JPS602194B2 - decorative board - Google Patents
decorative boardInfo
- Publication number
- JPS602194B2 JPS602194B2 JP5459880A JP5459880A JPS602194B2 JP S602194 B2 JPS602194 B2 JP S602194B2 JP 5459880 A JP5459880 A JP 5459880A JP 5459880 A JP5459880 A JP 5459880A JP S602194 B2 JPS602194 B2 JP S602194B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- decorative board
- coating film
- clear
- board according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
この発明は、建築材料などとして好適な高級化粧板に関
する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a high-grade decorative board suitable as a building material.
従釆の化粧板は、基村の表面に印刷したプラスチックフ
ィルムを貼着するか、着色が容易なプラスチックを基村
の表面に塗着するものであり、図柄が表面に浮き上って
強調され過ぎ、深みのある高級感が出ないきらいがあっ
た。For the decorative board of the retainer, a printed plastic film is attached to the surface of the base plate, or a plastic that can be easily colored is applied to the surface of the base plate, so that the design stands out on the surface and is emphasized. It was too much and I didn't feel like it gave off a deep, luxurious feel.
この発明は、かかる事実に着目して、基本的には自動車
塗装などで知られているメタリック塗装法を応用し、そ
れに独特専用の工夫を凝らして高級化した化粧板を提供
しようとするものであり、この発明によれば化粧板の表
面は深みのあるデラックスなメタリック感を与えるもの
となる。Focusing on this fact, this invention basically applies the metallic coating method known for automobile coating, etc., and attempts to provide a high-quality decorative board by adding unique and exclusive innovations to it. According to this invention, the surface of the decorative board has a deep, deluxe metallic feel.
以下、その詳細を図面に基づき説明する。第１発明
第１発明は第１の発明の実施例を示しており、図におい
て１はベニヤ板や合成樹脂版などからなる板材である。The details will be explained below based on the drawings. First invention The first invention shows an embodiment of the first invention, and in the figure, numeral 1 is a plate material such as a plywood board or a synthetic resin plate.
板材１の表面には、適当に下地調整してプラィマ−を塗
布し、そのプラィマ−塗膜２が乾燥したのち、使用原色
と同系色のサーフェーサ−をプラィマー塗膜２の表面に
塗布する。３がそのサーフェーサ−塗膜を示しており、
この両塗膜２，３で下塗り塗膜４が構成されている。A primer is coated on the surface of the board material 1 after suitably preparing the base, and after the primer coat 2 is dried, a surfacer of a color similar to the primary color used is coated on the surface of the primer coat 2. 3 shows the surfacer coating film,
These two coatings 2 and 3 constitute an undercoat coating 4.
次にサーフェーサー塗膜３の表面に、着色クリヤーのな
かに不規則形状に微粉砕されたアルミ微粒子を数％混入
分散させたメタリック塗料を塗布し、メタリック塗膜５
を形成し、続いて該塗膜５の表面にクリヤーを塗布する
。６がそのクリヤー塗膜を示しており、このクリヤー塗
膜６が乾燥したのちその表面に適当な図柄をインク印刷
する。Next, on the surface of the surfacer coating film 3, a metallic paint in which a few percent of finely pulverized aluminum particles in irregular shapes are mixed and dispersed in a colored clear is applied.
is formed, and then a clear coat is applied to the surface of the coating film 5. 6 shows the clear coating film, and after this clear coating film 6 dries, a suitable pattern is printed with ink on its surface.
７がその印刷処理層を示している。7 indicates the printing layer.
そして最後に印刷処理層７の表面にクリヤーを上塗りし
てクリヤー塗膜８を形成した断面構造になっている。か
かる断面構造の化粧板によれば、最表面のクリヤー塗膜
８を通して印刷処理層７の図柄が見えるとともに、メタ
リック塗膜５においてはアルミ微粒子が下塗り塗膜４の
表面に沈み、着色クリヤーを通してデラックスなメタリ
ック感が立体感をもって同時に出ることになる。Finally, the surface of the printed layer 7 is overcoated with clear to form a clear coating film 8, resulting in a cross-sectional structure. According to the decorative board having such a cross-sectional structure, the design of the printed layer 7 can be seen through the clear coating film 8 on the outermost surface, and the fine aluminum particles in the metallic coating film 5 sink to the surface of the undercoat coating 4, and the deluxe pattern can be seen through the colored clear coating. This creates a metallic feel with a three-dimensional effect at the same time.
