JPH0451189B2 - - Google Patents
Info
- Publication number
- JPH0451189B2 JPH0451189B2 JP3504485A JP3504485A JPH0451189B2 JP H0451189 B2 JPH0451189 B2 JP H0451189B2 JP 3504485 A JP3504485 A JP 3504485A JP 3504485 A JP3504485 A JP 3504485A JP H0451189 B2 JPH0451189 B2 JP H0451189B2
- Authority
- JP
- Japan
- Prior art keywords
- potassium
- parts
- weight
- fire extinguishing
- freezing point
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は液状消火薬剤に関するものである。
従来、強化液消火薬剤として炭酸カリウムを主
成分としたものがあることはよく知られている
が、このものは３リツトルで一般火災Ａ−１の軽
微なものに対する消火は可能であつても、それ以
上の消火能力は期待できない。また、水系の消火
剤としてリン酸とアンモニア、尿素、アミン態、
硫酸塩もしくはスルフアミン酸塩などを含み、こ
れに不凍剤、界面活性剤、増粘剤などを添加した
ものもあるが、これら消火薬剤は低温安定性また
は消火性能において一長一短であり、たとえば消
火性能について言えば一般火災Ａと油火災Ｂとの
いずれか一方に効果的であるものは多くあつて
も、双方に効果的なものはきわめて少ない。
成分としたものがあることはよく知られている
が、このものは３リツトルで一般火災Ａ−１の軽
微なものに対する消火は可能であつても、それ以
上の消火能力は期待できない。また、水系の消火
剤としてリン酸とアンモニア、尿素、アミン態、
硫酸塩もしくはスルフアミン酸塩などを含み、こ
れに不凍剤、界面活性剤、増粘剤などを添加した
ものもあるが、これら消火薬剤は低温安定性また
は消火性能において一長一短であり、たとえば消
火性能について言えば一般火災Ａと油火災Ｂとの
いずれか一方に効果的であるものは多くあつて
も、双方に効果的なものはきわめて少ない。
また、消火器用消火薬剤の技術上の規格を定め
る省令において凝固点−20℃以下と規定される消
火薬剤のほとんどのものには不凍剤または凝固点
降下剤が添加されていて、これらが添加されてい
ないものとしては炭酸カリウムなど一部のもので
しかない。そして、不凍剤または凝固点降下剤と
しては通常エチレングリコール、プロピレングリ
コールなどが用いられており、冷却効果の大きい
物質であると期待されているが、これらはいずれ
も危険物第四類に属するものであつて、消火性能
を向上させるという立場からは好ましくない物質
である。
る省令において凝固点−20℃以下と規定される消
火薬剤のほとんどのものには不凍剤または凝固点
降下剤が添加されていて、これらが添加されてい
ないものとしては炭酸カリウムなど一部のもので
しかない。そして、不凍剤または凝固点降下剤と
しては通常エチレングリコール、プロピレングリ
コールなどが用いられており、冷却効果の大きい
物質であると期待されているが、これらはいずれ
も危険物第四類に属するものであつて、消火性能
を向上させるという立場からは好ましくない物質
である。
したがつて、この発明は一般火災Ａおよび油火
災Ｂの双方に対し効果的な消火薬剤がきわめて少
なく、また、凝固点を−20℃以下にするための不
凍液もしくは凝固点降下剤の使用は消火性能の向
