JP5686584B2 - Moisture absorption fever carpet - Google Patents
Moisture absorption fever carpet Download PDFInfo
- Publication number
- JP5686584B2 JP5686584B2 JP2010267955A JP2010267955A JP5686584B2 JP 5686584 B2 JP5686584 B2 JP 5686584B2 JP 2010267955 A JP2010267955 A JP 2010267955A JP 2010267955 A JP2010267955 A JP 2010267955A JP 5686584 B2 JP5686584 B2 JP 5686584B2
- Authority
- JP
- Japan
- Prior art keywords
- carpet
- keratin protein
- feather keratin
- pile yarn
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、吸湿発熱効果のあるカーペットであり、人がカーペットの表面に触れたときに穏やかなほんのりとした暖かさを感じるようにしたカーペットに関するものである。 The present invention relates to a carpet having a hygroscopic heat-generating effect, and relates to a carpet that allows a gentle slight warmth to be felt when a person touches the surface of the carpet.
日本でのカーペットの使用方法は、欧米と違って、カーペットの上に座ったり、横になったりして使用することが多い。したがって、カーペットを手で触ったときの感触は、カーペット購入時の重要な要素となっている。特に最近では、柔らかく、毛足の長いファーのようなタッチ感の得られるようなものが好まれている。また一方では、省エネの観点からも、他の床材に比べ、断熱性、保温性に優れるカーペットが見直され、さらに機能性の付与されたカーペットが求められている。 In Japan, carpets are often used by sitting on the carpet or lying down. Therefore, the feel when the carpet is touched by hand is an important factor when purchasing the carpet. In particular, those that are soft and have a feeling of touch like fur with long bristle feet are preferred. On the other hand, from the viewpoint of energy saving, carpets that are superior in heat insulating properties and heat retaining properties compared to other flooring materials are reviewed, and carpets that are further functionalized are required.
特許文献１において出願人は、ポリカルボン酸系化合物のカルボキシル基の一部が金属塩化された吸湿発熱剤を架橋剤でカーペットのパイルに固着させることにより吸湿発熱効果のあるカーペットを開示している。
In
特許文献２には、メチロール系樹脂加工剤により、親水性のポリマーを強固に結合させることで吸湿発熱性を付与したセルロース繊維が開示されている。 Patent Document 2 discloses a cellulose fiber imparted with hygroscopic exothermicity by firmly bonding a hydrophilic polymer with a methylol resin processing agent.
しかしながら、汎用繊維であるポリエステル繊維を多く使用するカーペットに対しては、洗濯耐久性のある吸湿発熱効果として満足いくものではなかった。
本発明は、かかる技術的背景に鑑みてなされたものであって、人がカーペットの表面に触れた時に、穏やかな暖かさを得られ、洗濯耐久性があるカーペットを提供することを目的とする。 The present invention has been made in view of such a technical background, and an object of the present invention is to provide a carpet that can obtain a gentle warmth when a person touches the surface of the carpet and has a washing durability. .
本発明者らは、このような課題を解決するために鋭意検討の結果、吸湿発熱剤として羽毛ケラチン蛋白質を、パイル糸の繊維にバインダーにより固着させることによって、洗濯耐久性があり、暖かな触感のあるカーペットが得られることを見出し本発明に到達した。前記目的を達成するために、本発明は以下の手段を提供する。 As a result of diligent studies to solve such problems, the present inventors have fixed the keratin protein as a hygroscopic exothermic agent to the fibers of the pile yarn with a binder, thereby having a washing durability and a warm touch. As a result, the present invention was reached. In order to achieve the above object, the present invention provides the following means.