なお、印刷処理層７の図柄はメタリック塗膜５を陰ペイ
しない程に淡く印刷される。また、下塗り塗膜４はプラ
ィマーとサーフェーサーの機能を同時に有する塗料、つ
まりプライマー・サーフェーサーを塗布して一度塗りで
形成してもよい。第２発明
第２図ないし第４図は第２発明の実施例を示しており、
この場合の板材１と下塗り塗膜４とは第１発明における
と同様である。Note that the pattern on the printing layer 7 is printed so lightly that it does not shade the metallic coating film 5. Further, the undercoat film 4 may be formed by applying a paint having the functions of a primer and a surfacer at the same time, that is, a primer/surfacer. Second invention Figures 2 to 4 show embodiments of the second invention,
The plate material 1 and the undercoat film 4 in this case are the same as those in the first invention.
これでは、第２図及び第３図に示す特殊なアルミ微粒子
ａが使用される。In this case, special aluminum fine particles a shown in FIGS. 2 and 3 are used.
このアルミ微粒子ａは矩形の虎平体をなしており、その
外周縁に９００以下の鋭角部を有さず、一角部に丸い切
欠き１０を形成した基本形状になってい、その厚みは６
ｒ〜６０一、一辺の長さは６ム〜３肋程度である。そし
て、その外周側面１１は地金面のままとし、鏡面仕上げ
された上下の両扇平面１２，１２に透明の高い、つまり
反射輝度の良好な熱硬化性合成樹脂系の塗料（例えばア
クリル樹脂）が競付け塗装されたものとなっている。符
号１３がその着色塗膜を示しており、これの膜厚は約０
．１〜３ｒである。具体的にはこのアルミ微粒子ａは、
延辰したアルミシートの鏡面仕上げした両面に前記塗料
を焼付け塗装したのち、型抜き機で全てを同一形状に打
抜き形成して得られる。The aluminum fine particles a are in the form of a rectangular tiger flat body, have a basic shape with no acute angles of 900 or less on the outer periphery, and have a round notch 10 formed in one corner, and have a thickness of 6
The length of one side is about 6 mm to 3 ribs. The outer peripheral side surface 11 is left as a bare metal surface, and the mirror-finished upper and lower fan surfaces 12 are coated with a thermosetting synthetic resin paint (for example, acrylic resin) that is highly transparent, that is, has good reflective brightness. It has been competitively painted. Reference numeral 13 indicates the colored coating film, and the film thickness of this is approximately 0.
．． 1 to 3r. Specifically, this aluminum fine particle a is
The paint is baked onto both mirror-finished surfaces of a stretched aluminum sheet, and then all are punched into the same shape using a die cutter.
かかるアルミ微粒子ａは、２５ご○下でのフオードカッ
プ粘度が２の砂前後で、溶剤の含有量が４の重量％のク
リヤーのなかに混入分散させて、乾燥後のサーフェーサ
ー塗膜３の表面に数回に分け吹付塗布し、アルミ微粒子
ａが混在する中塗り塗膜１５を積層状態に形成した。The aluminum fine particles a are mixed and dispersed in a clear sand having a food cup viscosity of around 2 at 25 degrees Celsius and a solvent content of 4% by weight, and the surface of the surfacer coating film 3 after drying. The intermediate coating film 15 in which the aluminum fine particles a were mixed was formed in a laminated state by spraying it several times.
