JPH028577B2 - - Google Patents
Info
- Publication number
- JPH028577B2 JPH028577B2 JP60007270A JP727085A JPH028577B2 JP H028577 B2 JPH028577 B2 JP H028577B2 JP 60007270 A JP60007270 A JP 60007270A JP 727085 A JP727085 A JP 727085A JP H028577 B2 JPH028577 B2 JP H028577B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- polyvinyl alcohol
- alcohol resin
- aqueous solution
- nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、ポリエステル化粧板を製造する際に
用いる賦型フイルムの製造方法に関するものであ
る。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to a method for producing a shaped film used in producing a polyester decorative board.
（従来の技術）
ポリビニルアルコール樹脂はポリエステル樹脂
に対する耐性に優れ、ビニロンフイルムとしてポ
リエステル化粧板の製造用に従来より数多く使用
されている。(Prior Art) Polyvinyl alcohol resin has excellent resistance to polyester resin, and has been widely used as vinylon film for manufacturing polyester decorative laminates.
又、ビニロンフイルムの表面に凹凸を設け、表
面に凹凸模様を有するポリエステル化粧板を製造
する方法も行なわれている。この方法に使用する
ビニロンフイルムの表面に凹凸を設けるには、ビ
ニロンフイルムを型押しして凹凸状にする、ビニ
ロンフイルムの表面に樹脂を模様状に盛り上げ
る、凹凸原稿にポリビニルアルコール樹脂を塗工
して成膜化し、剥離する等種々の方法があるが、
凹凸の再現性、天然物の外観の表現等の点から、
原稿に樹脂を塗工する方法が優れている。 There is also a method of producing a polyester decorative board having an uneven pattern on the surface by providing unevenness on the surface of a vinylon film. To create unevenness on the surface of the vinylon film used in this method, the vinylon film is embossed to make it uneven, the resin is raised in a pattern on the surface of the vinylon film, and the uneven original is coated with polyvinyl alcohol resin. There are various methods such as forming a film and peeling it off.
From the viewpoint of reproducibility of unevenness, expression of appearance of natural products, etc.
An excellent method is to coat the manuscript with resin.
しかしながら、ポリビニルアルコール樹脂を塗
工して成膜するには加熱乾燥して水分を除去しな
ければならず、樹脂の塗布量が多ければ乾燥に時
間がかかつて生産性が悪くなつて賦型フイルムが
高価となり、塗布量が少ければ賦型フイルムの強
度が足りなくなり、使用出来なくなつたり、繰り
返し使用が出来なくなる。 However, in order to form a film by coating polyvinyl alcohol resin, it is necessary to heat and dry it to remove moisture, and if the amount of resin applied is large, it takes time to dry, which reduces productivity. is expensive, and if the amount of coating is small, the strength of the imprinted film will be insufficient, making it unusable or unable to be used repeatedly.
（発明が解決しようとする問題点）
本発明は以上のような従来技術の欠点を解消
し、耐久性を有する賦型フイルムを効率よく安価
に製造する方法を提供するものである。(Problems to be Solved by the Invention) The present invention solves the above-mentioned drawbacks of the prior art and provides a method for efficiently producing a durable shaped film at low cost.
（問題点を解決するための手段）
本発明は、賦型フイルムの耐久性を大きくする
ために裏打ちフイルムを用いるものであり、裏打
ちフイルムを重ねた後にポリビニルアルコール樹
脂中の水分を除去できるように、裏打ちフイルム
として透湿度が200ｇ／m2／24hr以上のナイロン
フイルムを用いることを特徴とするものである。(Means for Solving the Problems) The present invention uses a backing film to increase the durability of the imprinted film. , is characterized in that a nylon film having a moisture permeability of 200 g/m 2 /24 hr or more is used as the backing film.
本発明の製造方法は、まず天然木等の原稿の表
面にポリビニルアルコール樹脂の水溶液を塗布
し、その上からナイロンフイルムを重ね合わせて
ラミネートする。 In the manufacturing method of the present invention, first, an aqueous solution of polyvinyl alcohol resin is applied to the surface of a manuscript made of natural wood or the like, and a nylon film is superimposed and laminated thereon.
ナイロンフイルムのラミネートはポリビニルア
ルコール樹脂の乾燥前に行なう。これは接着剤等
を用いることなくナイロンフイルムとポリビニル
アルコール樹脂皮膜の接着一体化を可能とし、接
着剤の使用による、シワの発生、工程数の増加等
を防止する効果を有する。 The nylon film is laminated before the polyvinyl alcohol resin is dried. This makes it possible to bond and integrate the nylon film and the polyvinyl alcohol resin film without using an adhesive or the like, and has the effect of preventing the occurrence of wrinkles, increase in the number of steps, etc. due to the use of adhesives.
ナイロンフイルムは、ポリビニルアルコール樹
脂皮膜との接着を更に強固にするためにその接着
面をコロナ放電処理したものを使用し、かつ、ポ
リビニルアルコール樹脂中の水分の揮散を可能と
するために、透湿度が200ｇ／m2／24hr以上のも
のを使用する。 The nylon film used has its adhesion surface treated with corona discharge treatment to further strengthen the adhesion with the polyvinyl alcohol resin film, and is also moisture permeable to allow the moisture in the polyvinyl alcohol resin to evaporate. Use a material with a weight of 200g/m 2 /24hr or more.
ナイロンフイルムをラミネートした後に加熱し
てポリビニルアルコール樹脂中の水分を除去し、
ポリビニルアルコール樹脂を皮膜化すると共にナ
イロンフイルムと接着一体化させ、次いで原稿か
ら剥離して賦型フイルムを得る。 After laminating the nylon film, it is heated to remove the moisture in the polyvinyl alcohol resin.