［１］パイル糸と基布からなる表皮層と、バッキング層とを含むカーペットにおいて、羽毛から抽出された羽毛ケラチン蛋白質が前記パイル糸にバインダー樹脂により０．５〜３０．０ｇ／ｍ ２ で固着されており、前記バインダー樹脂の前記パイル糸に対する付着量は、０．５〜２０．０ｇ／ｍ ２ であり、前記羽毛ケラチン蛋白質を構成する疎水性アミノ酸の含有率が４０％〜６０％であり、前記羽毛ケラチン蛋白質の分子量が８０００〜１５０００である、ことを特徴とする吸湿発熱カーペット。 [1] In a carpet including a skin layer made of pile yarn and a base fabric, and a backing layer, feather keratin protein extracted from feathers is fixed to the pile yarn at 0.5 to 30.0 g / m 2 by a binder resin. The amount of the binder resin attached to the pile yarn is 0.5 to 20.0 g / m 2 , and the content of the hydrophobic amino acid constituting the feather keratin protein is 40% to 60%. A hygroscopic exothermic carpet , wherein the feather keratin protein has a molecular weight of 8000 to 15000 .
[１]の発明では、パイル糸と基布からなる表皮層と、バッキング層とを含むカーペットにおいて、羽毛ケラチン蛋白質が固着されているため、人がカーペット表面のパイル糸に触れたとき、パイル糸に付着した羽毛ケラチン蛋白質が、人の皮膚からの水分を吸着し、２〜５℃発熱上昇するので、穏やかな暖かさを感じることができる。また、バインダーで羽毛ケラチン蛋白質が固着されているため、洗濯耐久性を付与でき、実用の洗濯に耐えうるものとすることができる。 In the invention of [1], since the feather keratin protein is fixed in the carpet including the skin layer composed of the pile yarn and the base fabric, and the backing layer, when the person touches the pile yarn on the carpet surface, the pile yarn Feather keratin protein adhering to the skin adsorbs moisture from human skin and raises heat at 2-5 ° C., so that a gentle warmth can be felt. In addition, since the feather keratin protein is fixed with a binder, it is possible to impart washing durability and to withstand practical washing.
[１]の発明では、前記羽毛ケラチン蛋白質を構成する疎水性アミノ酸の含有率が４０％〜６０％であり、水への溶解性が低いため、より洗濯耐久性を高めることができる。 In the invention of [1] , since the content of the hydrophobic amino acid constituting the feather keratin protein is 40% to 60% and the solubility in water is low, washing durability can be further improved.
[１]の発明では、前記羽毛ケラチン蛋白質が０．５〜３０．０ｇ／ｍ２カーペットに固着しているので、人の皮膚が触れたときより効果的に人が吸湿発熱による暖かさを感じることができるとともに、前記羽毛ケラチン蛋白質の固着によってカーペットの風合いを損うことなく、柔らかな風合いを確保することができる。 In the invention of [1] , since the feather keratin protein is fixed to the carpet of 0.5 to 30.0 g / m 2 , the person feels warmth due to moisture absorption heat more effectively than when the human skin touches. In addition, it is possible to ensure a soft texture without impairing the texture of the carpet by the fixation of the feather keratin protein.
次にこの発明に係る吸湿発熱カーペットの一実施形態を図面に基づいて説明する。この実施形態の吸湿発熱カーペット１は、パイル糸２と基布３からなる表皮層４と、バッキング層５を含み、パイル糸２の糸表面に羽毛ケラチン蛋白質（図示せず）が付着されている。（図１参照）また、図１では、バッキング層５の保護やクッション性を付与するために不織布からなるセカンド基布６を積層している。
Next, an embodiment of a moisture-absorbing and heating carpet according to the present invention will be described with reference to the drawings. The hygroscopic
羽毛ケラチン蛋白質は、羽毛から抽出されたケラチン蛋白質であればよく、微粉砕化されたケラチン原料を加水分解して抽出する方法が一般的に取られるが、この限りではない。加水分解されたケラチンは、可溶性のケラチンと不溶性のケラチンに分離されるが、それらは、どちらも吸湿発熱剤として用いることが可能である。羽毛ケラチン蛋白質の疎水性アミノ酸の含有率は４０％〜６０％であれば、十分な吸湿発熱性を有し、かつ水への溶解性が低いため、高い洗濯耐久性を有する。好ましくは、４５％〜５０％である。 The feather keratin protein may be a keratin protein extracted from feathers, and a method of hydrolyzing and extracting a finely pulverized keratin raw material is generally used, but is not limited thereto. Hydrolyzed keratin is separated into soluble and insoluble keratin, both of which can be used as hygroscopic exothermic agents. If the content of the hydrophobic amino acid in the feather keratin protein is 40% to 60%, it has sufficient hygroscopic exothermic property and low solubility in water, and therefore has high washing durability. Preferably, it is 45% to 50%.