この吹付塗布に際しては、アルミ微粒子ａの着色塗膜１
３を使用原色つまりサーフェーサー塗膜３と同一色とし
、乾いては塗る作業を繰り返す。そして、この中塗り塗
膜１５の表面にクリヤー塗膜６を塗布形成し、その乾燥
表面に印刷処理層７、クリヤー塗膜８を第１発明と同様
に順次形成して第４図に示す断面構造としたものである
。かかる構造の化粧板は、これの表面に光が当ると、第
１発明のメタリック塗料使用のものに比べてより一層明
るい光沢を有してきらきら輝く深いメタリック感が得ら
れた。それは、アルミ微粒子ａが不規則形状に破砕され
たものと異なり、全てが同一形状で外周緑に９０ｏ以下
の鋭角部を有しないので、中塗り時にクリヤー中の溶剤
の蒸発にともなってアルミ微粒子ａが下塗り塗膜４の表
面に突き立つことなく同じ度合で沈降する。しかもアル
ミ微粒子ａは矩形の馬平体であるから、他の形状などの
ものと異なり、互に絡み合うことがないうえに、切欠き
１０の存在で沈降して行くときに重量バランスが崩れて
平らに倒れやすい。それに、アルミ微粒子ａを混入した
中塗り用クリヤーは２回以上乾いては塗る方式とし、一
回のクリヤー中におけるアルミ微粒子ａの量をそれだけ
少なくできるようにしたので、各層にわけてアルミ微粒
子ａを可及的に均一分散させることができる。これらの
ことが相乗して中塗り塗膜１６内においてアルミ微粒子
ａが層をなして平らに倒れ、かつ均一に分散する結果、
印刷図柄越し‘こ使用原色が明るい光沢を有して暗い夜
空にきらめく星を見るが如き感を呈するのだと考えられ
る。また、最終塗膜の物理的密着性も、間にアルミ微粒
子ａが多層にわたって介在するにもかかわらず、極めて
良好であり、はがれなどの塗装不良を生じなかった。During this spray coating, colored coating film 1 of aluminum fine particles a
3 is the primary color used, that is, the same color as surfacer coating 3, and the process of painting is repeated once it dries. Then, a clear coating film 6 is applied and formed on the surface of this intermediate coating film 15, and a printing treatment layer 7 and a clear coating film 8 are sequentially formed on the dried surface in the same manner as in the first invention. It is a structure. When the surface of the decorative board having such a structure was exposed to light, it had a brighter luster and a sparkling deep metallic feel compared to the one using the metallic paint of the first invention. Unlike fine aluminum particles a that are crushed into irregular shapes, they all have the same shape and do not have acute angles of 90 degrees or less on the outer periphery, so the aluminum fine particles a does not stand out on the surface of the undercoat film 4 and settles to the same degree. Moreover, since the aluminum fine particles a are rectangular bodies, they do not get entangled with each other, unlike particles of other shapes, and due to the presence of the notches 10, when they settle down, the weight balance is disrupted and the particles become flat. It is easy to fall down. In addition, the intermediate coating clear mixed with aluminum fine particles a is applied two or more times after drying, so that the amount of aluminum fine particles a in one clear coat can be reduced accordingly. can be dispersed as uniformly as possible. As a result of these factors working together, the aluminum fine particles a form a layer in the intermediate coating film 16, fall flat, and are uniformly dispersed.
It is thought that the primary colors used in this print have a bright luster that gives the impression of seeing twinkling stars in a dark night sky. Furthermore, the physical adhesion of the final coating film was extremely good despite the presence of multiple layers of aluminum fine particles a, and no coating defects such as peeling occurred.
これは、下塗り塗膜４と中塗り塗膜１５とが各アルミ微
粒子ａの切欠き１０を介して支障なく一体結合するから
であろう。更に、中塗り塗膜１５の乾燥後の表面は、凹
凸のない完全なフラット面に仕上がり、したがってその
塗膜表面に図柄の印刷が有効確実に行なえることも確認
した。This is probably because the undercoat film 4 and the intermediate coat film 15 are integrally bonded to each other through the notches 10 of each fine aluminum particle a without any problem. Furthermore, it was confirmed that the surface of the intermediate coating film 15 after drying was finished as a completely flat surface with no irregularities, and therefore a pattern could be printed effectively and reliably on the surface of the coating film.