上に対して不利であるという問題点を解決しよう
とするものである。
災Ｂの双方に対し効果的な消火薬剤がきわめて少
なく、また、凝固点を−20℃以下にするための不
凍液もしくは凝固点降下剤の使用は消火性能の向
上に対して不利であるという問題点を解決しよう
とするものである。
〔問題点を解決するための手段〕
上記の問題点を解決するために、この発明は酸
化カリウムK2Oの１モルに対して、無水リン酸
P2O5が0.05〜5.0モル、酸化ホウ素B2O3が0.1〜
1.0モルの割合で配合されたカリウム、リンおよ
びホウ素の三成分系の液体とする手段、ならび
に、この三成分系の液体にさらにアルカノールア
ミンを添加する手段を採つた。以下それらの詳細
を述べる。
化カリウムK2Oの１モルに対して、無水リン酸
P2O5が0.05〜5.0モル、酸化ホウ素B2O3が0.1〜
1.0モルの割合で配合されたカリウム、リンおよ
びホウ素の三成分系の液体とする手段、ならび
に、この三成分系の液体にさらにアルカノールア
ミンを添加する手段を採つた。以下それらの詳細
を述べる。
まず、この発明のカリウム、リンおよびホウ素
の三成分系の液体を構成する化合物としては、水
酸化カリウム、炭酸カリウム、重炭酸カリウム、
塩化カリウム、硫酸カリウム、酢酸カリウム等の
リン酸およびホウ酸を除くカリウム塩類、リン
酸、リン酸一カリウム、リン酸二カリウム、リン
酸三カリウム、リン酸一ナトリウム、リン酸二ナ
トリウム、リン酸三ナトリウム、亜リン酸、亜リ
ン酸カリウム、亜リン酸ナトリウム、無水リン酸
等のリン酸およびその塩類、無水ホウ酸、八ホウ
酸カリウム、六ホウ酸カリウム、五ホウ酸カリウ
ム、四ホウ酸カリウム、メタホウ酸カリウム、メ
タホウ酸ナトリウム、四ホウ酸ナトリウム、六ホ
ウ酸ナトリウム、八ホウ酸ナトリウムなどのホウ
酸およびホウ酸塩類の中から２種以上を選び、所
定のモル比に調合する。これを水100重量部に対
して固形成分40〜120重量部、好ましくは50〜100
重量部となるように加えて水溶液とする。
の三成分系の液体を構成する化合物としては、水
酸化カリウム、炭酸カリウム、重炭酸カリウム、
塩化カリウム、硫酸カリウム、酢酸カリウム等の
リン酸およびホウ酸を除くカリウム塩類、リン
酸、リン酸一カリウム、リン酸二カリウム、リン
酸三カリウム、リン酸一ナトリウム、リン酸二ナ
トリウム、リン酸三ナトリウム、亜リン酸、亜リ
ン酸カリウム、亜リン酸ナトリウム、無水リン酸
等のリン酸およびその塩類、無水ホウ酸、八ホウ
酸カリウム、六ホウ酸カリウム、五ホウ酸カリウ
ム、四ホウ酸カリウム、メタホウ酸カリウム、メ
タホウ酸ナトリウム、四ホウ酸ナトリウム、六ホ
ウ酸ナトリウム、八ホウ酸ナトリウムなどのホウ
酸およびホウ酸塩類の中から２種以上を選び、所
定のモル比に調合する。これを水100重量部に対
して固形成分40〜120重量部、好ましくは50〜100
重量部となるように加えて水溶液とする。
ここで、水100重量部に対し酸化カリウムK2O
と無水リン酸のモル比が3.20の固形分70重量部の
水溶液は、凝固点が−20℃以下ではあるが、消火
性能はこの発明が期待する水準には達しない。ま
た、水100重量部に対して酸化カリウムK2Oと酸
化ホウ素B2O3のモル比1.1の固形成分50重量部の
水溶液も前記カリウムとリンの二成分系のものと
同様に凝固点が−20℃以下であるが消火性能は期
待できない。しかし、これらの二成分系のそれぞ
れに、不足する成分を混合もしくは中和させて、
この発明のようなモル比のカリウム、リンおよび
ホウ素からなる三成分系の液体に調整すれば、凝
固点が−20℃以下であるということはもちろんの
こと、消火性能においても著しい効果を発揮する
ようになる。したがつて、酸化カリウムK2Oの１