バインダー樹脂としては、パイル糸２と基布３の表面に羽毛ケラチン蛋白質を強固に固着することが出来れば良いが、一般的には例えばウレタン樹脂、自己架橋アクリル樹脂、メタアクリル樹脂、シリコン樹脂、グリオキザール樹脂、ポリエステル樹脂、酢酸ビニル樹脂、塩化ビニル樹脂、塩化ビニリデン樹脂、ブタジエン樹脂、メラミン樹脂、エポキシ樹脂、アクリル−シリコン樹脂、スチレン−ブタジエン共重合体樹脂（ＳＢＲ）、エチレン-酢酸ビニル共重合体樹脂（ＥＶＡ）、イソブチレン無水マレイン酸共重合体樹脂、エチレン−スチレン−アクリレート−メタアクリレート共重合体樹脂等を挙げることができる。 As the binder resin, it is sufficient that the feather keratin protein can be firmly fixed to the surface of the pile yarn 2 and the base fabric 3, but generally, for example, urethane resin, self-crosslinked acrylic resin, methacrylic resin, silicone resin, Glyoxal resin, polyester resin, vinyl acetate resin, vinyl chloride resin, vinylidene chloride resin, butadiene resin, melamine resin, epoxy resin, acrylic-silicone resin, styrene-butadiene copolymer resin (SBR), ethylene-vinyl acetate copolymer Examples thereof include a resin (EVA), an isobutylene maleic anhydride copolymer resin, and an ethylene-styrene-acrylate-methacrylate copolymer resin.
羽毛ケラチン蛋白質及びバインダーをパイル糸に付着させる方法は特に限定されず、浸漬法による方法、スプレーによる方法が挙げられる。 The method for attaching the feather keratin protein and the binder to the pile yarn is not particularly limited, and examples thereof include a dipping method and a spray method.
熱処理の方法は特に限定はされず、乾熱処理、常圧蒸気による加熱、170℃程度の高圧蒸気による加熱処理を挙げることができる。 The heat treatment method is not particularly limited, and examples thereof include dry heat treatment, heating with normal pressure steam, and heat treatment with high pressure steam at about 170 ° C.
羽毛ケラチン蛋白質のパイル糸に対する付着量は、０．５〜３０．０ｇ／ｍ２が好適である。羽毛ケラチン蛋白質のパイル糸に対する付着量が０．５ｇ／ｍ２を下回ると、吸湿発熱による効果が少なく、また、３０．０ｇ／ｍ２超えても付着量の増加に見合う効果は得られないし、カーペットの風合いが硬くなり好ましくない。 The amount of feather keratin protein attached to the pile yarn is preferably 0.5 to 30.0 g / m 2 . When the amount of adhesion to the pile yarns of feather keratin protein is below 0.5 g / m 2, less effect of heat absorption, and the effect that it exceeds 30.0 g / m 2 commensurate with the increase in the amount of adhering to not obtained, The texture of the carpet becomes hard, which is not preferable.
バインダー樹脂のパイル糸に対する付着量に、特に制限はないが、０．５〜２０．０ｇ／ｍ２が好適である。バインダーの付着量が０．５ｇ／ｍ２を下回るとカーペットへの固着が弱くなり、洗濯耐久性が損われる恐れがあり、また、２０．０ｇ／ｍ２を超えるとカーペットの風合いが硬くなり好ましくない。 Although there is no restriction | limiting in particular in the adhesion amount with respect to the pile yarn of binder resin, 0.5-20.0 g / m < 2 > is suitable. If the adhesion amount of the binder is less than 0.5 g / m 2 , the adhesion to the carpet is weakened and the washing durability may be impaired, and if it exceeds 20.0 g / m 2 , the texture of the carpet becomes hard. Absent.
