JPH0436474B2 - - Google Patents
Info
- Publication number
- JPH0436474B2 JPH0436474B2 JP58104694A JP10469483A JPH0436474B2 JP H0436474 B2 JPH0436474 B2 JP H0436474B2 JP 58104694 A JP58104694 A JP 58104694A JP 10469483 A JP10469483 A JP 10469483A JP H0436474 B2 JPH0436474 B2 JP H0436474B2
- Authority
- JP
- Japan
- Prior art keywords
- light emitting
- emitting diode
- stem
- submount
- pellet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
〔産業上の利用分野〕
この発明は半導体発光ダイオード、特にその放
熱特性の改良に関するものである。
〔従来の技術〕
発光ダイオードは電流駆動による大電力素子で
あるため、動作中の発熱が量大きい。そのため、
適切な放熱設計が行われていない場合には、通電
使用中の発熱により性能の劣化、素子寿命の低
下、あるいは発光ダイオードペレツトの破壊をま
ねく危険がある。
したがつて、発光ダイオードペレツトを支持す
るステムは、熱伝導率の高い材料を用いて熱放散
を良好にする必要がある。
また、上記ステムと発光ダイオードペレツトの
熱膨張係数に差があると、発熱に伴つてひずみが
発生し、発光ダイオードペレツトに不必要なスト
レスが加わる。このようなストレスは、発光ダイ
オードペレツトの性能の劣化を加速し、更にはそ
の破壊の原因となるものである。
したがつて、ステムの材料としては、熱伝導率
が高く、しかも熱膨張係数が発光ダイオードペレ
ツトのそれとできるだけ近いものであることが要
求される。
そこで、従来は、図面に示すように、発光ダイ
オードペレツト１をサブマウント２を介してパツ
ケージのステム３に取付け、そのサブマウント２
の材料として、コバール（商品名）の如き低熱膨
張特性を示す材料を使用することが行われてい
た。
〔発明が解決しようとする課題〕
サブマウント２の材料は、前述のとおり熱伝導
率が良好で、かつ熱膨張係数が発光ダイオードペ
レツト１のそれに近いことが要求される。
しかしながら、従来使用されているコバール
は、第１表に示すように、熱膨張係数は発光ダイ
オードペレツト１に非常に近いが、熱伝導率が低
い問題があり、このことが発光ダイオードの性能
改良の上で大きな障害となつていた。
〔課題を解決するための手段〕
この発明は、InAs、InP又はInSbを基板とする
発光ダイオードペレツトを対象とし、その場合の
サブマウント及びステムの材料として、熱膨張係
数4.7〜7.5×10-6cm／cm・℃の範囲にある次の金
属、すなわち
(1) ＷのCuを均一に含有させた合金
(2) MoにCuを均一に含有させた合金
(3) Ｗ・Mo合金にCuを均一に含有させた合金
のいずれか一つを使用することとし、かつステム
とサブマウントを一体成形したものである。上記
の合金は溶浸法によつて製造することができる。
サブマウントの材料が上記の熱膨張係数の範囲
を越えると、発光ダイオードペレツトとの熱膨張
係数の不整合が大きくなり、ペレツトに生じるス
トレスにより、ペレツトの破損又は発光効率の低
下など起こる。
また、上記範囲の熱膨張係数を満足する上記金
属材料のCu含有量を重量％で示せば次のとおり
である。
Ｗ＋Cu：0.5〜30％（前記(1)の金属材料）
Mo＋Cu：５〜35％（前記(2)の金属材料）
Ｗ・Mo＋Cu：0.5〜35％（前記(3)の金属材料）
なお、上記金属材料の熱伝導率は、0.35〜
0.70cal／cm・sec.℃である。
この発明の金属材料と従来例（コバール）との
対比、及び発光ダイオードペレツトの基板の熱膨
張係数を参考までに示せば、次の第１表に示すと
おりである。
[Industrial Field of Application] The present invention relates to semiconductor light emitting diodes, particularly to improvements in their heat dissipation characteristics. [Prior Art] Since a light emitting diode is a current-driven high-power device, it generates a large amount of heat during operation. Therefore,
If an appropriate heat dissipation design is not performed, there is a danger that heat generation during energized use may lead to performance deterioration, shortened element life, or destruction of the light emitting diode pellet. Therefore, the stem supporting the light emitting diode pellet must be made of a material with high thermal conductivity to provide good heat dissipation. Further, if there is a difference in the coefficient of thermal expansion between the stem and the light emitting diode pellet, distortion occurs due to heat generation, and unnecessary stress is applied to the light emitting diode pellet. Such stress accelerates the deterioration of the performance of the light emitting diode pellet and even causes its destruction. Therefore, the material for the stem is required to have high thermal conductivity and a coefficient of thermal expansion as close as possible to that of the light emitting diode pellet. Therefore, conventionally, as shown in the drawing, the light emitting diode pellet 1 is attached to the stem 3 of the package via the submount 2, and the submount 2 is attached to the stem 3 of the package.
