the adhesive composition can be produced by mixing an aqueous emulsion (31) containing the natural rubber fine particles (30) and the a radiation curable compound having a cyclic ether (32), heating the mixture under stirring to evaporate and remove water in the aqueous emulsion with dispersed natural rubber fine particles to replace water with the radiation curable compound having a cyclic ether in the medium.例文帳に追加

この接着剤組成物は、天然ゴム系微粒子３０を含有する水系エマルジョン３１と、含環状エーテル放射線硬化性化合物３２とを混合し、混合物を攪拌しながら昇温し、水系エマルジョンの水を気化させ除去し、天然ゴム系微粒子が分散している媒体を水から含環状エーテル放射線硬化性化合物に置換して製造できる。 - 特許庁

The veneer plate and a substrate material are bonded by applying heat and pressure by using an adhesive composition characterized by containing resin emulsion based on vinyl acetate introduced with an acetoacetyl group, produced by a method of using a polyvinyl alcohol having the acetoacetyl group in emulsion polymerization, or copolymerizing the vinyl acetate with a monomer such as acetoacetoxyethyl methacrylate (AAEM), and having ≥10°C lowest film-forming temperature.例文帳に追加

乳化重合の際にアセトアセチル基を有するポリビニルアルコールを使用したり、酢酸ビニルとアセトアセトキシエチルメタクリレート（ＡＡＥＭ）のような単量体を共重合するなどの方法によってアセトアセチル基を導入した酢酸ビニル系樹脂エマルジョンを含有し、最低造膜温度が１０℃以上であることを特徴とする接着剤組成物を用いて、突板と基材を加熱圧締する。 - 特許庁

To provide an aqueous resin emulsion widely applicable as various coating materials such as an inorganic material, film, etc., and as aqueous materials such as a binder for an adhesive, ink, binder for a coating, etc., and having strong film strength, cohesive strength, chemicals resistance, and smoothness.例文帳に追加

無機材料、フイルム等の各種コーティング剤、粘接着用バインダー、インキ・塗料用バインダーなどに水系材料として広く応用することが出来、強い膜強度と密着強度、耐薬品性、さらに滑らかさを持った水系樹脂エマルションを得る。 - 特許庁

The aqueous adhesive composition comprises a main agent comprised of one or two or more from among an aqueous solution of a water-soluble polymer, an aqueous latex and an aqueous emulsion, a curing agent comprised of an isocyanate compound, a compound (A) having an ether structure, and a compound (B) having an imide structure.例文帳に追加

水溶性高分子水溶液、水性ラテックス、水性エマルジョンの１種または２種以上からなる主剤と、イソシアネート化合物からなる硬化剤と、エーテル構造を有する化合物（Ａ）と、イミド構造を有する化合物（Ｂ）とを含む。 - 特許庁

An adhesive liquid having a minimum film forming temperature of not higher than the minimum film forming temperature of a resin emulsion which constitutes the thermoplastic resin layer is driven into the recorded face of the recording medium by an ink jet system before thermally bonding the thermoplastic resin layer thereto.例文帳に追加

熱可塑性樹脂層を加熱圧着させる前に、記録媒体の被記録面に、最低造膜温度が該熱可塑性樹脂層を構成する樹脂エマルジョンの最低造膜温度以下である接着液を、インクジェット方式により打ち込む。 - 特許庁

An abrasive and water are kneaded with a caking additive, e.g. a vinyl acetate resin emulsion adhesive, the mixture is poured from one side of waste to obtain water-holding abrasive cloth utilizing the staple length as part of a combination, and the painted face or the like is polished with it.例文帳に追加

研磨剤と水分を粘結剤、例えば酢酸ビニル樹脂エマルジョン系接着剤で練り合わせた物をウエスの片側から流し込む事によりそれの毛足を結合体の一部に利用した保水研摩布とし、これで塗装面等を研磨する。 - 特許庁

The adhesive layer is formed from an aqueous dispersion liquid containing an acrylic polymer obtained by emulsion-polymerizing monomer raw materials containing a 4-12C alkyl (meth)acrylate in a proportion of ≥60 mass% of all monomer components.例文帳に追加

前記粘着剤層は、炭素数が４〜１２のアルキル基を有するアルキル（メタ）アクリレートを全モノマー成分の６０質量％以上の割合で含むモノマー原料を乳化重合してなるアクリル系ポリマーを含む水分散液から形成される。 - 特許庁

The aqueous vinyl urethane-based adhesive comprises a resin emulsion containing an aqueous polymer as a main agent and an isocyanate compound composed of MDI or crude MDI as a curing agent.例文帳に追加