羽毛ケラチン蛋白質の分子量は、特に限定されるものではないが、さらに高度の耐久性を得るためには、分子量５０００以上のものが好ましく、特に８０００〜１５０００のものが耐久性のある固着及び加工後の風合いの面から好適である。 The molecular weight of the feather keratin protein is not particularly limited, but in order to obtain a higher level of durability, those having a molecular weight of 5000 or more are preferable, and those having a molecular weight of 8000 to 15000 are particularly durable after fixing and processing. It is suitable from the surface of the texture.
対象となるカーペットの繊維類にも特に限定はないが、ポリエステル、アクリル、ナイロン、ポリプロピレンのような合成繊維、レーヨンのような半合成繊維、綿、絹、羊毛、麻のような天然繊維を挙げることができる。パイルの形態としてもカットパイルであっても、ル−プパイルであってもよいが、カットパイルのほうが温感は感じやすい。パイル糸２の目付についても、特に限定されるものではなく、カーペットの形態をなすものであればよい。 The target carpet fibers are not particularly limited, but include synthetic fibers such as polyester, acrylic, nylon and polypropylene, semi-synthetic fibers such as rayon, and natural fibers such as cotton, silk, wool and hemp. be able to. The pile may be a cut pile or a loop pile, but the cut pile is more warm. The basis weight of the pile yarn 2 is not particularly limited as long as it forms a carpet.
また、基布３としても、特に限定されるものではなく、ポリエステル繊維やポリプロピレン繊維、麻、綿等の天然繊維からなる織、編基布、不織布等通常使用される基布でよい。 The base fabric 3 is not particularly limited, and may be a commonly used base fabric such as a woven fabric, a knitted base fabric, or a nonwoven fabric made of natural fibers such as polyester fibers, polypropylene fibers, hemp, and cotton.
次に、バッキング層５としては、パイル糸２と基布３とを固定できる樹脂組成物やゴム組成物であれば特に限定されず、例えば樹脂組成物の樹脂成分としてはアクリル系、ウレタン系、ポリ塩化ビニル、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体（ＥＶＡ）等の樹脂が挙げられる。ゴム組成物のゴム成分としてはＳＢＲ（スチレン−ブタジエン）、ＮＢＲ（アクリロニトリル−ブタジエンゴム）、ＭＢＲ（メチルメタクリレート−ブタジエンゴム）あるいは天然ゴム等が挙げられる。また、充填剤として炭酸カルシウム、水酸化アルミニウム、水酸化マグネシウム、フライアッシュ等を添加してバッキング層として使用するのが一般的である。 Next, the backing layer 5 is not particularly limited as long as it is a resin composition or a rubber composition that can fix the pile yarn 2 and the base fabric 3. For example, the resin component of the resin composition may be acrylic, urethane, Examples thereof include resins such as polyvinyl chloride, polyethylene, polypropylene, and ethylene-vinyl acetate copolymer (EVA). Examples of the rubber component of the rubber composition include SBR (styrene-butadiene), NBR (acrylonitrile-butadiene rubber), MBR (methyl methacrylate-butadiene rubber), and natural rubber. In general, calcium carbonate, aluminum hydroxide, magnesium hydroxide, fly ash or the like is added as a filler and used as a backing layer.
また、図１に示すようにバッキング層５の下側にクッション性能とバッキング層の保護性能を付与すべく、不織布からなるセカンド基布６を設けてもよい。セカンド基布６としては、特に限定されず、ニ−ドルパンチ不織布、スパンボンド不織布等を例示できる。セカンド基布６の目付は５０〜１０００ｇ／ｍ２、その厚さを０．５〜１５ｍｍ、構成繊維の繊度を０．１〜３０デシテックスの範囲に設定するのが好ましい。セカンド基布６の目付が、５０ｇ／ｍ２未満ではカ−ペットとしての機能や品位の劣ったものとなり、好ましくない。１０００ｇ／ｍ２を超えると徒にコスト増大となるだけで好ましくない。素材としては、パイル糸、基布と同様に特に限定されない。また、セカンド基布６の最下部表面に、樹脂組成物やゴム組成物で滑り止め層を形成してもよい。 Further, as shown in FIG. 1, a second base fabric 6 made of a nonwoven fabric may be provided below the backing layer 5 in order to provide cushion performance and backing layer protection performance. It does not specifically limit as the second base fabric 6, A needle punch nonwoven fabric, a spun bond nonwoven fabric, etc. can be illustrated. The basis weight of the second base fabric 6 is preferably 50 to 1000 g / m 2 , its thickness is set to 0.5 to 15 mm, and the fineness of the constituent fibers is preferably set to a range of 0.1 to 30 dtex. If the basis weight of the second base fabric 6 is less than 50 g / m 2 , the function and quality of the carpet are inferior, which is not preferable. If it exceeds 1000 g / m 2 , the cost will increase unnecessarily. The material is not particularly limited as in the case of pile yarn and base fabric. Further, an anti-slip layer may be formed on the lowermost surface of the second base fabric 6 with a resin composition or a rubber composition.
