JP7848588B2 - Anti-slip flooring decorative sheets and anti-slip flooring decorative materials - Google Patents
Anti-slip flooring decorative sheets and anti-slip flooring decorative materialsInfo
- Publication number
- JP7848588B2 JP7848588B2 JP2022083137A JP2022083137A JP7848588B2 JP 7848588 B2 JP7848588 B2 JP 7848588B2 JP 2022083137 A JP2022083137 A JP 2022083137A JP 2022083137 A JP2022083137 A JP 2022083137A JP 7848588 B2 JP7848588 B2 JP 7848588B2
- Authority
- JP
- Japan
- Prior art keywords
- slip
- protrusions
- printed
- area
- plan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、防滑床用化粧シート及び防滑床用化粧材に関する。 This invention relates to a decorative sheet and decorative material for anti-slip floors.
従来の化粧シートに関する技術としては、例えば、特許文献１、２に記載されたものがある。
従来の化粧シート（特に防滑床用化粧シート）においては、不規則に配置された凸部形状を付与することで防滑性を付与する手法があったが、その多くには木目柄等が形成されておらず、意匠性が劣るものが多い。
また、不規則に配置された凸部形状に合わせて単に木目柄のエンボスを形成しただけでは、化粧シートに防滑性を付与することは困難である。
このように、従来技術に係る化粧シート（特に防滑床用化粧シート）には、意匠性と防滑性の両方を備えるものが少なかった。
Conventional technologies related to decorative sheets include, for example, those described in Patent Documents 1 and 2.
Conventional decorative sheets (especially those for anti-slip flooring) have been designed to provide anti-slip properties by adding irregularly placed protrusions, but many of these do not have wood grain patterns or other designs, resulting in inferior aesthetic appeal.
Furthermore, simply forming a wood grain pattern embossed to match the irregularly arranged protrusions makes it difficult to impart anti-slip properties to the decorative sheet.
Thus, there were few decorative sheets (especially decorative sheets for anti-slip floors) that possessed both aesthetic appeal and anti-slip properties.
本発明はこのような状況に鑑みてなされたものであって、意匠性と防滑性の両方を備えた防滑床用化粧シート及びその防滑床用化粧シートを備えた防滑床用化粧材を提供することを目的とする。 This invention has been made in view of the above circumstances, and aims to provide a decorative sheet for anti-slip flooring that possesses both aesthetic appeal and anti-slip properties, and a decorative material for anti-slip flooring equipped with this decorative sheet.
上記の課題を解決するために、本発明の一態様に係る防滑床用化粧シートは、基材シートと、前記基材シート上に形成された印刷層と、前記印刷層上に形成された樹脂層と、を備え、前記樹脂層に凸部及び凹部の少なくとも一方が形成されており、前記樹脂層の、前記印刷層の絵柄が印刷された領域と平面視で重なる領域には、規則的に配置された前記凸部及び前記凹部の少なくとも一方が形成されており、前記樹脂層の、前記印刷層の絵柄が印刷されていない領域と平面視で重なる領域には、ランダムに配置された前記凸部及び前記凹部の少なくとも一方が形成されていることを特徴とする。
本発明の別の態様に係る防滑床用化粧材は、上記態様の防滑床用化粧シートを床用基材に貼り合わせたことを特徴とする。
To solve the above problems, a decorative sheet for anti-slip floors according to one aspect of the present invention comprises a base sheet, a printed layer formed on the base sheet, and a resin layer formed on the printed layer, wherein at least one of convex portions and concave portions is formed on the resin layer, and in the area of the resin layer that overlaps in plan view with the area where the pattern of the printed layer is printed, at least one of the regularly arranged convex portions and concave portions is formed, and in the area of the resin layer that overlaps in plan view with the area where the pattern of the printed layer is not printed, at least one of the randomly arranged convex portions and concave portions is formed.
Another embodiment of the present invention provides a decorative anti-slip flooring material characterized by laminating the anti-slip flooring decorative sheet described above onto a flooring base material.
本発明の一態様によれば、意匠性と防滑性の両方を備えた防滑床用化粧シート及びその防滑床用化粧シートを備えた防滑床用化粧材を提供することができる。 According to one aspect of the present invention, it is possible to provide a decorative sheet for anti-slip flooring that possesses both aesthetic appeal and anti-slip properties, and a decorative material for anti-slip flooring equipped with the decorative sheet.
以下、本発明を実施するための形態について図面を参照しながら説明する。
＜実施形態＞
図１（ａ）及び（ｂ）は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０の構成例を模式的に示す断面図である。
図１（ａ）に示すように、防滑床用化粧材１０は、防滑床用化粧シート１と床用基材１１とを備える。また、防滑床用化粧シート１は、基材シート２と、基材シート２上に形成された印刷層３と、印刷層３上に形成された透明熱可塑性樹脂層（樹脂層）４と、透明熱可塑性樹脂層４上に形成されたトップコート層７を備える。
The embodiments for carrying out the present invention will be described below with reference to the drawings.
<Implementation>
Figures 1(a) and 1(b) are schematic cross-sectional views showing examples of the configuration of the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to the present invention.
As shown in Figure 1(a), the anti-slip flooring decorative material 10 comprises an anti-slip flooring decorative sheet 1 and a flooring base material 11. The anti-slip flooring decorative sheet 1 comprises a base sheet 2, a printed layer 3 formed on the base sheet 2, a transparent thermoplastic resin layer (resin layer) 4 formed on the printed layer 3, and a top coat layer 7 formed on the transparent thermoplastic resin layer 4.
防滑床用化粧シート１は、その表面（図１では、上面）に複数の凸部５（５ａ、５ｂ、５ｃ）を有しており、その表面にトップコート層７が設けられている。トップコート層７によって防滑床用化粧シート１の耐候性、耐傷性、耐汚染性などが強化される。
また、この防滑床用化粧シート１の裏面（図１では、下面）側を床用基材１１に貼付することで防滑床用化粧材１０となる。
床用基材１１としては、南洋材合板、パーティクルボード、中密度繊維板（以後ＭＤＦ）、日本農林規格に規定される普通合板が使用可能である。また、木紛添加オレフィン系樹脂からなる基材も使用可能である。床用基材１１の厚さは３～２５ｍｍ程度が好適である。
The anti-slip floor decorative sheet 1 has a plurality of protrusions 5 (5a, 5b, 5c) on its surface (top surface in Figure 1), and a top coat layer 7 is provided on this surface. The top coat layer 7 enhances the weather resistance, scratch resistance, and stain resistance of the anti-slip floor decorative sheet 1.
Furthermore, by attaching the back side (bottom side in Figure 1) of this anti-slip floor decorative sheet 1 to the floor base material 11, it becomes an anti-slip floor decorative material 10.
Suitable flooring materials 11 include tropical hardwood plywood, particleboard, medium-density fiberboard (MDF), and ordinary plywood as defined in the Japanese Agricultural Standards. A base material made of wood-powder-added olefin resin is also suitable. The thickness of the flooring material 11 is preferably 3 to 25 mm.
図２は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０の構成例を模式的に示す平面拡大図である。図３は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０の構成例を模式的に示す斜視図である。
図２、３に示すように、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａ（以下、単に「非絵柄領域Ａ」とも称する）には、ランダムに配置された複数の凸部５ａが形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂ（以下、単に「絵柄領域Ｂ」とも称する）には、規則的に配置された複数の凸部５ｂが形成されている。つまり、非絵柄領域Ａには、ランダムに配置された複数の凸部５ａが形成されている。また、絵柄領域Ｂには、規則的に配置された複数の凸部５ｂが形成されている。
Figure 2 is a schematic enlarged plan view showing an example of the configuration of the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to an embodiment of the present invention. Figure 3 is a schematic perspective view showing an example of the configuration of the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to an embodiment of the present invention.
As shown in Figures 2 and 3, in the transparent thermoplastic resin layer 4, in region A (hereinafter also simply referred to as "non-pattern region A") which overlaps in a plan view with the area of the printed layer 3 where the pattern is not printed, a plurality of randomly arranged protrusions 5a are formed, and in the transparent thermoplastic resin layer 4, in region B (hereinafter also simply referred to as "pattern region B") which overlaps in a plan view with the area of the printed layer 3 where the pattern is printed, a plurality of regularly arranged protrusions 5b are formed. In other words, in the non-pattern region A, a plurality of randomly arranged protrusions 5a are formed. In addition, in the pattern region B, a plurality of regularly arranged protrusions 5b are formed.