つまり、通常のメタＩＪック塗料では、一般に５０％前
後の溶剤が入っているのでこの溶剤の蒸発する分だけ塗
膜がやせることになり、塗布直後の塗膜Ａの表面Ａ′は
第５図の仮想線で示すようにフラットではあっても、乾
燥後の塗膜表面Ａ＾はアルミ微粒子の分散不均一により
同図実線で示すように曲面状になりがちであるが、かか
る不具合が生じなかったのである。その理由としては、
アルミ微粒子ａが均一に分散するうえに中塗り用クリヤ
ー中の溶剤含有量が４血重量％に抑えられており、中塗
り塗膜１５が溶剤の蒸発にともなってやせて行くときに
、クリヤー自体の流動性からくる表面張力作用が有効に
働いて乾燥後の表面が曲面状になるのを抑えているから
だと考えられる。かかる作用・効果を確実に期すために
は中塗り用クリヤー中の溶剤含有量は４の重量％が上限
であり、これより少なければ少ない程よい。また、中塗
り用クリヤー中の溶剤の蒸発時間を長くすればする程、
中塗り塗膜１５の表面をフラット化するのにより有利で
ある。なお、図示せるクリヤー塗膜６は省略して中塗り
塗膜１５の表面に直接印刷処理をしてもよい。In other words, since ordinary Meta IJ paints generally contain around 50% solvent, the paint film thins by the amount of evaporation of this solvent, and the surface A' of the paint film A immediately after application is Even though it is flat as shown by the imaginary line in the figure, the coating surface A^ after drying tends to become curved as shown by the solid line in the figure due to uneven dispersion of the aluminum particles. There wasn't. The reason is that
In addition to uniformly dispersing the aluminum fine particles a, the solvent content in the intermediate coating clear is suppressed to 4% by weight, so that when the intermediate coating film 15 thins as the solvent evaporates, the clearer itself It is thought that this is because the surface tension effect resulting from the fluidity of the powder works effectively and prevents the surface from becoming curved after drying. In order to ensure such effects and effects, the upper limit of the solvent content in the intermediate coating clear is 4% by weight, and the lower the content, the better. Also, the longer the evaporation time of the solvent in the intermediate coat clear, the more
This is more advantageous in flattening the surface of the intermediate coating film 15. Note that the illustrated clear coating film 6 may be omitted and printing may be performed directly on the surface of the intermediate coating film 15.
第３発明第６図及び第７図は第３の発明の実施例を示し
ており、この場合の板材１と下塗り塗膜４とは上記実施
例におけると同様であり、また第２発明におけるアルミ
微粒子ａが同機に使用される。Third invention Figures 6 and 7 show an embodiment of the third invention, in which the plate material 1 and the undercoat film 4 are the same as in the above embodiment, and the aluminum in the second invention. Fine particles a are used in the same machine.