次に、この発明の実施例として使用したカーペットの材質、構造、加工方法、洗濯方法、吸湿発熱性能測定試験および判定方法は次の通りである。 Next, the material, structure, processing method, washing method, hygroscopic performance measurement test and judgment method of the carpet used as an example of the present invention are as follows.
＜使用材料＞
基布・・・・目付１００ｇ／ｍ２ポリプロピレンテープヤーン織布（１４×１３）
パイル糸・・・ポリエステル繊維からなるパイル糸をカット状にタフティング機（１／８G）で基布に植え込む（パイル長７．０ｍｍ、目付け７３０ｇ／ｍ２）
バッキング層・・・・ＳＢＲラテックス（充填剤としての炭酸カルシウム）
セカンド基布・・・・５デシテックスのポリエステル繊維からなるニードルパンチ不織布（目付３００ｇ／ｍ２、厚さ６ｍｍ）
羽毛ケラチン蛋白質・・・・羽毛抽出ケラチン
バインダー・・・・・エタナーラPUD（大和化学工業製）（固形分５０％）
<Materials used>
Base fabric: 100g / m 2 basis weight woven fabric of polypropylene tape (14 x 13)
Pile yarn: Pile yarn made of polyester fiber is cut into a base fabric with a tufting machine (1 / 8G) (pile length 7.0 mm, basis weight 730 g / m 2 )
Backing layer ... SBR latex (calcium carbonate as filler)
Second base fabric: Needle punched nonwoven fabric made of 5 decitex polyester fibers (300 g / m 2 basis weight, thickness 6 mm)
Feather keratin protein ... Feather extracted keratin binder ... Etanara PUD (manufactured by Yamato Chemical) (solid content 50%)
＜洗濯方法＞
下記の条件で一定回数（１０回）洗濯を行い、吸湿発熱性の洗濯耐久性試験に供した。
洗濯条件：家庭洗濯に準じたＪＩＳ L０２１７ １０３法によった。
<How to wash>
Washing was performed a certain number of times (10 times) under the following conditions, and this was subjected to a hygroscopic exothermic washing durability test.
Washing conditions: According to JIS L0217 103 method according to household laundry.
<吸湿発熱性能測定試験＞
温度上昇測定・・・・乾燥温度１２０℃で３０分行った後、デシケーターにいれ、２０℃で放冷し１時間後２０℃、湿度９０％の環境下でサーモグラフによって測定し最大の値を温度上昇値とした。２℃より大きいものを合格とした。
官能評価・・・・・・吸湿発熱剤を固着していないカーペット（比較例１）を手で触れた感触を基準に、温かいと感じるかどうかを一対比較法で評価し、被験者数を１０人とし、８０％以上の人が温かいと感じたものを合格とした（気温２０℃、湿度３０％の室内にて評価）。
<Hygroscopic heat generation performance measurement test>
Measurement of temperature rise ··· After 30 minutes at a drying temperature of 120 ° C, put in a desiccator, let cool at 20 ° C, and after 1 hour, measure by thermograph in an environment of 20 ° C and humidity of 90%. The temperature rise value was used. The thing larger than 2 degreeC was set as the pass.