図４（ａ）及び（ｂ）は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０に備わる、ランダムに配置された凸部の構成例を模式的に示す平面図である。図４に示すように、複数の凸部５ａの各々の平面視による形状（以下、平面形状）は矩形（例えば、正方形）であり、それらの配置はランダム配置（すなわち、規則性のない配置）となっている。非絵柄領域Ａに、ランダムに配置された凸部５ａが形成されていることで、靴下やストッキング等、室内を想定した防滑性が向上するとともに、擦れ等による不快な干渉音が軽減される。 Figures 4(a) and 4(b) are schematic plan views illustrating an example of the configuration of randomly arranged protrusions on the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to an embodiment of the present invention. As shown in Figure 4, the planar shape of each of the multiple protrusions 5a (hereinafter referred to as the planar shape) is rectangular (for example, a square), and their arrangement is random (i.e., without regularity). The formation of randomly arranged protrusions 5a in the non-patterned area A improves slip resistance, such as when wearing socks or stockings indoors, and reduces unpleasant interference noises caused by friction.
凸部５ａは、規則性を持たないように考慮して配置されたものであればよく、例えば、乱数計算を用いて無作為（ランダム）に配置されたものである。具体的には、非絵柄領域Ａには、乱数計算によって算出された情報を基に凸部５ａがランダムに配置されていてもよい。ここで、「ランダムな配置」とは、１ｃｍ２当たりに形成された凸部５ａ間の平均距離のばらつき（３σ：標準偏差σの３倍値）が０．１μｍ超となるように、凸部５ａが配置されている状態をいう。
凸部５ａとしては、高さ２０μｍ以上８０μｍ以下が好ましい。凸部５ａの高さが２０μｍ未満では防滑性能が劣り、８０μｍより大きいと凸部形状の形成が難しい等の製造工程が困難となる。ここで、凸部５ａの高さとは、図１（ｂ）に示すように、凸部５ａの底部から頂部までの高さＡのことである。この高さＡは、透明熱可塑性樹脂層４の表面に形成された凹凸のうち、隣り合う凸部５（５ａ）と凹部６との高低差でもある。
The protrusions 5a can be arranged in a manner that avoids any regularity, for example, by randomizing them using random number calculations. Specifically, in the non-pattern area A, the protrusions 5a may be randomly arranged based on information calculated by random number calculations. Here, "random arrangement" refers to a state in which the protrusions 5a are arranged such that the variation in the average distance between the protrusions 5a formed per 1 cm² (3σ: three times the standard deviation σ) is greater than 0.1 μm.
The height of the protrusion 5a is preferably 20 μm or more and 80 μm or less. If the height of the protrusion 5a is less than 20 μm, the anti-slip performance will be poor, and if it is greater than 80 μm, the manufacturing process will be difficult, such as difficulty in forming the shape of the protrusion. Here, the height of the protrusion 5a is the height A from the bottom to the top of the protrusion 5a, as shown in Figure 1(b). This height A is also the height difference between adjacent protrusions 5 (5a) and recesses 6 among the irregularities formed on the surface of the transparent thermoplastic resin layer 4.
また、図４（ｂ）に示すように、凸部５ａの外径は、２５μｍ以上６０μｍ以下の範囲内であれば好ましい。より詳しくは、平面視で、凸部５ａの一辺の長さＢ（凸部５ａの外径）は２５μｍ以上６０μｍ以下が好ましい。凸部５ａの一辺の長さＢが２５μｍ未満では防滑性が劣り、６０μｍより大きいと凸部５ａが肉眼で視認し易くなり意匠感が好ましくない。
また、凸部５ａの面密度（すなわち、平面視で単位面積当たりの凸部が占める割合）は、０．０５以上０．５以下が好ましい。この面密度が０．０５未満の場合や０．５より大きい場合はいずれも防滑性が劣る。なお、凸部５ａの平面形状が正方形の場合、凸部５ａの面密度は、ｎ×Ｂ２／Ｃ２で表すことができる。ここで、Ｃは、平面視で任意に画定した正方形の一辺の長さであり、ｎはこの正方形に含まれる凸部５ａの個数である。
また、凸部５ａは、１ｍｍ２当り７０個以上１６０個以下の範囲内で形成されていれば好ましく、９０個以上１４０個以下の範囲内で形成されていればより好ましく、１１０個以上１２０個以下の範囲内で形成されていればさらに好ましい。１ｍｍ２当りの凸部５ａの数が７０個未満では防滑性が劣り、１６０個より多いと凸部５ａが肉眼で視認し易くなり意匠感が好ましくない。
Furthermore, as shown in Figure 4(b), the outer diameter of the protrusion 5a is preferably within the range of 25 μm to 60 μm. More specifically, in a plan view, the length B of one side of the protrusion 5a (outer diameter of the protrusion 5a) is preferably 25 μm to 60 μm. If the length B of one side of the protrusion 5a is less than 25 μm, the anti-slip properties are poor, and if it is greater than 60 μm, the protrusion 5a becomes easily visible to the naked eye, which is undesirable in terms of design.
Furthermore, the surface density of the protrusions 5a (i.e., the ratio of protrusions per unit area in a plan view) is preferably 0.05 or more and 0.5 or less. If this surface density is less than 0.05 or greater than 0.5, the anti-slip properties are poor. Note that if the planar shape of the protrusions 5a is a square, the surface density of the protrusions 5a can be expressed as n × B² / C² . Here, C is the length of one side of a square arbitrarily defined in a plan view, and n is the number of protrusions 5a contained in this square.
Furthermore, it is preferable that the number of protrusions 5a per 1 mm² be between 70 and 160, more preferably between 90 and 140, and even more preferably between 110 and 120. If the number of protrusions 5a per 1 mm² is less than 70, the anti-slip properties are poor, and if it is more than 160, the protrusions 5a become easily visible to the naked eye, resulting in an undesirable aesthetic appearance.
図５は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０に備わる、規則的に配置された凸部の構成例を模式的に示す平面図である。図５に示すように、複数の凸部５ｂの各々の平面形状は矩形（例えば、正方形）であり、それらの配置は、例えば千鳥格子のような等間隔で規則性のある配置となっている。絵柄領域Ｂに、規則的に配置された凸部５ｂが形成されていることで、自然な絵柄（例えば、木目柄）を再現できる、即ち意匠性が高まるとともに、さらに防滑性が向上する。 Figure 5 is a schematic plan view illustrating an example of the configuration of regularly arranged protrusions in the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to an embodiment of the present invention. As shown in Figure 5, the planar shape of each of the multiple protrusions 5b is rectangular (for example, square), and their arrangement is regular and evenly spaced, such as a houndstooth pattern. The regularly arranged protrusions 5b are formed in the pattern area B, allowing for the reproduction of natural patterns (for example, wood grain patterns), thus enhancing both aesthetic appeal and slip resistance.
凸部５ｂは、規則性を持つように考慮して配置されたものであればよく、例えば、格子状に配置されたものである。ここで、「規則的な配置」とは、１ｃｍ２当たりに形成された凸部５ｂ間の平均距離のばらつき（３σ：標準偏差σの３倍値）が０．１μｍ以下となるように、凸部５ｂが配置されている状態をいう。
凸部５ｂとしては、凸部５ａと同様に、高さ２０μｍ以上８０μｍ以下が好ましい。凸部５ｂの高さが２０μｍ未満では防滑性能が劣り、８０μｍより大きいと凸部形状の形成が難しい等の製造工程が困難となる。ここで、凸部５ｂの高さとは、凸部５ａと同様に、図１（ｂ）に示すように、凸部５ｂの底部から頂部までの高さＡのことである。この高さＡは、透明熱可塑性樹脂層４の表面に形成された凹凸のうち、隣り合う凸部５（５ｂ）と凹部６との高低差でもある。
The protrusions 5b only need to be arranged in a way that gives them regularity, for example, they can be arranged in a grid pattern. Here, "regular arrangement" means that the protrusions 5b are arranged such that the variation in the average distance between the protrusions 5b formed per 1 cm² (3σ: three times the standard deviation σ) is 0.1 μm or less.
Similar to the protrusion 5a, the height of the protrusion 5b is preferably 20 μm or more and 80 μm or less. If the height of the protrusion 5b is less than 20 μm, the anti-slip performance will be poor, and if it is greater than 80 μm, the manufacturing process will be difficult, such as difficulty in forming the protrusion shape. Here, the height of the protrusion 5b is the height A from the bottom to the top of the protrusion 5b, as shown in Figure 1(b), similar to the height of the protrusion 5a. This height A is also the height difference between adjacent protrusions 5 (5b) and recesses 6 among the irregularities formed on the surface of the transparent thermoplastic resin layer 4.