すなわち、下塗り塗膜４の乾燥後の表面に、その着色塗
膜１３がサーフェーサー塗膜３と同一色のアルミ微粒子
ａを、溶剤のみ若し〈は極めて僅かの（０．１重量％以
下）の重合体を含有する組成物に混入分散させて吹付塗
布する。第６図イは塗布直後の塗布膜１６の状態を示し
ており、溶剤が空気中に飛散すると第６図口に示す如く
、アルミ微粒子ａは下塗り塗膜４の表面に仮付けされた
状態となる。アルミ微粒子ａは下塗り塗膜４の表面に突
き立つことなく倒れ、前記重合体で仮付け状態が維持さ
れる。この重合体がなくても溶剤で下塗り塗膜４の表面
が溶けるのでアルミ微粒子ａを仮付けすることはできる
。こうしてアルミ微粒子ａを仮付けしたのち、その外表
面にクリヤー塗膜６、印刷処理層７ついでクリヤー塗膜
８を上記実施例におけると同様に順次形成して第７図に
示す如き断面構造のイｑ乾板を得た。That is, on the surface of the undercoat film 4 after drying, fine aluminum particles a whose colored coating film 13 has the same color as the surfacer coating film 3 are applied only with a solvent or with a very small amount (0.1% by weight or less). It is mixed and dispersed in a composition containing a polymer and applied by spraying. Figure 6A shows the state of the coating film 16 immediately after application, and when the solvent is scattered in the air, the aluminum particles a are temporarily attached to the surface of the undercoat film 4, as shown in the opening of Figure 6. Become. The aluminum fine particles a fall down without standing up on the surface of the undercoat film 4, and are maintained in a temporarily attached state by the polymer. Even without this polymer, the surface of the undercoat film 4 can be dissolved by the solvent, so that the aluminum fine particles a can be temporarily attached. After temporarily attaching the aluminum fine particles a in this way, a clear coating film 6, a printing treatment layer 7, and a clear coating film 8 are sequentially formed on the outer surface in the same manner as in the above embodiment to obtain a cross-sectional structure as shown in FIG. A dry plate was obtained.
この化粧板においても、クリヤー塗膜６，８を通して印
刷処理層７の図柄とアルミ微粒子ａとを見ることになり
、見る者をして夜空に明るくきらめく星を見る如きデラ
ックス感を与えるものとなつた。In this decorative board as well, the design of the printed layer 7 and the fine aluminum particles a can be seen through the clear coatings 6 and 8, giving the viewer a deluxe feeling as if they were looking at bright, twinkling stars in the night sky. Ta.
なお、各発明におけるアルミ微粒子は金属微粒子のひと
つの例であって、これはその他の銅、ステンレス、真鈴
などに代えてもよい。Note that the aluminum fine particles in each invention are one example of metal fine particles, and may be replaced with other materials such as copper, stainless steel, and silver.
また、前記のクリヤー塗腰６，８を形成するクリヤーは
、必ずしも無色透明である必要はなく、透明度の高い着
色クリヤーであってもよい。Further, the clear forming the clear coating thickness 6, 8 does not necessarily have to be colorless and transparent, and may be a highly transparent colored clear.
第１図は第１発明の実施例を示す化粧板断面図である。
第２図ないし第４図は第２発明の実施例を示すものであ
って、第２図は第２発明の構成部材のひとつである金属
微粒子の外観拡大斜視図、第３図はこの金属微粒子の断
面図、第４図は化粧板の断面図である。第５図は第２発
明の作用効果を確認するために挙げた説明図である。第
６図イ・口及び第７図は第３発明の実施例を示すもので
あって、第６図イ及び口は金属微粒子が下塗り塗際に付
着される状態を示すそれぞれ断面図、第７図は化粧板の
断面図である。１・・・板材、２・・・プライマー塗膜
、３・・・サーフェーサー塗腰、４・・・下塗り塗膜、
５・・・メタリック塗膜、６，８・・・クリヤー塗膜、
７・・・印刷処理層、ａ・・・金属微粒子、１０・・・
金属微粒子の切欠き、１１・・・金属微粒子の外周側面
、１２・・・金属微粒子の扇平面、１３・・・着色塗膜
、１５・・・中塗り塗腰。
第１図第２図
第３図
第４図
第５図
第６図
第７図FIG. 1 is a sectional view of a decorative board showing an embodiment of the first invention. 2 to 4 show examples of the second invention, in which FIG. 2 is an enlarged perspective view of the external appearance of fine metal particles, which is one of the constituent members of the second invention, and FIG. 3 is an enlarged perspective view of the fine metal particles. FIG. 4 is a cross-sectional view of the decorative board. FIG. 5 is an explanatory diagram taken to confirm the effects of the second invention. 6A and 7 show an embodiment of the third invention, and FIGS. The figure is a cross-sectional view of the decorative board. 1... Board material, 2... Primer coating film, 3... Surfacer coating strength, 4... Undercoat coating film,
5...Metallic coating film, 6,8...Clear coating film,
7...Printing layer, a...Metal fine particles, 10...