モルに対して無水リン酸P2O5が0.05〜0.50モル、
酸化ホウ素B2O3が0.1〜1.0モルである三成分系液
体とすることが望ましい。なお、各成分がこの限
定範囲の上限値を越える多量になると、消火性能
が低下し、また凝固点が−20℃に達しないことも
あつて好ましくない。
と無水リン酸のモル比が3.20の固形分70重量部の
水溶液は、凝固点が−20℃以下ではあるが、消火
性能はこの発明が期待する水準には達しない。ま
た、水100重量部に対して酸化カリウムK2Oと酸
化ホウ素B2O3のモル比1.1の固形成分50重量部の
水溶液も前記カリウムとリンの二成分系のものと
同様に凝固点が−20℃以下であるが消火性能は期
待できない。しかし、これらの二成分系のそれぞ
れに、不足する成分を混合もしくは中和させて、
この発明のようなモル比のカリウム、リンおよび
ホウ素からなる三成分系の液体に調整すれば、凝
固点が−20℃以下であるということはもちろんの
こと、消火性能においても著しい効果を発揮する
ようになる。したがつて、酸化カリウムK2Oの１
モルに対して無水リン酸P2O5が0.05〜0.50モル、
酸化ホウ素B2O3が0.1〜1.0モルである三成分系液
体とすることが望ましい。なお、各成分がこの限
定範囲の上限値を越える多量になると、消火性能
が低下し、また凝固点が−20℃に達しないことも
あつて好ましくない。
このようなカリウム、リンおよびホウ素の三成
分系溶液100容量部に対し、アルカノールアミン、
たとえば、ジイソプロパノールアミン、Ｎ，Ｎ−
ジアルキル（炭素数１〜３）−Ｎ−エタノールア
ミン、トリエタノールアミン、２−メチル−２ジ
メチルアミノメチル、１，３−プロパンジオー
ル、トリイソプロパノールアミン、Ｎ−エチルジ
エタノールアミン、Ｎ−メチルジエタノールアミ
ン、ジメチルアミノプロパノールなどの単独もし
くは混合物を５〜50容量部、好ましくは10〜30容
量部を添加すれば、凝固点降下においても、また
消火性能の向上においてもきわめて有効である。
ここで、アルカノールアミンが上記下限値よりも
少量のときは顕著な効果は現われず、逆に上限値
よりも多量のときは粘度が高くなり消火性能を低
下させる要因となつて好ましくない。
分系溶液100容量部に対し、アルカノールアミン、
たとえば、ジイソプロパノールアミン、Ｎ，Ｎ−
ジアルキル（炭素数１〜３）−Ｎ−エタノールア
ミン、トリエタノールアミン、２−メチル−２ジ
メチルアミノメチル、１，３−プロパンジオー
ル、トリイソプロパノールアミン、Ｎ−エチルジ
エタノールアミン、Ｎ−メチルジエタノールアミ
ン、ジメチルアミノプロパノールなどの単独もし
くは混合物を５〜50容量部、好ましくは10〜30容
量部を添加すれば、凝固点降下においても、また
消火性能の向上においてもきわめて有効である。
ここで、アルカノールアミンが上記下限値よりも
少量のときは顕著な効果は現われず、逆に上限値
よりも多量のときは粘度が高くなり消火性能を低
下させる要因となつて好ましくない。
この発明の消火薬剤の作用は詳らかではない
が、リン化合物およびホウ素化合物はよく知られ
ているように難燃作用を示す物質であつて、これ
らを含有するこの発明の消火薬剤が可燃物表面に
付着し、被膜の形成または浸透して空気中の酸素
または火災の熱源を遮断する作用を発揮するのは
当然であろうが、この発明の消火薬剤はこれらリ
ン化合物またはホウ素化合物の単独使用もしくは
両者の併用の際の作用よりも遥かに優れた消火作
用を示すことから、三成分を共存させたことによ
る特別な相乗作用が現われるものと推定される。
が、リン化合物およびホウ素化合物はよく知られ
ているように難燃作用を示す物質であつて、これ