また、図５（ｂ）に示すように、凸部５ｂの外径は、凸部５ａと同様に、２５μｍ以上６０μｍ以下の範囲内であれば好ましい。より詳しくは、平面視で、凸部５ｂの一辺の長さＢ（凸部５ｂの外径）は２５μｍ以上６０μｍ以下が好ましい。凸部５ｂの一辺の長さＢが２５μｍ未満では防滑性が劣り、６０μｍより大きいと凸部５ａが肉眼で視認し易くなり意匠感が好ましくない。
また、凸部５ｂの面密度は、凸部５ａと同様に、０．０５以上０．５以下が好ましい。この面密度が０．０５未満の場合や０．５より大きい場合はいずれも防滑性が劣る。なお、凸部５ｂの平面形状が正方形の場合、凸部５ｂの面密度は、ｎ×Ｂ２／Ｃ２で表すことができる。ここで、Ｃは、平面視で任意に画定した正方形の一辺の長さであり、ｎはこの正方形に含まれる凸部５ｂの個数である。
また、凸部５ｂは、凸部５ａと同様に、１ｍｍ２当り７０個以上１６０個以下の範囲内で形成されていれば好ましく、９０個以上１４０個以下の範囲内で形成されていればより好ましく、１１０個以上１２０個以下の範囲内で形成されていればさらに好ましい。１ｍｍ２当りの凸部５ｂの数が７０個未満では防滑性が劣り、１６０個より多いと凸部５ｂが肉眼で視認し易くなり意匠感が好ましくない。
Furthermore, as shown in Figure 5(b), the outer diameter of the protrusion 5b is preferably within the range of 25 μm to 60 μm, similar to the protrusion 5a. More specifically, in a plan view, the length B of one side of the protrusion 5b (outer diameter of the protrusion 5b) is preferably 25 μm to 60 μm. If the length B of one side of the protrusion 5b is less than 25 μm, the anti-slip properties are poor, and if it is greater than 60 μm, the protrusion 5a becomes easily visible to the naked eye, resulting in an undesirable design.
Furthermore, the surface density of the protrusions 5b is preferably 0.05 or more and 0.5 or less, similar to the protrusions 5a. If the surface density is less than 0.05 or greater than 0.5, the anti-slip properties are poor. When the planar shape of the protrusions 5b is a square, the surface density of the protrusions 5b can be expressed as n × B² / C² . Here, C is the length of one side of a square arbitrarily defined in plan view, and n is the number of protrusions 5b contained in this square.
Furthermore, the protrusions 5b are preferably formed in the same range as the protrusions 5a, with a number of 70 to 160 per 1 mm² , more preferably in the range of 90 to 140, and even more preferably in the range of 110 to 120. If the number of protrusions 5b per 1 mm² is less than 70, the anti-slip properties are poor, and if there are more than 160, the protrusions 5b become easily visible to the naked eye, resulting in an undesirable aesthetic appearance.
図６は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０に備わる傾斜部の構成例を模式的に示す断面図である。図６に示すように、絵柄領域Ｂの周囲の少なくとも一部には、絵柄領域Ｂから離れるにしたがって、高さが低くなるように傾斜した傾斜面Ｓを備えた傾斜凸部５ｃが単数、または複数形成されている。
この傾斜面Ｓの傾斜度は、絵柄領域Ｂの周囲から１μｍ離れるごとに、高さが０．１０μｍ以上１０．０μｍ以下の範囲内で低くなるように傾斜していれば好ましく、高さが０．１μｍ以上５μｍ以下の範囲内で低くなるように傾斜していればより好ましく、高さが０．１μｍ以上０．３μｍ以下の範囲内で低くなるように傾斜していればさらに好ましい。傾斜面Ｓの傾斜度が上記数値範囲内であれば、自然な絵柄（例えば、木目柄）を再現できる、即ち意匠性が高まるとともに、さらに防滑性が向上する。また、靴下やストッキング等、室内を想定した防滑性が向上するとともに、擦れ等による不快な干渉音が軽減される。
複数の傾斜凸部５ｃの各々の平面形状は矩形（例えば、正方形）であれば好ましい。
Figure 6 is a schematic cross-sectional view showing an example of the configuration of the inclined portion provided in the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to an embodiment of the present invention. As shown in Figure 6, at least a portion of the area around the pattern area B has one or more inclined protrusions 5c, each having an inclined surface S that decreases in height as it moves away from the pattern area B.
The inclination of this inclined surface S is preferably such that the height decreases by 0.10 μm to 10.0 μm for every 1 μm distance from the periphery of the pattern area B, more preferably by 0.1 μm to 5 μm, and even more preferably by 0.1 μm to 0.3 μm. If the inclination of the inclined surface S is within the above numerical range, a natural pattern (for example, a wood grain pattern) can be reproduced, that is, the design quality is enhanced, and the slip resistance is further improved. In addition, the slip resistance is improved for indoor use, such as with socks and stockings, and unpleasant interference noises caused by rubbing are reduced.
It is preferable that the planar shape of each of the multiple inclined protrusions 5c is rectangular (for example, a square).
防滑床用化粧シート１は、基材シート２に印刷層３を設けて基材層とする。印刷は通常知られている。例えばグラビア印刷法などを用いることができる。
基材シート２には、たとえば塩化ビニル樹脂、アクリル樹脂、またポリオレフィン系のポリプロピレン樹脂あるいはポリエチレン樹脂、などを用いることができる。なかでも環境適合性や加工性、価格の点でポリオレフィン系熱可塑性樹脂を好ましく用いることができる。樹脂のグレードや組成は、そのほかにシーティングの容易さや印刷適性、曲げ加工に対する適性を考慮して選択することができる。
The anti-slip floor decorative sheet 1 has a base sheet 2 on which a printed layer 3 is provided as the base layer. Printing is generally known; for example, gravure printing can be used.
The base sheet 2 can be made of, for example, polyvinyl chloride resin, acrylic resin, or polyolefin-based polypropylene resin or polyethylene resin. Among these, polyolefin-based thermoplastic resins are preferred in terms of environmental compatibility, processability, and cost. The grade and composition of the resin can also be selected considering ease of sheeting, printability, and suitability for bending.
印刷層３の上に透明熱可塑性樹脂層４を設け、その表面に複数の凸部５（５ａ、５ｂ、５ｃ）を形成する。複数の凸部５ａ、５ｂの各々の形状及び大きさは、例えば、互いに同一である。透明熱可塑性樹脂層４の形成方法は、ポリプロピレンのフィルムを貼りあわせる方法でもよく、透明熱可塑性樹脂層４を押し出し機を用いて印刷層３の上に形成する方法でもよい。凸部５（５ａ、５ｂ、５ｃ）の形成方法は、例えばエンボス型を用いて加熱、加圧して透明熱可塑性樹脂層４の表面に凹凸形状を形成する方法（いわゆるエンボス加工）などでもよい。押し出し機により透明熱可塑性樹脂層４を形成する場合は、押し出しの直後にエンボスロールなどによって、透明熱可塑性樹脂層４の表面に凸部５（５ａ、５ｂ、５ｃ）を形成することができる。 A transparent thermoplastic resin layer 4 is provided on the printed layer 3, and multiple protrusions 5 (5a, 5b, 5c) are formed on its surface. The shape and size of each of the multiple protrusions 5a, 5b are, for example, identical. The transparent thermoplastic resin layer 4 may be formed by laminating polypropylene films, or by forming the transparent thermoplastic resin layer 4 on the printed layer 3 using an extruder. The method for forming the protrusions 5 (5a, 5b, 5c) may be, for example, a method of forming an uneven surface on the transparent thermoplastic resin layer 4 by heating and pressurizing using an embossing die (so-called embossing). When forming the transparent thermoplastic resin layer 4 using an extruder, the protrusions 5 (5a, 5b, 5c) can be formed on the surface of the transparent thermoplastic resin layer 4 immediately after extrusion using an embossing roll or the like.
