基材層を備えた積層
ポリマーセメントコンクリートを製造することを特徴と
するゴム基材層を備えた積層ポリマーセメントコンクリ
ートの製造方法。 1. Powder particles of rubber, plastic, wood, metal, etc.
Distribute a latex emulsion that kneads the body or fibers.
Placing combined polymer cement mortar on the surface layer formation side
The same as that added to this polymer cement mortar.
Polymer sem with one latex emulsion
Concrete cement mortar
Laminated by placing it inside the place and providing a rubber base layer on the surface
Characterized by producing polymer cement concrete
Laminated polymer cement concrete with rubber base layer
Manufacturing method.
ルジョンを配合したポリマーセメントモルタルと、同一
のラテックス・エマルジョンを配合したポリマーセメン
トコンクリートとを、上下方向に重ねて打設したことを
特徴とする請求項１記載のゴム基材層を備えた積層ポリ
マーセメントコンクリートの製造方法。 2. A above method, according to claim, characterized in that the polymer cement mortar formulated with the latex emulsion, and a polymer cement concrete compounded with the same latex emulsion was pouring stacked vertically A method for producing a laminated polymer cement concrete comprising the rubber substrate layer according to 1 .
ルジョンを配合したポリマーセメントモルタルと、同一
のラテックス・エマルジョンを配合したポリマーセメン
トコンクリートとを、側面方向に積層させたことを特徴
とする請求項１記載のゴム基材層を備えた積層ポリマー
セメントコンクリートの製造方法。3. A above method, and characterized in that the polymer cement mortar formulated with latex emulsion, the polymer cement <br/> bets concrete formulated with the same latex emulsion were stacked laterally A method for producing a laminated polymer cement concrete comprising the rubber substrate layer according to claim 1 .
て製造された積層ポリマーセメントコンクリート構造材
であって、ゴム、プラスチック、その他の有機系、無機
系の微粒体または繊維を混練したラテックス・エマルジ
ョンが配合されたゴム基材層を形成し、表層側に配設さ
れたポリマーセメントモルタルと、このポリマーセメン
トモルタルに配合されたラテックス・エマルジョンと同
一のラテックス・エマルジョンが配合され、ポリマーセ
メントモルタル打設個所の内側に配設されたポリマーセ
メントコンクリートとからなることを特徴とする積層ポ
リマーセメントコンクリート構造材。 4. A manufacturing method according to any one of claims 1 to 3.
Manufactured laminated polymer cement concrete structural material
And rubber, plastic, other organic, inorganic
Latex emulsion made by kneading fine particles or fibers
Is formed on the surface side of the rubber base material layer
Polymer cement mortar and this polymer cement
Same as latex emulsion blended in tomortar
One latex emulsion is blended,
Ment mortar
Laminated porosity
Limmer cement concrete structural material.