Notch in metal fine particles, 11... Outer peripheral side surface of metal fine particles, 12... Fan plane of metal fine particles, 13... Colored coating film, 15... Intermediate coating strength. Figure 1 Figure 2 Figure 3 Figure 4 Figure 5 Figure 6 Figure 7
Claims (1)
塗り塗膜４の表面に、着色クリヤーのなかに金属微粒子
を混入分散させたメタリツク塗料の塗膜５を形成し、こ
のメタリツク塗膜５の表面に所定の図柄を印刷処理し、
その印刷処理層７の表面にクリヤーの塗膜８を塗布形成
したことを特徴とする化粧板。 ２ 板材１がベニヤ板である特許請求の範囲第１項記載
の化粧板。 ３ 板材１が合成樹脂板である特許請求の範囲第１項記
載の化粧板。 ４ 下塗り塗膜４が、板材１の表面に塗布形成されるプ
ライマーの塗膜２と、このプライマー塗膜２の表面に塗
布形成されるサーフエーサーの塗膜３とからなる特許請
求の範囲第１項記載の化粧板。 ５ 下塗り塗膜４が、プライマーとサーフエーサーの機
能を同時にもつプライマー・サーフエーサーの塗膜であ
る特許請求の範囲第１項記載の化粧板。 ６ 金属微粒子が、不規則形状に微粉砕されたアルミ微
粒子である特許請求の範囲第１項記載の化粧板。 ７ メタリツク塗膜５の表面にクリヤーの塗膜６を塗布
形成したのち、このクリヤー塗膜６の表面に所定の図柄
を印刷処理するものとした特許請求の範囲第１項記載の
化粧板。 ８ 板材１の表面に下塗り塗膜４を塗布形成し、この下
塗り塗膜４の表面に、外周側面１１を除く両扁平面１２
，１２に下塗り塗膜４と同系色の透明度の高い着色塗膜
１３が塗布形成された金属微粒子ａをクリヤーのなかに
混入分散させたものを塗布して中塗り塗膜１５を形成し
、この中塗り塗膜１５の表面に所定の図柄を印刷処理し
、その印刷処理層７の表面にクリヤーの塗膜８を塗布形
成したことを特徴とする化粧板。 ９ 板材１がベニヤ板である特許請求の範囲第８項記載
の化粧板。 １０ 板材１が合成樹脂板である特許請求の範囲第８項
記載の化粧板。 １１ 下塗り塗膜４が、板材１の表面に塗布形成される
プライマーの塗膜２と、このプライマー塗膜２の表面に
塗布形成されるサーフエーサーの塗膜３とからなり、こ
のサーフエーサー塗膜３と金属微粒子ａの着色塗膜１３
とが同系色である特許請求の範囲第８項記載の化粧板。 １２ 下塗り塗膜４が、プライマーとサーフエーサーの
機能を同時にもつプライマー・サーフエーサーの塗膜で
ある特許請求の範囲第８項記載の化粧板。１３ 金属微
粒子ａが、延伸アルミシートの両扁平面に熱硬化性合成
樹脂系塗料を焼付け塗装したのち、型抜き機で同一形状
に型抜き形成されたアルミ微粒子である特許請求の範囲
第８項記載の化粧板。 １４ アルミ微粒子が、その外周縁に９０°以下の鋭角
部を有さず、一角部に丸い切欠き１０を形成したものと
なっている特許請求の範囲第１３項記載の化粧板。 １５ 中塗り塗膜１５は、金属微粒子ａをクリヤーのな
かに混入分散させたものを数次にわたって乾いては塗布
する工程を繰り返して積層状態に形成されたものである
特許請求の範囲第８項記載の化粧板。 １６ 中塗り塗膜１５のクリヤーは、２５℃下でのフオ
ードカツプ粘度が１０〜３０秒で、溶剤の含有量が４０
重量％以下のものである特許請求の範囲第８項又は第１
５項記載の化粧板。 １７ 中塗り塗膜１５の表面にクリヤーの塗膜６を塗布
形成したのち、このクリヤー塗膜６の表面に所定の図柄
を印刷処理するものとした特許請求の範囲第８項記載の
化粧板。 １８ 塗膜６，８のクリヤーが、透明度の高い着色クリ
ヤーである特許請求の範囲第１７項記載の化粧板。 １９ 板材１の表面に下塗り塗膜４を塗布形成し、この
下塗り塗膜４の表面に、外周側面１１を除く両扁平面１
２，１２に下塗り塗膜４と同系色の透明度の高い着色塗
膜１３が塗布形成された金属微粒子ａを溶剤中に混入分
散させて吹付けこの金属微粒子ａの表面にクリヤーの塗
膜６を塗布形成し、このクリヤー塗膜６の表面に所定の
図柄を印刷処理し、この印刷処理層７の表面にクリヤー
の塗膜８を塗布形成したことを特徴とする化粧板。 ２０ 板材１がベニヤ板である特許請求の範囲第１９項
記載の化粧板。 ２１ 板材１が合成樹脂板である特許請求の範囲第１９
項記載の化粧板。 ２２ 下塗り塗膜４が、板材１の表面に塗布形成される
プライマーの塗膜と、このプライマー塗膜の表面に塗布
形成されるサーフエーサーの塗膜とからなり、このサー