防滑床用化粧シート１の最表面にはトップコート層７を設ける。トップコート層７には、熱硬化性樹脂、紫外線硬化型樹脂、若しくは電子線硬化型樹脂などの架橋型の樹脂を用いることで、防滑床用化粧シートの耐候性、耐傷性、耐汚染性などを強化することができる。これらの樹脂は単独で用いてもよく、混合して用いてもよい。例えば、トップコート層７として、上記樹脂のうち複数の樹脂を混合して用いてもよいし、上記樹脂のうち一の樹脂と上記以外の他の樹脂とを混合して用いてもよい。また、これらの樹脂は既知のコーティング機を用いて塗布すればよく、架橋のタイプに合わせて熱あるいは紫外線、もしくは電子線の照射を行って硬化させればよい。なお、透明熱可塑性樹脂層４の表面に形成された凸部５（５ａ、５ｂ、５ｃ）の形状は、その上に形成されるトップコート層７に反映され、トップコート層７の表面にも凸部が形成される。 A topcoat layer 7 is provided on the outermost surface of the anti-slip floor decorative sheet 1. By using a cross-linked resin such as a thermosetting resin, UV-curing resin, or electron beam-curing resin for the topcoat layer 7, the weather resistance, scratch resistance, and stain resistance of the anti-slip floor decorative sheet can be enhanced. These resins may be used individually or in mixtures. For example, the topcoat layer 7 may be a mixture of several of the above resins, or one of the above resins may be mixed with another resin. These resins can be applied using a known coating machine and cured by heat, UV light, or electron beam irradiation according to the cross-linking type. The shape of the protrusions 5 (5a, 5b, 5c) formed on the surface of the transparent thermoplastic resin layer 4 is reflected in the topcoat layer 7 formed on top of it, and protrusions are also formed on the surface of the topcoat layer 7.
＜実施形態の効果＞
本発明の実施形態は、以下の効果（１）～（６）を奏する。
（１）透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、ランダムに配置された凸部５ａが形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂには、規則的に配置された凸部５ｂが形成されている。これにより、優れた意匠性と、高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を維持することができる。
<Effects of the embodiment>
Embodiments of the present invention provide the following effects (1) to (6).
(1) In the transparent thermoplastic resin layer 4, randomly arranged protrusions 5a are formed in region A, which overlaps in a plan view with the area of the printed layer 3 where the pattern is not printed, and in the transparent thermoplastic resin layer 4, regularly arranged protrusions 5b are formed in region B, which overlaps in a plan view with the area of the printed layer 3 where the pattern is printed. This makes it possible to achieve excellent design and high slip resistance. Furthermore, with the above configuration, the stain resistance required for flooring can be maintained.
（２）ランダムに配置された凸部５ａの外径Ｂは、２５μｍ以上６０μｍ以下の範囲内であれば好ましい。これにより、さらに優れた意匠性と、高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を容易に維持することができる。 (2) The outer diameter B of the randomly arranged protrusions 5a is preferably within the range of 25 μm to 60 μm. This allows for even better design and high slip resistance. Furthermore, with the above configuration, the stain resistance required for flooring can be easily maintained.
（３）ランダムに配置された凸部５ａは、１ｍｍ２当り７０個以上１６０個以下の範囲内で形成されていれば好ましい。これにより、さらに優れた意匠性と、さらに高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を確実に維持することができる。 (3) Preferably, the randomly arranged protrusions 5a are formed in a range of 70 to 160 per 1 mm² . This makes it possible to achieve even better design and even higher slip resistance. Furthermore, with the above configuration, the stain resistance required for flooring can be reliably maintained.
（４）透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、乱数計算によって算出された情報を基に凸部５ａがランダムに配置されていれば好ましい。これにより、さらに優れた意匠性と、さらに高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を容易に維持することができる。 (4) It is preferable that the protrusions 5a are randomly arranged in the region A of the transparent thermoplastic resin layer 4 that overlaps with the area of the printed layer 3 where the pattern is not printed, in a plan view, based on information calculated by random number calculation. This makes it possible to achieve even better design and even higher slip resistance. Furthermore, with the above configuration, the stain resistance required for flooring can be easily maintained.
（５）透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂの周囲の少なくとも一部には、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂから離れるにしたがって、高さが低くなるように傾斜した傾斜面Ｓを備えた傾斜凸部５ｃ、及び深さが浅くなるように傾斜した傾斜面Ｓを備えた傾斜凹部（図示せず）の少なくとも一方が形成されていれば好ましい。これにより、さらに優れた意匠性と、さらに高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を確実に維持することができる。 (5) Preferably, at least one of the following is formed on the periphery of the transparent thermoplastic resin layer 4: an inclined convex portion 5c with an inclined surface S that decreases in height as it moves away from the area B where the pattern of the printed layer 3 is printed, and an inclined recess (not shown) with an inclined surface S that decreases in depth as it moves away from the area B where the pattern of the printed layer 3 is printed. This allows for even better design and even higher slip resistance. Furthermore, with the above configuration, the stain resistance required for flooring can be reliably maintained.
（６）傾斜面Ｓは、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ａの周囲から１μｍ離れるごとに、高さが０．１０μｍ以上１０μｍ以下の範囲内で低くなるように、または高くなるように傾斜していれば好ましい。これにより、さらに優れた意匠性と、さらに高い防滑性能とを実現することができる。さらに、上記構成であれば、床として必要な耐汚染性を維持することができる。 (6) Preferably, the inclined surface S is inclined such that its height decreases or increases by a range of 0.10 μm to 10 μm for every 1 μm distance from the periphery of the region A where the pattern of the printed layer 3 of the transparent thermoplastic resin layer 4 overlaps in a plan view. This allows for even better design and even higher slip resistance. Furthermore, with the above configuration, the stain resistance required for a floor can be maintained.
＜変形例１＞
上記の実施形態では、凸部５ａ、５ｂの平面形状が正方形である場合について説明した。しかしながら、本発明において、凸部５ａ、５ｂの平面形状は正方形に限定されるものではない。凸部５ａ、５ｂの平面形状は長方形でもよいし、四角以外の多角形（三角形、五角形、六角形、…）でもよし、十字形でもよい。以下、凸部５ａを例に挙げて、変形例１を説明する。なお、凸部５ｂは、以下で説明する変形例１と同様の形態を取り得る。
<Variation 1>
In the above embodiment, the case where the planar shape of the protrusions 5a and 5b is a square was described. However, in the present invention, the planar shape of the protrusions 5a and 5b is not limited to a square. The planar shape of the protrusions 5a and 5b may be a rectangle, a polygon other than a square (triangle, pentagon, hexagon, ...), or a cross shape. Below, Modification 1 will be described using the protrusion 5a as an example. Note that the protrusion 5b may take the same form as Modification 1 described below.
図７（ａ）及び（ｂ）は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０の他の構成例（変形例１）を模式的に示す平面図である。
図７（ａ）に示すように、ランダムに配置された凸部５ａの平面形状は正三角形でもよい。図７（ｂ）に示すように、正三角形の一辺の長さＢは２５μｍ以上６０μｍ以下が好ましい。一辺の長さＢが２５μｍ未満では防滑性が劣り、６０μｍより大きいと凸部５ａが肉眼で視認し易くなり意匠感が好ましくない。また、この変形例１においても、凸部５ａの面密度（すなわち、平面視で単位面積当たりの凸部が占める割合）は、０．０５以上０．５以下が好ましい。この面密度が０．０５未満の場合や０．５より大きい場合はいずれも防滑性が劣る。凸部５ａの平面形状が正三角形の場合、その面密度は、ｎ×（√３／４）×Ｂ２／Ｃ２で表すことができる。ここで、Ｃは、平面視で任意に画定した正方形の一辺の長さであり、ｎはこの正方形に含まれる正三角形の凸部５ａの個数である。
Figures 7(a) and 7(b) are schematic plan views showing another configuration example (modification 1) of the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to the present invention.
As shown in Figure 7(a), the planar shape of the randomly arranged protrusions 5a may be an equilateral triangle. As shown in Figure 7(b), the side length B of the equilateral triangle is preferably 25 μm or more and 60 μm or less. If the side length B is less than 25 μm, the anti-slip properties are poor, and if it is greater than 60 μm, the protrusions 5a become easily visible to the naked eye, which is undesirable in terms of design. In this modified example 1 as well, the surface density of the protrusions 5a (i.e., the ratio of protrusions per unit area in a planar view) is preferably 0.05 or more and 0.5 or less. If this surface density is less than 0.05 or greater than 0.5, the anti-slip properties are poor in both cases. When the planar shape of the protrusions 5a is an equilateral triangle, its surface density can be expressed as n × (√3/4) × B² / C² . Here, C is the side length of a square arbitrarily defined in a planar view, and n is the number of equilateral triangular protrusions 5a contained in this square.