らを含有するこの発明の消火薬剤が可燃物表面に
付着し、被膜の形成または浸透して空気中の酸素
または火災の熱源を遮断する作用を発揮するのは
当然であろうが、この発明の消火薬剤はこれらリ
ン化合物またはホウ素化合物の単独使用もしくは
両者の併用の際の作用よりも遥かに優れた消火作
用を示すことから、三成分を共存させたことによ
る特別な相乗作用が現われるものと推定される。
実施例 １
水100重量部に、リン酸カリウム20重量部、ホ
ウ酸カリウム20重量部、重炭酸カリウム10重量部
を添加し、モル比K2O：P2O5：B2O3＝1.0：
0.25：0.32の水溶液を調製した。この水溶液に対
して、消火器用消火薬剤の技術上の規格を定める
省令に定められた凝固点試験（内径18mmの試験管
に試料10mlを採取し、温度計を入れ、試験管寒剤
浴で撹拌しながら冷却し、結晶物が析出し始めた
ならば試験管を浴から取り出し、撹拌を継続し析
出した結晶片が無くなつて液全体が透明になつた
ときの温度を読み取る）による凝固点を求めたと
ころ、凝固点は−26.5℃であつた。また、消火テ
ストはＡ（一般火災）およびＢ（油火災）の消火単
位法を採用し、かつ、蓄圧式３リツトル型消火器
に水溶液３リツトルを充填して実施した。その結
果は一般火災に対してはＡ−２、油火災に対して
はＢ−２であつた。
ウ酸カリウム20重量部、重炭酸カリウム10重量部
を添加し、モル比K2O：P2O5：B2O3＝1.0：
0.25：0.32の水溶液を調製した。この水溶液に対
して、消火器用消火薬剤の技術上の規格を定める
省令に定められた凝固点試験（内径18mmの試験管
に試料10mlを採取し、温度計を入れ、試験管寒剤
浴で撹拌しながら冷却し、結晶物が析出し始めた
ならば試験管を浴から取り出し、撹拌を継続し析
出した結晶片が無くなつて液全体が透明になつた
ときの温度を読み取る）による凝固点を求めたと
ころ、凝固点は−26.5℃であつた。また、消火テ
ストはＡ（一般火災）およびＢ（油火災）の消火単
位法を採用し、かつ、蓄圧式３リツトル型消火器
に水溶液３リツトルを充填して実施した。その結
果は一般火災に対してはＡ−２、油火災に対して
はＢ−２であつた。
実施例 ２
水100重量部に対し、水酸化カリウム40重量部、
ホウ酸ナトリウム20重量部、リン酸10重量部を添
加し、モル比K2O：P2O5：B2O3＝1.0：0.11：
0.57とした以外は実施例１と同様の方法で得られ
た水溶液の凝固点の測定、消火テストを実施し
た。凝固点は−22℃、消火テストはＡ−２および
Ｂ−２であつた。
ホウ酸ナトリウム20重量部、リン酸10重量部を添
加し、モル比K2O：P2O5：B2O3＝1.0：0.11：
0.57とした以外は実施例１と同様の方法で得られ
た水溶液の凝固点の測定、消火テストを実施し
た。凝固点は−22℃、消火テストはＡ−２および
Ｂ−２であつた。
実施例 ３
水100重量部に対し、リン酸ナトリウム10重量
部、ホウ酸カリウム30重量部、硫酸カリウム10重
量部、炭酸カリウム40重量部を添加し、モル比
K2O：P2O5：B2O3＝1.0：0.14：0.50とした以外
は実施例１と同様の操作をした。その結果、凝固
点は−24℃であり、消火テストはＡ−２およびＢ
−２であつた。
部、ホウ酸カリウム30重量部、硫酸カリウム10重
量部、炭酸カリウム40重量部を添加し、モル比
K2O：P2O5：B2O3＝1.0：0.14：0.50とした以外
は実施例１と同様の操作をした。その結果、凝固
点は−24℃であり、消火テストはＡ−２およびＢ
−２であつた。
実施例 ４
水100重量部に水酸化カリウム30重量部、リン
酸カリウム30重量部、ホウ酸20重量部を添加し、