フエーサー塗膜と金属微粒子ａの着色塗膜１３とが同系
色である特許請求の範囲第１９項記載の化粧板。 ２３ 下塗り塗膜４が、プライマーとサーフエーサーの
機能を同時にもつプライマー・サーフエーサーの塗膜で
ある特許請求の範囲第１９項記載のイ化粧板。 ２４ 金属微粒子ａが、延伸アルミシートの両扁平面に
熱硬化性合性樹脂系塗料を焼付け塗装したのち、型抜き
機で同一形状に型抜き形成されたアルミ微粒子である特
許請求の範囲第１９項記載の化粧板。 ２５ アルミ微粒子が、その外周縁に９０°以下の鋭角
部を有さず、一角部に丸い切欠き１０を形成したものと
なっている特許請求の範囲第２４項記載の化粧板。 ２６ 金属微粒子ａを溶剤と０．１重量％以下の重合体
とからなる組成物に混入分散させて下塗り塗膜４に吹付
けるようにした特許請求の範囲第１９項記載の化粧板。 ２７ 塗膜６，８のクリヤーが、透明度の高い着色クリ
ヤーである特許請求の範囲第１９項記載の化粧板。[Claims] 1. An undercoat film 4 is applied and formed on the surface of the board material 1, and a paint film 5 of metallic paint in which fine metal particles are mixed and dispersed in a colored clear is formed on the surface of this undercoat film 4. Then, a predetermined pattern is printed on the surface of this metallic coating film 5,
A decorative board characterized in that a clear coating film 8 is coated on the surface of the printed layer 7. 2. The decorative board according to claim 1, wherein the board material 1 is a plywood board. 3. The decorative board according to claim 1, wherein the board material 1 is a synthetic resin board. 4. Claim 1, in which the undercoat film 4 comprises a primer film 2 coated and formed on the surface of the board material 1, and a surfacer coat 3 coated and formed on the surface of the primer coat 2. Decorative board as described in section. 5. The decorative board according to claim 1, wherein the undercoat film 4 is a primer-surfacer film having both the functions of a primer and a surfer. 6. The decorative board according to claim 1, wherein the metal fine particles are aluminum fine particles pulverized into irregular shapes. 7. The decorative board according to claim 1, wherein a clear coating film 6 is applied and formed on the surface of the metallic coating film 5, and then a predetermined pattern is printed on the surface of the clear coating film 6. 8 An undercoat film 4 is applied and formed on the surface of the plate material 1, and both flat surfaces 12 excluding the outer peripheral side surface 11 are formed on the surface of this undercoat film 4.