また、図示しないが、この変形例１においても、凸部５ａの高さは２０μｍ以上８０μｍ以下が好ましい。凸部５ａの高さが２０μｍ未満では防滑性能が劣り、８０μｍより大きいと凸部形状の形成が難しい等の製造工程が困難となる。
図７に示す変形例１も、上記の実施形態と同様の効果を奏する。
Furthermore, although not shown in the figures, in this modified example 1 as well, the height of the protrusion 5a is preferably 20 μm or more and 80 μm or less. If the height of the protrusion 5a is less than 20 μm, the anti-slip performance will be poor, and if it is greater than 80 μm, the manufacturing process will be difficult, such as difficulty in forming the shape of the protrusion.
Modification 1 shown in Figure 7 also achieves the same effects as the embodiment described above.
＜変形例２＞
また、本発明において、凸部５ａ、５ｂの平面形状は多角形に限定されるものでなく、円形（正円形や、楕円形など）でもよい。以下、凸部５ａを例に挙げて、変形例２を説明する。なお、凸部５ｂは、以下で説明する変形例２と同様の形態を取り得る。
図８（ａ）及び（ｂ）は、本発明の実施形態に係る防滑床用化粧シート１及び防滑床用化粧材１０の他の構成例（変形例２）を模式的に示す平面図である。
図８（ａ）に示すように、ランダムに配置された凸部５ａの平面形状は正円形でもよい。図８（ｂ）に示すように、正円形の直径Ｂは２５μｍ以上６０μｍ以下が好ましい。直径Ｂが２５μｍ未満では防滑性が劣り、６０μｍより大きいと凸部５ａが肉眼で視認し易くなり意匠感が好ましくない。また、この変形例２においても、凸部５ａの面密度（すなわち、平面視で単位面積当たりの凸部が占める割合）は、０．０５以上０．５以下が好ましい。この面密度が０．０５未満の場合や０．５より大きい場合はいずれも防滑性が劣る。凸部５ａの平面形状が正円形の場合、その面密度は、ｎ×（π／４）×Ｂ２／Ｃ２で表すことができる。ここで、Ｃは、平面視で任意に画定した正方形の一辺の長さであり、ｎはこの正方形に含まれる正円形の凸部５ａの個数である。
<Modified Example 2>
Furthermore, in the present invention, the planar shape of the protrusions 5a and 5b is not limited to a polygon, but may be circular (such as a perfect circle or an ellipse). Below, Modification 2 will be described using protrusion 5a as an example. Note that protrusion 5b may take the same form as Modification 2 described below.
Figures 8(a) and 8(b) are schematic plan views showing another configuration example (modification 2) of the anti-slip floor decorative sheet 1 and anti-slip floor decorative material 10 according to the present invention.
As shown in Figure 8(a), the planar shape of the randomly arranged protrusions 5a may be a perfect circle. As shown in Figure 8(b), the diameter B of the perfect circle is preferably 25 μm or more and 60 μm or less. If the diameter B is less than 25 μm, the anti-slip properties are poor, and if it is greater than 60 μm, the protrusions 5a become easily visible to the naked eye, which is undesirable in terms of design. In this modified example 2 as well, the surface density of the protrusions 5a (i.e., the ratio of protrusions per unit area in a planar view) is preferably 0.05 or more and 0.5 or less. If this surface density is less than 0.05 or greater than 0.5, the anti-slip properties are poor in both cases. When the planar shape of the protrusions 5a is a perfect circle, its surface density can be expressed as n × (π/4) × B² / C² . Here, C is the length of one side of a square arbitrarily defined in a planar view, and n is the number of perfect circular protrusions 5a contained in this square.
また、図示しないが、この変形例２においても、凸部５ａの高さは２０μｍ以上８０μｍ以下が好ましい。凸部５ａの高さが２０μｍ未満では防滑性能が劣り、８０μｍより大きいと凸部形状の形成が難しい等の製造工程が困難となる。
図８に示す変形例２も、上記の実施形態と同様の効果を奏する。
Furthermore, although not shown in the figures, in this modified example 2, the height of the protrusion 5a is preferably 20 μm or more and 80 μm or less. If the height of the protrusion 5a is less than 20 μm, the anti-slip performance is poor, and if it is greater than 80 μm, the manufacturing process becomes difficult, such as when it is difficult to form the shape of the protrusion.
Modification 2 shown in Figure 8 also achieves the same effects as the embodiment described above.
＜変形例３＞
また、図１に示したように、上記の実施形態では、凸部５ａ、５ｂの断面視による形状（以下、断面形状）が矩形である場合（つまり、底部から頂部にかけて幅が一定の柱状である場合）について説明した。しかしながら、本発明において、凸部５ａ、５ｂの断面形状は矩形に限定されるものではない。本発明において、凸部５ａ、５ｂの断面形状は台形（すなわち、底部から頂部に向かって、幅が徐々に小さくなる柱状）でもよいし、錐状でもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。
<Example 3>
Furthermore, as shown in Figure 1, the above embodiment described the case where the cross-sectional shape of the protrusions 5a and 5b (hereinafter referred to as the cross-sectional shape) is rectangular (that is, a columnar shape with a constant width from the bottom to the top). However, in the present invention, the cross-sectional shape of the protrusions 5a and 5b is not limited to a rectangle. In the present invention, the cross-sectional shape of the protrusions 5a and 5b may be trapezoidal (that is, a columnar shape with a gradually decreasing width from the bottom to the top) or conical. Even with such a configuration, the same effects as in the above embodiment can be achieved.
＜変形例４＞
また、図１に示したように、上記の実施形態では、防滑床用化粧シート１及び防滑床用化粧材１０の表面構造として、凸部５ａ、５ｂを備えた場合について説明した。しかしながら、本発明において、防滑床用化粧シート１及び防滑床用化粧材１０の表面構造は凸部５ａ、５ｂに限定されるものではない。本発明において、凸部５ａ、５ｂに代えて、凹部（図示せず）が形成されていてもよい。つまり、透明熱可塑性樹脂層４には凹部が形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂには、規則的に配置された凹部が形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、ランダムに配置された凹部が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。
<Modification 4>
Furthermore, as shown in Figure 1, the above embodiment described a case in which the surface structure of the anti-slip floor decorative sheet 1 and the anti-slip floor decorative material 10 is provided with protrusions 5a and 5b. However, in the present invention, the surface structure of the anti-slip floor decorative sheet 1 and the anti-slip floor decorative material 10 is not limited to protrusions 5a and 5b. In the present invention, recesses (not shown) may be formed instead of protrusions 5a and 5b. That is, recesses may be formed in the transparent thermoplastic resin layer 4, and regularly arranged recesses may be formed in region B of the transparent thermoplastic resin layer 4 that overlaps in plan view with the area where the pattern of the printed layer 3 is printed, and randomly arranged recesses may be formed in region A of the transparent thermoplastic resin layer 4 that overlaps in plan view with the area where the pattern of the printed layer 3 is not printed. Even with such a configuration, the same effects as in the above embodiment can be achieved.
勿論、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂには、規則的に配置された凹部と凸部の両方が形成されていてもよく、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、ランダムに配置された凹部と凸部の両方が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。
また、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂには、規則的に配置された凹部が形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、ランダムに配置された凸部が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。
Of course, in the transparent thermoplastic resin layer 4, region B which overlaps in a plan view with the area where the pattern of the printed layer 3 is printed may have both regularly arranged recesses and protrusions, and in the transparent thermoplastic resin layer 4, region A which overlaps in a plan view with the area where the pattern of the printed layer 3 is not printed may have both randomly arranged recesses and protrusions. Even with such a configuration, the same effects as in the above embodiment will be achieved.
Furthermore, in the transparent thermoplastic resin layer 4, the region B that overlaps with the printed area of the printed layer 3 in a plan view may have regularly arranged recesses, and in the transparent thermoplastic resin layer 4, the region A that overlaps with the unprinted area of the printed layer 3 in a plan view may have randomly arranged protrusions. Even with such a configuration, the same effects as in the above embodiment can be achieved.
これと同様に、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂには、規則的に配置された凸部が形成されており、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷されていない領域と平面視で重なる領域Ａには、ランダムに配置された凹部が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。 Similarly, in the transparent thermoplastic resin layer 4, the region B that overlaps with the printed area of the printed layer 3 in a plan view may have regularly arranged protrusions, while in the transparent thermoplastic resin layer 4, the region A that overlaps with the unprinted area of the printed layer 3 in a plan view may have randomly arranged recesses. Even with this configuration, the same effects as in the above embodiment can be achieved.