The polyvinyl alcohol resin is formed into a film and adhered to the nylon film, and then peeled off from the original to obtain a shaped film.
ポリビニルアルコール樹脂は、できる限りケン
化度が高く、重合度が高い方がポリエステル樹脂
に対する耐性が優れているので望ましいが、粘度
が高くなり過ぎると溶解度（濃度）が低くなつて
しまい、作業性が落ちるので、ケン化度97〜99％
重合度500〜1000位が望ましい。 Polyvinyl alcohol resin has a saponification degree as high as possible, and a higher degree of polymerization is desirable because it has better resistance to polyester resin, but if the viscosity becomes too high, the solubility (concentration) will decrease and workability will decrease. Since it falls, the degree of saponification is 97-99%
A degree of polymerization of 500 to 1000 is desirable.
またポリビニルアルコール樹脂水溶液は、後に
気泡が発生するのを防ぐために出来る限り事前に
真空脱泡した方が良い。裏打ちフイルムは、ポリ
ビニルアルコール樹脂との密着が良く、加熱した
時にポリビニルアルコール樹脂中の水分が抜けや
すいものが良く、透湿度が200ｇ／m2／24hr以上
のナイロンフイルムにコロナ放電処理を施したも
のを用いる。 Further, it is preferable that the polyvinyl alcohol resin aqueous solution is vacuum defoamed as much as possible in advance in order to prevent bubbles from being generated later. The backing film should be one that has good adhesion to the polyvinyl alcohol resin and allows the moisture in the polyvinyl alcohol resin to escape easily when heated, and should be a nylon film with a moisture permeability of 200 g/m 2 /24 hr or more that has been subjected to corona discharge treatment. Use.
また、裏打ちフイルムを用いず、ポリビニルア
ルコール樹脂単体の皮膜を形成して賦型フイルム
とすることも考えられるが、「はじき」が出やす
く、またレベリングが悪いために平滑な皮膜が得
られず、また強度も弱いため、裏打ちフイルムを
用いたものの方がより優れた賦形フイルムとな
る。 It is also possible to form a molded film by forming a film of polyvinyl alcohol alone without using a backing film, but it tends to "repel" and a smooth film cannot be obtained due to poor leveling. In addition, since the strength is weak, a molded film using a backing film is better.
（実施例）
樹脂配合
デンカポバールＫ−05（電気化学工業(株)製）
100重量部
グリセリン 10 〃
水 300 〃
上記樹脂配合のポリビニルアルコール樹脂水溶
液を作製し、真空にて30分間脱泡する。(Example) Resin formulation Denka Poval K-05 (manufactured by Denki Kagaku Kogyo Co., Ltd.)
100 parts by weight Glycerin 10 Water 300 A polyvinyl alcohol resin aqueous solution containing the above resin composition is prepared and defoamed in a vacuum for 30 minutes.
次に木目凹凸模様が賦型された型の表面に上記
ポリビニルアルコール樹脂水溶液を塗布して、次
にナイロンフイルム（(株)興人製、ボニールS15μ
厚）を重ね合わせ、泡を巻き込まないようにラミ
ネートする。 Next, the above polyvinyl alcohol resin aqueous solution was applied to the surface of the mold on which the wood grain pattern was formed, and then a nylon film (manufactured by Kojin Co., Ltd., Bonyl S15μ) was applied.
(thickness) and laminate them, taking care not to get the bubbles involved.
次に80℃のオーブンに１時間入れて水溶液の水
分をフイルムを通して揮散させ、次いで型から剥
離すると、木目凹凸模様が賦型されたポリビニル
アルコール樹脂皮膜とナイロンフイルムが一体化
されたポリエステル化粧板用賦型フイルムが得ら
れた。 Next, the water in the aqueous solution is volatilized through the film by placing it in an oven at 80℃ for 1 hour, and then peeling it off from the mold.The result is a polyester decorative board that integrates a polyvinyl alcohol resin film with an uneven wood grain pattern and a nylon film. A shaped film was obtained.
（発明の効果）
ポリビニルアルコール樹脂の成膜化が短時間
で完了し、安価な賦型フイルムが得られる。(Effects of the Invention) Film formation of polyvinyl alcohol resin is completed in a short time, and an inexpensive shaped film can be obtained.
ナイロンフイルムが裏打ちされているので耐
久性が大きく、繰り返し使用が可能である。 Because it is lined with nylon film, it is highly durable and can be used repeatedly.
裏打ちフイルムのラミネートに接着剤を使用
していないので、フイルム同志のラミネート時
に発生し易いシワの発生がなく、又、工程数の
増加もない。 Since no adhesive is used to laminate the backing film, wrinkles that tend to occur when laminating films together are not generated, and there is no increase in the number of steps.
Claims (1)
を塗布し、その上から透湿度が200ｇ／m2／24hr
以上のナイロンフイルムにコロナ放電処理を施し
たものを処理面がポリビニルアルコール樹脂水溶
液側に向くように重ね合わせてラミネートし、次
いで加熱してポリビニルアルコール樹脂水溶液中
の水分を除去し、次いでポリビニルアルコール樹
脂皮膜とナイロンフイルムとが一体となつたフイ
ルムを原稿表面から剥離することを特徴とするポ
リエステル化粧板用賦型フイルムの製造方法。1 Apply a polyvinyl alcohol resin aqueous solution to the surface of the original, and then increase the moisture permeability to 200g/m 2 /24hr.
The above nylon films subjected to corona discharge treatment are stacked and laminated with the treated side facing the polyvinyl alcohol resin aqueous solution, heated to remove water in the polyvinyl alcohol resin aqueous solution, and then polyvinyl alcohol resin A method for producing a molded film for a polyester decorative board, which comprises peeling a film in which a film and a nylon film are integrated from the surface of a document.