モル比K2O：P2O5：B2O3＝1.0：0.20：0.34とし
た以外は実施例１と同様の操作をした。その結
果、凝固点は−28℃、消火テストはＡ−２および
Ｂ−２であつた。
酸カリウム30重量部、ホウ酸20重量部を添加し、
モル比K2O：P2O5：B2O3＝1.0：0.20：0.34とし
た以外は実施例１と同様の操作をした。その結
果、凝固点は−28℃、消火テストはＡ−２および
Ｂ−２であつた。
実施例 ５
実施例１の消火薬剤100容量部に対し、トリエ
タノールアミン20容量部を添加した。このものの
凝固点は−29℃であり、消火テストはＡ−３およ
びＢ−２を示し、実施例１と比べて凝固点降下お
よび消火性能向上に顕著な効果が見られた。
タノールアミン20容量部を添加した。このものの
凝固点は−29℃であり、消火テストはＡ−３およ
びＢ−２を示し、実施例１と比べて凝固点降下お
よび消火性能向上に顕著な効果が見られた。
比較例 １
水100重量部にリン酸カリウム70重量部を添加
して、モル比K2O：P2O5＝1.0：3.20とした水溶
液に対して実施例１と同様の操作を行なつた。得
られた凝固点は−22℃で消火テストはＡ−１およ
びＢ−１であり、前記実施例１〜５のいずれより
も劣つていた。
して、モル比K2O：P2O5＝1.0：3.20とした水溶
液に対して実施例１と同様の操作を行なつた。得
られた凝固点は−22℃で消火テストはＡ−１およ
びＢ−１であり、前記実施例１〜５のいずれより
も劣つていた。
比較例 ２
水100重量部にホウ酸カリウム70重量部を添加
して、モル比K2O：B2O3＝1.0：1.1とした水溶液
に対して実施例１と同様の操作を行なつた。得ら
れた凝固点は−21℃で、消火テストはＡ−１およ
びＢ−１であつて実施例１〜５のいずれにも及ば
なかつた。
して、モル比K2O：B2O3＝1.0：1.1とした水溶液
に対して実施例１と同様の操作を行なつた。得ら
れた凝固点は−21℃で、消火テストはＡ−１およ
びＢ−１であつて実施例１〜５のいずれにも及ば
なかつた。
比較例 ３
水100重量部に炭酸カリウム66.6重量部を添加
し、実施例１と同様の操作をした。得られた凝固
点は−26℃であつたが消火テストはＡ−１および
Ｂ−２であつて、好ましい消火性能を示さなかつ
た。
し、実施例１と同様の操作をした。得られた凝固
点は−26℃であつたが消火テストはＡ−１および
Ｂ−２であつて、好ましい消火性能を示さなかつ
た。
以上のことから明らかなように、この発明のよ
うに、ある特定のモル比で配合したカリウム、リ
ンおよびホウ素の三成分系組成物の水溶液および
この水溶液にさらにアルカノールアミンを添加し
た水溶液は、凝固点のみならず消火性能のうえで
従来の消火薬剤よりも遥かに優れたものである。
よつてこの発明の意義はきわめて大きいと言え
る。
うに、ある特定のモル比で配合したカリウム、リ
ンおよびホウ素の三成分系組成物の水溶液および
この水溶液にさらにアルカノールアミンを添加し
た水溶液は、凝固点のみならず消火性能のうえで
従来の消火薬剤よりも遥かに優れたものである。
よつてこの発明の意義はきわめて大きいと言え
る。
Claims (1)
- 【特許請求の範囲】 １ 酸化カリウムK2Oの１モルに対して、無水リ
ン酸P2O5が0.05〜0.50モル、酸化ホウ素B2O3が
0.1〜1.0モルの割合で配合されたカリウム、リン
およびホウ素の三成分系であることを特徴とする
液状消火薬剤。 ２ 酸化カリウムK2Oの１モルに対して、無水リ
ン酸P2O5が0.05〜0.50モル、酸化ホウ素B2O3が
0.1〜1.0モルの割合で配合されたカリウム、リン
およびホウ素の三成分にアルカノールアミンを添
加したことを特徴とする液状消火薬剤。