＜変形例５＞
また、図６に示したように、上記の実施形態では、防滑床用化粧シート１及び防滑床用化粧材１０の表面構造として、傾斜凸部５ｃを備えた場合について説明した。しかしながら、本発明において、防滑床用化粧シート１及び防滑床用化粧材１０の表面構造は傾斜凸部５ｃに限定されるものではない。本発明において、傾斜凸部５ｃに代えて、傾斜凹部（図示せず）が形成されていてもよい。つまり、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂの周囲の少なくとも一部には、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂから離れるにしたがって、深さが浅くなるように傾斜した傾斜面を備えた傾斜凹部が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。
<Example 5>
Furthermore, as shown in Figure 6, the above embodiment described a case in which the surface structure of the anti-slip floor decorative sheet 1 and the anti-slip floor decorative material 10 is provided with inclined protrusions 5c. However, in the present invention, the surface structure of the anti-slip floor decorative sheet 1 and the anti-slip floor decorative material 10 is not limited to inclined protrusions 5c. In the present invention, inclined recesses (not shown) may be formed instead of inclined protrusions 5c. That is, at least a portion of the area B of the transparent thermoplastic resin layer 4 that overlaps with the area of the printed layer 3 in a plan view may be formed, and inclined recesses may be formed with inclined surfaces that become shallower as they move away from the area B that overlaps with the area of the printed layer 3 in a plan view. Even with such a configuration, the same effects as in the above embodiment will be achieved.
勿論、透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂの周囲の少なくとも一部には、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂから離れるにしたがって、深さが浅くなるように傾斜した傾斜面を備えた傾斜凹部と、印刷層３の絵柄が印刷された領域と平面視で重なる領域Ｂから離れるにしたがって、高さが低くなるように傾斜した傾斜面Ｓを備えた傾斜凸部５ｃの両方が形成されていてもよい。このような構成であっても、上記の実施形態と同様の効果を奏する。 Of course, at least a portion of the transparent thermoplastic resin layer 4 around the region B that overlaps with the printed area of the printed layer 3 in a plan view may have both an inclined recess with an inclined surface that becomes shallower as it moves away from region B, and an inclined protrusion 5c with an inclined surface S that becomes lower as it moves away from region B, the area where the printed pattern of the printed layer 3 overlaps in a plan view. Even with such a configuration, the same effects as in the above embodiment can be achieved.
［実施例］
以下、本発明の実施例について説明するが、本発明は、以下の実施例に限定されるものではない。
[Examples]
The following describes embodiments of the present invention, but the present invention is not limited to the following embodiments.
（実施例１）
防滑床用化粧シートを下記の材料と手順で作成した。
ポリプロピレン原反層（基材シート２）として、厚さ６０μｍの顔料配合ランダムポリプロピレンシート（リケンテクノス社製）を用いた。
次に、このポリプロピレン原反層上に、グラビア印刷によってウレタンインキ（東洋インキ製造製ラミスター）を用いて、木目柄が印刷された印刷層（印刷層３）を形成した。
次に、この印刷層上にポリプロピレンクリア層（透明熱可塑性樹脂層４）として、ホモポリプロピレン樹脂（プライムポリマー社製）を押出し機によって形成し、押し出すと同時にエンボス版を用いてエンボス部（凸部５及び凹部６）を形成した。
最後に、トップコート層（トップコート層７）として、紫外線硬化型樹脂（ＤＩＣグラフィック社製ウレタンアクリレート樹脂）を１０μｍの厚さになるよう塗布し、メタルハライドランプにて紫外線照射を行って塗工液を硬化させた。こうして、トップコート層を形成した。
(Example 1)
The anti-slip floor covering sheet was created using the following materials and procedure.
A 60 μm thick pigment-blended random polypropylene sheet (manufactured by Riken Technos Co., Ltd.) was used as the polypropylene raw material layer (base sheet 2).
Next, a printed layer (printed layer 3) with a wood grain pattern was formed on this polypropylene base layer using gravure printing with urethane ink (Laminar, manufactured by Toyo Ink Mfg. Co., Ltd.).
Next, a polypropylene clear layer (transparent thermoplastic resin layer 4) made of homopolypropylene resin (manufactured by Prime Polymer Co., Ltd.) was formed on this printed layer using an extruder, and at the same time as the extrusion, embossed portions (recesses 5 and recesses 6) were formed using an embossing plate.
Finally, as a topcoat layer (topcoat layer 7), a UV-curable resin (urethane acrylate resin manufactured by DIC Graphic Co., Ltd.) was applied to a thickness of 10 μm, and the coating liquid was cured by UV irradiation with a metal halide lamp. In this way, the topcoat layer was formed.
また、木目柄領域以外の領域（透明熱可塑性樹脂層４の、印刷層３の木目柄が印刷されていない領域と平面視で重なる領域である非絵柄領域Ａ）には、平面視で正方形状の凸部をランダムに配置した。また、その凸部の外径を２５μｍ以上６０μｍ以下の範囲内とした。また、その凸部を１ｍｍ２当り１００個形成した。
また、木目柄領域（透明熱可塑性樹脂層４の、印刷層３の絵柄が印刷された領域と平面視で重なる領域である絵柄領域Ｂ）には、平面視で十字形状の凹部を規則的に配置した。
また、木目柄領域の周囲には傾斜部（傾斜凸部５ｃ）を設けた。傾斜部（傾斜凸部５ｃ）の傾斜面は、絵柄領域Ｂの周囲から１μｍ離れるごとに、高さが０．２５μｍ低くなるように傾斜している。
なお、エンボス版の深度（凸部の高さ及び凹部の深さ）は、５０μｍとした。
こうして、実施例１の防滑床用化粧シート（防滑床用化粧シート１）を形成した。
Furthermore, in areas other than the wood grain pattern area (non-pattern area A, which is the area of the transparent thermoplastic resin layer 4 that overlaps in a plan view with the area of the printed layer 3 where the wood grain pattern is not printed), square-shaped protrusions were randomly arranged in a plan view. The outer diameter of these protrusions was set to be within the range of 25 μm to 60 μm. In addition, 100 of these protrusions were formed per 1 mm² .
Furthermore, in the wood grain pattern area (the pattern area B, which is the area of the transparent thermoplastic resin layer 4 that overlaps with the printed area of the printed layer 3 in a plan view), cross-shaped recesses are regularly arranged in a plan view.
In addition, inclined sections (inclined protrusions 5c) are provided around the wood grain pattern area. The inclined surface of the inclined section (inclined protrusions 5c) is inclined such that its height decreases by 0.25 μm for every 1 μm distance from the periphery of the pattern area B.
The depth of the embossed plate (height of the raised areas and depth of the recessed areas) was set to 50 μm.
Thus, the anti-slip decorative sheet for floors (anti-slip decorative sheet 1) of Example 1 was formed.
（実施例２）
木目柄領域に、平面視で四角形状の凸部を規則的に配置した以外は、実施例１と同じにして、実施例２の防滑床用化粧シートを形成した。
（実施例３）
木目柄領域に、平面視で三角形状の凹部を規則的に配置した以外は、実施例１と同じにして、実施例３の防滑床用化粧シートを形成した。
（実施例４）
木目柄領域に、平面視で丸形状の凸部を規則的に配置した以外は、実施例１と同じにして、実施例４の防滑床用化粧シートを形成した。
（実施例５）
エンボス深度を７０μｍとした以外は、実施例１と同じにして、実施例５の防滑床用化粧シートを形成した。
(Example 2)
The anti-slip decorative sheet for floors of Example 2 was formed in the same manner as in Example 1, except that square-shaped protrusions were regularly arranged in the wood grain pattern area when viewed from above.
(Example 3)
The anti-slip decorative sheet for floors of Example 3 was formed in the same manner as in Example 1, except that triangular recesses were regularly arranged in the wood grain pattern area when viewed from above.
(Example 4)
Except for regularly arranging circular protrusions in a plan view within the wood grain pattern area, the same procedure as in Example 1 was followed to form the anti-slip floor decorative sheet of Example 4.
(Example 5)
Except for setting the embossing depth to 70 μm, the same procedure as in Example 1 was used to form the anti-slip decorative sheet for floors of Example 5.
（実施例６）
エンボス深度を３０μｍとした以外は、実施例１と同じにして、実施例６の防滑床用化粧シートを形成した。
（実施例７）
木目柄領域の周囲に、傾斜部を設けなかった以外は、実施例１と同じにして、実施例７の防滑床用化粧シートを形成した。
（実施例８）
非絵柄領域Ａに、凸部を１ｍｍ２当り７０個形成した以外は、実施例１と同じにして、実施例８の防滑床用化粧シートを形成した。
（実施例９）
非絵柄領域Ａに、凸部を１ｍｍ２当り１６０個形成した以外は、実施例１と同じにして、実施例９の防滑床用化粧シートを形成した。
(Example 6)
Except for setting the embossing depth to 30 μm, the same procedure as in Example 1 was used to form the anti-slip decorative sheet for floors of Example 6.