As a material for this, a material exhibiting low thermal expansion characteristics such as Kovar (trade name) has been used. [Problems to be Solved by the Invention] As mentioned above, the material of the submount 2 is required to have good thermal conductivity and a coefficient of thermal expansion close to that of the light emitting diode pellet 1. However, as shown in Table 1, the conventionally used Kovar has a thermal expansion coefficient very close to that of light-emitting diode pellets 1, but has a problem of low thermal conductivity, which makes it difficult to improve the performance of light-emitting diodes. It was a big obstacle on the top. [Means for Solving the Problems] The present invention is directed to a light emitting diode pellet using InAs, InP or InSb as a substrate, and the material for the submount and stem in this case has a thermal expansion coefficient of 4.7 to 7.5×10 - The following metals in the range of 6 cm/cm・℃, namely (1) W alloy containing Cu uniformly (2) Alloy containing Mo uniformly containing Cu (3) W・Mo alloy containing Cu uniformly The stem and submount are integrally molded. The above alloys can be manufactured by an infiltration method. If the material of the submount exceeds the above-mentioned thermal expansion coefficient range, there will be a large mismatch in thermal expansion coefficient with the light emitting diode pellet, and the stress generated on the pellet will cause pellet breakage or decrease in luminous efficiency. Further, the Cu content of the metal material satisfying the thermal expansion coefficient in the above range is as follows in weight percent. W + Cu: 0.5 to 30% (metal material in (1) above) Mo + Cu: 5 to 35% (metal material in (2) above) W・Mo+Cu: 0.5 to 35% (metal material in (3) above) The thermal conductivity of metal materials is 0.35~
It is 0.70cal/cm・sec.℃. A comparison between the metal material of the present invention and a conventional example (Kovar) and the coefficient of thermal expansion of the substrate of the light emitting diode pellet are shown in Table 1 below for reference.
InP基板上にInGaAsをエピタキシヤル成長さ
せたダブルヘテロ構造を持つ発光ダイオードを第
２表に示す各種のサブマウント、ステムに固着し
た発光ダイオードを製作し、その性能の比較を行
つた。
Light-emitting diodes with a double heterostructure in which InGaAs was epitaxially grown on an InP substrate were manufactured by fixing them to the various submounts and stems shown in Table 2, and their performances were compared.
【表】【table】
【表】【table】
以上のとおりであるから、この発明によれば、
放熱が良好でかつ発熱に伴うストレスの少ない発
光ダイオードを得ることができる。
As described above, according to this invention,
A light emitting diode with good heat dissipation and less stress due to heat generation can be obtained.
図面は発光ダイオードの一例を示す断面図であ
る。
１……発光ダイオードペレツト、２……サブマ
ウント、３……ステム。
The drawing is a cross-sectional view showing an example of a light emitting diode. 1...Light emitting diode pellet, 2...Submount, 3...Stem.
Claims (1)
ードペレツトをサブマウントを介してパツケージ
のステムに取付けてなる発光ダイオードにおい
て、上記サブマウント及びステム材料として、熱
膨張係数が4.5〜7.5×10-6cm／cm℃の範囲にある
Ｗ，Mo若しくはＷ・Mo合金のいずれかに溶浸
法によりCuを均一に含有させた合金を用い、か
つ上記ステムとサブマウントを一体成形したこと
を特徴とする発光ダイオード。1. In a light emitting diode in which a light emitting diode pellet having a substrate of InAs, InP or InSb is attached to a stem of a package via a submount, the material for the submount and stem has a coefficient of thermal expansion of 4.5 to 7.5×10 -6 It is characterized by using an alloy in which Cu is uniformly contained in W, Mo or W/Mo alloy by an infiltration method in the range of cm/cm℃, and the stem and submount are integrally molded. light emitting diode.