Sensory evaluation ··· Based on the feeling of touching the carpet (Comparative Example 1) to which the hygroscopic exothermic agent is not fixed with the hand, whether or not it feels warm is evaluated by a paired comparison method, and the number of subjects is 10 And 80% or more of people felt warm (evaluated indoors at a temperature of 20 ° C. and a humidity of 30%).
＜実施例１＞
水１００重量部に羽毛ケラチン蛋白質（疎水性アミノ酸比率４５．８％）２重量部を分散させておいてから、バインダー４重量部を分散した水溶液をスプレーにてカーペット表面に２５０ｇ／ｍ２塗布し、１２０℃、１０分間乾燥処理をして、カーペット上にバインダー樹脂５ｇ／ｍ２および羽毛ケラチンを５ｇ／ｍ２固着したカーペットを得た。温度上昇測定試験では、４．５℃上昇し、比較例1との官能評価においては１０人全員が温かいと感じていた。また洗濯１０回後でも４．３℃上昇し、比較例１との官能評価においては１０人全員が温かいと感じていた。
<Example 1>
After 2 parts by weight of feather keratin protein (hydrophobic amino acid ratio 45.8%) is dispersed in 100 parts by weight of water, an aqueous solution in which 4 parts by weight of binder is dispersed is applied to the carpet surface by spraying 250 g / m 2. At 120 ° C. for 10 minutes, a carpet having a binder resin of 5 g / m 2 and feather keratin fixed to 5 g / m 2 was obtained. In the temperature rise measurement test, the temperature rose by 4.5 ° C., and in the sensory evaluation with Comparative Example 1, all 10 people felt warm. Moreover, even after 10 washings, the temperature rose by 4.3 ° C., and in the sensory evaluation with Comparative Example 1, all 10 people felt warm.
＜実施例２＞
実施例１において、羽毛ケラチン蛋白質を構成する疎水性アミノ酸比率が３５．０％のものを用いた以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、４．８℃上昇し、比較例１との官能評価においては１０人全員が温かいと感じていた。また洗濯１０回後でも２．９℃上昇し、比較例１との官能評価においては９人が温かいと感じていた。
<Example 2>
A carpet was obtained in the same manner as in Example 1 except that a hydrophobic amino acid ratio constituting the feather keratin protein in Example 1 was 35.0%. In the temperature rise measurement test, the temperature rose by 4.8 ° C., and in the sensory evaluation with Comparative Example 1, all 10 people felt warm. In addition, even after 10 washes, the temperature rose by 2.9 ° C., and in sensory evaluation with Comparative Example 1, 9 people felt warm.
＜実施例３＞
実施例１において、羽毛ケラチン蛋白質０．１重量部を分散させ、０．２ｇ／m2を固着させた以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、２．８℃上昇し、比較例１との官能評価においては８人が温かいと感じていた。また洗濯１０回後でも２．５℃上昇し、比較例１との官能評価においては８人が温かいと感じていた。
<Example 3>
A carpet was obtained in the same manner as in Example 1 except that 0.1 part by weight of feather keratin protein was dispersed and 0.2 g / m 2 was fixed. In the temperature rise measurement test, the temperature rose by 2.8 ° C., and in sensory evaluation with Comparative Example 1, eight people felt warm. Further, even after 10 washings, the temperature rose by 2.5 ° C., and in sensory evaluation with Comparative Example 1, 8 people felt warm.
＜実施例４＞
実施例１において、羽毛ケラチン蛋白質２５重量部を分散させ、５０g/m2を固着させた以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、５．５℃上昇し、比較例１との官能評価においては１０人が温かいと感じていた。しかし、風合いが硬かった。また洗濯１０回後でも５．２℃上昇し、比較例1との官能評価においては１０人が温かいと感じていた。
<Example 4>
A carpet was obtained in the same manner as in Example 1 except that 25 parts by weight of feather keratin protein was dispersed and 50 g / m 2 was fixed. In the temperature rise measurement test, the temperature rose by 5.5 ° C., and in sensory evaluation with Comparative Example 1, 10 people felt warm. However, the texture was hard. Further, even after 10 washings, the temperature rose by 5.2 ° C., and in sensory evaluation with Comparative Example 1, 10 people felt warm.