(Example 7)
Except for not providing a sloping section around the wood grain pattern area, the anti-slip decorative sheet for flooring of Example 7 was formed in the same manner as in Example 1.
(Example 8)
Except for forming 70 protrusions per 1 mm² in the non-patterned area A, the same procedure as in Example 1 was followed to form the anti-slip floor decorative sheet of Example 8.
(Example 9)
Except for forming 160 protrusions per 1 mm² in the non-patterned area A, the same procedure as in Example 1 was followed to form the anti-slip floor decorative sheet of Example 9.
（実施例１０）
傾斜部（傾斜凸部５ｃ）の傾斜面は、絵柄領域Ｂの周囲から１μｍ離れるごとに、高さが０．１０μｍ低くなるように傾斜している以外は、実施例１と同じにして、実施例１０の防滑床用化粧シートを形成した。
（実施例１１）
傾斜部（傾斜凸部５ｃ）の傾斜面は、絵柄領域Ｂの周囲から１μｍ離れるごとに、高さが１０μｍ低くなるように傾斜している以外は、実施例１と同じにして、実施例１１の防滑床用化粧シートを形成した。
(Example 10)
The inclined surface of the inclined portion (inclined protrusion 5c) is inclined such that its height decreases by 0.10 μm for every 1 μm distance from the periphery of the pattern area B, otherwise the same configuration as in Example 1 was used to form the anti-slip floor decorative sheet of Example 10.
(Example 11)
The inclined surface of the inclined portion (inclined protrusion 5c) is inclined such that its height decreases by 10 μm for every 1 μm distance from the periphery of the pattern area B, otherwise the same configuration as in Example 1 was used to form the anti-slip floor decorative sheet of Example 11.
（比較例１）
木目柄のエンボス版で木目柄領域のみを形成し、木目柄領域以外の領域には、凸部または凹部をランダムに配置しなかった以外は、実施例１と同じにして、比較例１の防滑床用化粧シートを形成した。
（比較例２）
規則的に配置された凸部または凹部を備える木目柄領域を形成せず、不規則に配置された凸部のみを形成した以外は、実施例１と同じにして、比較例２の防滑床用化粧シートを形成した。
(Comparative Example 1)
Comparative Example 1 was formed by creating a decorative anti-slip floor sheet in the same manner as in Example 1, except that only the wood grain pattern area was formed using an embossed wood grain plate, and no protrusions or recesses were randomly placed in the areas outside the wood grain pattern area.
(Comparative Example 2)
The anti-slip decorative sheet for floors of Comparative Example 2 was formed in the same manner as in Example 1, except that a wood grain pattern area with regularly arranged protrusions or recesses was not formed, and only irregularly arranged protrusions were formed.
（比較例３）
エンボス深度を７０μｍとした以外は、比較例１と同じにして、比較例３の防滑床用化粧シートを形成した。
（比較例４）
エンボス深度を７０μｍとした以外は、比較例２と同じにして、比較例４の防滑床用化粧シートを形成した。
（比較例５）
エンボス深度を３０μｍとした以外は、比較例１と同じにして、比較例５の防滑床用化粧シートを形成した。
（比較例６）
エンボス深度を３０μｍとした以外は、比較例２と同じにして、比較例６の防滑床用化粧シートを形成した。
(Comparative Example 3)
The anti-slip decorative sheet for floors of Comparative Example 3 was formed using the same method as Comparative Example 1, except that the embossing depth was set to 70 μm.
(Comparative Example 4)
The anti-slip decorative sheet for floors of Comparative Example 4 was formed using the same method as Comparative Example 2, except that the embossing depth was set to 70 μm.
(Comparative Example 5)
The anti-slip decorative sheet for floors of Comparative Example 5 was formed using the same method as Comparative Example 1, except that the embossing depth was set to 30 μm.
(Comparative Example 6)
The anti-slip decorative sheet for floors of Comparative Example 6 was formed using the same method as Comparative Example 2, except that the embossing depth was set to 30 μm.
＜評価方法および評価基準＞
実施例および比較例の各防滑床用化粧シートを床用基材（床用基材１１）である厚み３ｍｍのＭＤＦ（広葉樹）の表面に接着剤として２液水性エマルジョン接着剤（中央理化工業（株）製「リカボンド」（重量比ＢＡ－１０Ｌ／ＢＡ－１１Ｂ＝１００：２．５））をウェット状態で１００ｇ／ｍ２に塗工した後に貼り合わせ、２４時間養生することで床用化粧材（防滑床用化粧材１０）とした。
本実施例では、これらの床用化粧材を以下の方法により評価した。
<Evaluation Methods and Criteria>
Each of the anti-slip floor decorative sheets in the examples and comparative examples was bonded to the surface of a 3 mm thick MDF (hardwood) floor base material (floor base material 11) after applying a two-component aqueous emulsion adhesive ("Ricabond" manufactured by Chuo Rika Kogyo Co., Ltd. (weight ratio BA-10L/BA-11B = 100:2.5)) at a rate of 100 g/ m² in a wet state, and then cured for 24 hours to obtain a floor decorative material (anti-slip floor decorative material 10).
In this embodiment, these floor covering materials were evaluated by the following method.
（１）意匠性評価
意匠性評価は、木目柄が形成されているか、および木目柄が際立って見えるかを目視にて確認した。
木目柄が形成されている場合を「〇」（合格）と評価し、木目柄が形成されていない場合を「×」（不合格）と評価した。
また、木目柄が形成されていて、さらに際立ってみえる場合を「◎」（合格）と評価した。
(1) Evaluation of design aesthetics The evaluation of design aesthetics involved visually confirming whether a wood grain pattern was formed and whether the wood grain pattern was clearly visible.
If a wood grain pattern was formed, it was evaluated as "○" (pass), and if a wood grain pattern was not formed, it was evaluated as "×" (fail).
Furthermore, cases where a wood grain pattern was formed and stood out were rated as "◎" (pass).
（２）汚染性評価
汚染性評価は、ＪＡＳ汚染Ａ試験に準拠した試験を行い、評価した。
目視にて著しい着色のない場合を「〇」（合格）と評価し、肉眼（目視）では確認が難しいがルーペでの着色残りがある場合を「△」（合格）と評価し、目視にて着色残りがある場合を「×」（不合格）と評価した。
(2) Contamination assessment The contamination assessment was conducted using tests in accordance with the JAS contamination A test.
If there was no significant discoloration visible to the naked eye, it was evaluated as "○" (pass). If there was some remaining discoloration that was difficult to confirm with the naked eye but could be seen with a magnifying glass, it was evaluated as "△" (pass). If there was any remaining discoloration visible to the naked eye, it was evaluated as "×" (fail).
（３）防滑性能評価
防滑性能評価は、ＪＩＳ－Ａ１４５４に準じて試験を行い、Ｃ．Ｓ．Ｒ．値を求めた。
評価基準は、Ｃ．Ｓ．Ｒ値が０．３６以上を「〇」（合格）と評価し、０．３５以下を「×」（不合格）と評価した。
(3) Anti-slip performance evaluation The anti-slip performance was evaluated by testing in accordance with JIS-A1454 and the C.S.R. value was determined.
The evaluation criteria were as follows: a C.S.R. score of 0.36 or higher was evaluated as "○" (pass), and a score of 0.35 or lower was evaluated as "×" (fail).
（４）足触り感評価
足触り感（ほど良い滑りづらさ）は、官能試験にて評価した。
評価は１６人の試験員で行った。
評価基準は、「足触り感が良い（ほど良い滑りづらさがある）」と感じた人が０～３人の場合を「×」（不合格）と評価し、４～８人の場合を「△」（合格）と評価し、９～１６人の場合を「○」（合格）と評価した。
(4) Evaluation of feel underfoot The feel underfoot (appropriate level of slip resistance) was evaluated through sensory testing.
The evaluation was conducted by 16 examiners.
The evaluation criteria were as follows: if 0 to 3 people felt that the surface had a "good feel underfoot (just the right amount of slip resistance)," it was rated as "×"(fail); if 4 to 8 people felt this way, it was rated as "△"(pass); and if 9 to 16 people felt this way, it was rated as "○" (pass).