, 12 is coated with a highly transparent colored coating film 13 of a similar color to the undercoat coating film 4. Metal fine particles a mixed and dispersed in clear are coated to form an intermediate coating film 15. A decorative board characterized in that a predetermined pattern is printed on the surface of an intermediate coating film 15, and a clear coating film 8 is coated on the surface of the printed layer 7. 9. The decorative board according to claim 8, wherein the board material 1 is a plywood board. 10. The decorative board according to claim 8, wherein the board material 1 is a synthetic resin board. 11 The undercoat film 4 consists of a primer film 2 applied and formed on the surface of the board material 1, and a Surf Acer paint film 3 applied and formed on the surface of this primer paint film 2, and this Surf Acer paint film 3 and colored coating film 13 of metal fine particles a
9. The decorative board according to claim 8, wherein and are of similar colors. 12. The decorative board according to claim 8, wherein the undercoat film 4 is a primer/surfacer film having both the functions of a primer and a surfer. 13. Claim 8, wherein the metal fine particles a are aluminum fine particles that are formed by baking a thermosetting synthetic resin paint on both flat surfaces of a stretched aluminum sheet, and then die-cutting them into the same shape using a die-cutting machine. Decorative board as described. 14. The decorative board according to claim 13, wherein the aluminum fine particles do not have an acute angle of 90° or less on their outer periphery and have a round notch 10 formed at one corner. 15. The intermediate coating film 15 is formed into a layered state by repeating the process of drying and coating several times the fine metal particles (a) mixed and dispersed in a clear material. Decorative board as described. 16 The clear intermediate coating film 15 has a Ford Cup viscosity of 10 to 30 seconds at 25°C and a solvent content of 40
Claim 8 or 1 which is less than % by weight
Decorative board according to item 5. 17. The decorative board according to claim 8, wherein a clear coating film 6 is applied and formed on the surface of the intermediate coating film 15, and then a predetermined pattern is printed on the surface of the clear coating film 6. 18. The decorative board according to claim 17, wherein the clear coating films 6 and 8 are colored clear with high transparency. 19 Coating and forming an undercoat film 4 on the surface of the plate material 1, and forming both flat surfaces 1 on the surface of this undercoat film 4 excluding the outer peripheral side surface 11.
2 and 12 are coated with a highly transparent colored coating film 13 of a similar color to the undercoat coating film 4. The formed metal fine particles a are mixed and dispersed in a solvent and sprayed to form a clear coating film 6 on the surface of the metal fine particles a. A decorative board characterized by coating and forming a clear coating film 6, printing a predetermined pattern on the surface of this clear coating layer 6, and coating and forming a clear coating film 8 on the surface of this printed layer 7. 20. The decorative board according to claim 19, wherein the board material 1 is a plywood board. 21 Claim 19, in which the plate material 1 is a synthetic resin plate
Decorative board as described in section. 22 The undercoat film 4 consists of a primer film applied and formed on the surface of the plate material 1, and a Surf Acer paint film applied and formed on the surface of this primer paint film, and this Surf Acer paint film and metal fine particles The decorative board according to claim 19, wherein the colored coating film 13 of a has a similar color. 23. The decorative board according to claim 19, wherein the undercoat film 4 is a primer/surfacer film that has the functions of a primer and a surfer at the same time. 24. Claim 19, wherein the metal fine particles a are aluminum fine particles formed by baking and painting a thermosetting synthetic resin paint on both flat surfaces of a stretched aluminum sheet, and then die-cutting them into the same shape using a die-cutting machine. Decorative board as described in section. 25. The decorative board according to claim 24, wherein the aluminum fine particles have no acute angle of 90° or less on their outer periphery and have a round notch 10 formed at one corner. 26. The decorative board according to claim 19, wherein the fine metal particles a are mixed and dispersed in a composition consisting of a solvent and 0.1% by weight or less of a polymer and sprayed onto the undercoat film 4. 27. The decorative board according to claim 19, wherein the clear coating films 6 and 8 are colored clear with high transparency.