＜比較例１＞
実施例１において、羽毛ケラチン蛋白質を用いなかった以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、１℃であった。また洗濯１０回後でも１℃の上昇であった。また、官能評価においての基準となるカーペットとした。
<Comparative Example 1>
In Example 1, a carpet was obtained in the same manner as in Example 1 except that feather keratin protein was not used. In the temperature rise measurement test, it was 1 ° C. Moreover, even after 10 washings, the temperature rose 1 ° C. Moreover, it was set as the carpet used as a reference | standard in sensory evaluation.
＜比較例２＞
実施例１において、羽毛ケラチン蛋白質２重量部の変わりにポリアクリル酸ナトリウム２重量部を用いた以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、４．０℃上昇し、比較例１との官能評価においては１０人全員が温かいと感じていた。また洗濯１０回後では１．２℃上昇し、比較例１との官能評価においては２人しか温かいと感じなかった。
<Comparative example 2>
A carpet was obtained in the same manner as in Example 1 except that 2 parts by weight of sodium polyacrylate was used instead of 2 parts by weight of feather keratin protein. In the temperature rise measurement test, the temperature rose by 4.0 ° C. In the sensory evaluation with Comparative Example 1, all 10 people felt warm. Further, after 10 washes, the temperature rose by 1.2 ° C., and in sensory evaluation with Comparative Example 1, only two people felt that they were warm.
＜比較例３＞
実施例１において、羽毛ケラチン蛋白質２重量部の変わりに羊毛ケラチン蛋白質（疎水性アミノ酸比率３０．８％）２重量部を用いた以外は実施例１と同様にしてカーペットを得た。温度上昇測定試験では、４．８℃上昇し、比較例１との官能評価においては１０人全員が温かいと感じていた。また洗濯１０回後では１．８℃上昇し、比較例１との官能評価においては４人しか温かいと感じなかった。
<Comparative Example 3>
A carpet was obtained in the same manner as in Example 1 except that 2 parts by weight of wool keratin protein (hydrophobic amino acid ratio 30.8%) was used instead of 2 parts by weight of feather keratin protein. In the temperature rise measurement test, the temperature rose by 4.8 ° C., and in the sensory evaluation with Comparative Example 1, all 10 people felt warm. Further, after 10 washes, the temperature rose by 1.8 ° C., and in sensory evaluation with Comparative Example 1, only 4 people felt that it was warm.
上述のように、羽毛ケラチン蛋白質をバインダーでパイル表面に固着したカーペットは、洗濯後でも未加工と比較して明らかに吸湿発熱効果があるカーペットとすることができた。 As described above, the carpet in which the feather keratin protein was fixed to the pile surface with the binder was able to be a carpet that clearly had a moisture absorption exothermic effect even after washing as compared with the unprocessed one.
１・・・吸湿発熱カーペット
２・・・パイル糸
３・・・基布
４・・・表皮層
５・・・バッキング層
６・・・セカンド基布
DESCRIPTION OF
Claims (1)
羽毛から抽出された羽毛ケラチン蛋白質が前記パイル糸にバインダー樹脂により０．５〜３０．０ｇ／ｍ ２ で固着されており、
前記バインダー樹脂の前記パイル糸に対する付着量は、０．５〜２０．０ｇ／ｍ ２ であり、
前記羽毛ケラチン蛋白質を構成する疎水性アミノ酸の含有率が４０％〜６０％であり、
前記羽毛ケラチン蛋白質の分子量が８０００〜１５０００である、
ことを特徴とする吸湿発熱カーペット。 In a carpet including a skin layer made of pile yarn and a base fabric, and a backing layer,
Feather keratin protein extracted from feathers is fixed to the pile yarn with a binder resin at 0.5 to 30.0 g / m 2 ,
The adhesion amount of the binder resin to the pile yarn is 0.5 to 20.0 g / m 2 .
The content of hydrophobic amino acids constituting the feather keratin protein is 40% to 60%,
The feather keratin protein has a molecular weight of 8000 to 15000,
A hygroscopic fever carpet characterized by that .