（５）判定
上述した各評価結果を総合的に評価し、総合評価が「〇」、「△」の場合を合格とし、総合評価が「×」の場合を不合格とした。
評価結果を表１に示す。
(5) Judgment The evaluation results described above were comprehensively assessed, and a comprehensive evaluation of "○" or "△" was considered a pass, while a comprehensive evaluation of "×" was considered a fail.
The evaluation results are shown in Table 1.
表１の結果から、実施例１～１１の防滑床用化粧シート及びそれを用いた床用化粧材は、防滑性能を損じることなく意匠性を高めることができる、ということを検証することができた。 From the results in Table 1, it was confirmed that the anti-slip decorative sheets for floors of Examples 1 to 11 and the decorative floor materials using them can enhance the design without compromising anti-slip performance.
＜その他の実施形態＞
本発明は、以上に記載した実施形態とその変形例、実施例に限定されるものではない。当業者の知識に基づいて実施形態とその変形例、実施例に設計の変更等を加えることが可能であり、そのような変更等を加えた態様も本発明の技術的範囲に含まれる。
<Other Embodiments>
The present invention is not limited to the embodiments, modifications, and examples described above. Based on the knowledge of those skilled in the art, design changes and other modifications can be made to the embodiments, modifications, and examples, and such modified embodiments are also included within the technical scope of the present invention.
また、例えば、本発明は以下のような構成を取ることができる。
（１）
基材シートと、
前記基材シート上に形成された印刷層と、
前記印刷層上に形成された樹脂層と、を備え、
前記樹脂層に凸部及び凹部の少なくとも一方が形成されており、
前記樹脂層の、前記印刷層の絵柄が印刷された領域と平面視で重なる領域には、規則的に配置された前記凸部及び前記凹部の少なくとも一方が形成されており、
前記樹脂層の、前記印刷層の絵柄が印刷されていない領域と平面視で重なる領域には、ランダムに配置された前記凸部及び前記凹部の少なくとも一方が形成されていることを特徴とする防滑床用化粧シート。
（２）
ランダムに配置された前記凸部の外径または前記凹部の外径は、２５μｍ以上６０μｍ以下の範囲内であることを特徴とする上記（１）に記載の防滑床用化粧シート。
（３）
ランダムに配置された前記凸部または前記凹部は、１ｍｍ２当り７０個以上１６０個以下の範囲内で形成されていることを特徴とする上記（１）または（２）に記載の防滑床用化粧シート。
（４）
前記樹脂層の、前記印刷層の絵柄が印刷されていない領域と平面視で重なる領域には、乱数計算によって算出された情報を基に前記凸部及び前記凹部の少なくとも一方がランダムに配置されていることを特徴とする上記（１）から（３）のいずれか１項に記載の防滑床用化粧シート。
（５）
規則的に配置された前記凸部または前記凹部は、その形状が、十字形状、四角形状、三角形状、及び丸形状のいずれか１つであることを特徴とする上記（１）から（４）のいずれか１項に記載の防滑床用化粧シート。
（６）
前記樹脂層の、前記印刷層の絵柄が印刷された領域と平面視で重なる領域の周囲の少なくとも一部には、前記印刷層の絵柄が印刷された領域と平面視で重なる領域から離れるにしたがって、高さが低くなるように傾斜した傾斜面を備えた傾斜凸部、及び深さが浅くなるように傾斜した傾斜面を備えた傾斜凹部の少なくとも一方が形成されていることを特徴とする上記（１）から（５）のいずれか１項に記載の防滑床用化粧シート。
（７）
前記傾斜面は、前記樹脂層の、前記印刷層の絵柄が印刷された領域と平面視で重なる領域の周囲から１μｍ離れるごとに、高さが０．１０μｍ以上１０μｍ以下の範囲内で低くなるように、または高くなるように傾斜していることを特徴とする上記（６）に記載の防滑床用化粧シート。
（８）
上記（１）から（７）のいずれか１項に記載の防滑床用化粧シートを床用基材に貼り合わせた防滑床用化粧材。
Furthermore, for example, the present invention can take the following configuration.
(1)
Base sheet and
A printed layer formed on the base sheet,
The printed layer comprises a resin layer formed on the printed layer,
At least one of a convex portion and a concave portion is formed in the resin layer.
In the region of the resin layer that overlaps with the region on which the pattern of the printed layer is printed in a plan view, at least one of the regularly arranged protrusions and recesses is formed.
A decorative sheet for anti-slip floors, characterized in that at least one of the randomly arranged protrusions and recesses is formed in the area of the resin layer that overlaps in a plan view with the area of the printed layer where the pattern is not printed.
(2)
The anti-slip decorative sheet for floors according to (1) above, characterized in that the outer diameter of the randomly arranged protrusions or the outer diameter of the recesses is within the range of 25 μm to 60 μm.
(3)
The anti-slip decorative sheet for floors according to (1) or (2) above, characterized in that the randomly arranged protrusions or recesses are formed in a range of 70 to 160 per 1 mm².
(4)
The anti-slip decorative sheet for floors according to any one of (1) to (3) above, characterized in that in the region of the resin layer that overlaps in a plan view with the region where the pattern of the printed layer is not printed, at least one of the convex portion and the concave portion is randomly arranged based on information calculated by random number calculation.
(5)
The anti-slip decorative sheet for floors according to any one of the above (1) to (4), characterized in that the regularly arranged protrusions or recesses have one of the shapes of a cross shape, a square shape, a triangular shape, and a round shape.
(6)
The decorative sheet for anti-slip flooring according to any one of (1) to (5) above, characterized in that at least a portion of the resin layer around the area in which the pattern of the printed layer is printed in a plan view is formed, wherein at least one of an inclined convex portion having an inclined surface that decreases in height as it moves away from the area in which the pattern of the printed layer is printed in a plan view, and an inclined recess having an inclined surface that decreases in depth.
(7)
The decorative anti-slip floor sheet according to (6) above, characterized in that the inclined surface is inclined such that the height decreases or increases by a range of 0.10 μm to 10 μm for every 1 μm distance from the periphery of the area of the resin layer that overlaps with the area on which the pattern of the printed layer is printed in a plan view.
(8)
A decorative anti-slip flooring material obtained by laminating an anti-slip flooring decorative sheet described in any one of the above items (1) to (7) onto a flooring base material.
１ 防滑床用化粧シート（床用化粧シートの一例）
２ 基材シート
３ 印刷層
４ 透明熱可塑性樹脂層（樹脂層）
５ 凸部
５ａ 凸部（非絵柄領域Ａに形成された凸部）
５ｂ 凸部（絵柄領域Ｂに形成された凸部）
５ｃ 傾斜凸部
６ 凹部
７ トップコート層
１０ 防滑床用化粧材
１１ 床用基材
Ａ 非絵柄領域（絵柄領域以外の領域）
Ｂ 絵柄領域
1. Anti-slip decorative flooring sheets (an example of decorative flooring sheets)
2. Base sheet 3. Printed layer 4. Transparent thermoplastic resin layer (resin layer)
5. Protrusion 5a: Protrusion (a protrusion formed in the non-pattern area A)
5b. Protrusion (a protrusion formed in the pattern area B)
5c Inclined protrusion 6 Recess 7 Top coat layer 10 Anti-slip flooring material 11 Flooring base material A Non-patterned area (area other than the patterned area)
B. Image area
Claims (8)
前記基材シート上に形成された印刷層と、
前記印刷層上に形成された樹脂層と、を備え、
前記樹脂層に凸部及び凹部の少なくとも一方が形成されており、
前記樹脂層の、前記印刷層の絵柄が印刷された領域と平面視で重なる領域には、規則的に配置された前記凸部及び前記凹部の少なくとも一方が形成されており、
前記樹脂層の、前記印刷層の絵柄が印刷されていない領域と平面視で重なる領域には、ランダムに配置された前記凸部及び前記凹部の少なくとも一方が形成されていることを特徴とする防滑床用化粧シート。 A base sheet and
A printed layer formed on the base sheet,
The printed layer comprises a resin layer formed on the printed layer,
At least one of a convex portion and a concave portion is formed in the resin layer.
In the region of the resin layer that overlaps with the region on which the pattern of the printed layer is printed in a plan view, at least one of the regularly arranged protrusions and recesses is formed.
A decorative sheet for anti-slip floors, characterized in that at least one of the randomly arranged protrusions and recesses is formed in the area of the resin layer that overlaps in a plan view with the area of the printed layer where the pattern is not printed.