ところが、水性ビニルウレタン系接着剤で接着加工した集成材などを漂白処理のために過酸化水素処理を施す場合があり、ジフェニルメタンジイソシアネート系の硬化剤を使用した場合には接着層が茶色に変色するという問題がある。 - 特許庁

To provide an O/W emulsion composition containing amorolfine that is less irritating to the skin owing to substantially no incorporation of surfactants and is assumed to retain manifestation of medicinal effects of amorolfine owing to high adhesive retention of amorolfine.例文帳に追加

実質的に界面活性剤を配合していないため皮膚への刺激がより少なく、アモロルフィンの付着滞留性が高いため、アモロルフィンの薬効の発現が持続すると考えられるアモロルフィンを含有するＯ／Ｗエマルション組成物を提供する。 - 特許庁

The thermoconductive emulsion is used as a highly thermoconductive coating or adhesive agent, exhibiting high thermoconductivity as at least 5 W/m×k for it contains at least 1,000 pts.wt. of the loaded thermoconductive particle based on 100 pts.wt. of the resin.例文帳に追加

本発明に係る熱伝導性エマルジョンは、高熱伝導性コート剤または接着剤として使用されるが、樹脂100重量部に対して1000重量部以上の熱伝導性粒子が充填されているため、5W／m・k以上といった高い熱伝導性を示す。 - 特許庁

To provide a non-halogen spandrel wall material capable of even being bonded with an aqueous acrylic emulsion adhesive by having sufficient surface durability without occurrence of any fold in an internal or external corner in the case of construction.例文帳に追加

厚みによるボリューム感を持ちながら、施工時に出入り隅での曲げしわ、角の発生が無く、充分な表面耐久性を備え、水性アクリル系エマルジョン接着剤でも接着することができる非ハロゲン系腰壁材を提供することである。 - 特許庁

The aqueous adhesive composition comprises a urethane prepolymer having a blocked isocyanate group and having a glass transition temperature of 0°C or lower, an acrylic resin having a glass transition temperature of 0°C or lower, and water, wherein the urethane prepolymer and the acryl resin form an emulsion in the water.例文帳に追加

ブロックイソシアネート基を有しガラス転移温度が０℃以下であるウレタンプレポリマーと、ガラス転移温度が０℃以下であるアクリル樹脂と、水とを含有し、前記ウレタンプレポリマーと前記アクリル樹脂とが水中でエマルジョンとなっている水系接着剤組成物。 - 特許庁

This repairing material 1 includes a solid sheet body 7 formed by sticking a powder agent 3 containing polymer powder of (meth)acrylate and a polymerization initiator causing polymerization of a (meth)acrylate monomer onto a reinforcing cloth body 2 by a synthetic resin emulsion adhesive 4.例文帳に追加

補修材１は、（メタ）アクリレートのポリマー粉末と（メタ）アクリレートモノマーの重合を引き起こす重合開始剤とを含んで成る粉剤３を合成樹脂エマルジョン接着剤４により補強用布体２に付着させた固形シート体７を備えている。 - 特許庁

This aq. adhesive is obtd. by combining a plasticizer and an aq. polymer emulsion contg. a vinyl acetate polymer as a polymer particle using a modified polyvinyl alcohol contg. a carboxy group and a 5-15C alkyl group as an emulsifier, and it may contain a water-soluble polymer.例文帳に追加

カルボキシル基及びＣ_5-15アルキル基を含有するポリビニルアルコール変成体を乳化剤とし、酢酸ビニル系重合体を重合体粒子として含む水性高分子エマルジョンと、可塑剤とを組み合わせることにより、水性接着剤を得る。 - 特許庁

The object is achieved by using the adhesive composition for the the wooden fibrous plate, and the composition comprises a compound having two or more isocyanate groups in a molecule, wax emulsion and a compound having three or more hydroxyl groups in a molecule.例文帳に追加

１分子中に２個以上のイソシアネート基を有する化合物、ワックスエマルジョン、及び、１分子中に３個以上の水酸基を有する化合物、からなる、木質繊維板用接着剤組成物を用いることにより、上記の課題を解決する。 - 特許庁

The light-diffusing pressure-sensitive adhesive composition includes an aqueous emulsion containing polymer particles (A-1) comprising acrylic copolymer (A), organic particulates (B), a curing agent (C) curing the acrylic copolymer (A) and a quaternary ammonium compound (D).例文帳に追加

アクリル系共重合体（Ａ）からなるポリマー粒子（Ａ−１）を含む水系エマルジョンと、有機系微粒子（Ｂ）と、前記アクリル系共重合体（Ａ）を硬化させ得る硬化剤（Ｃ）と、４級アンモニウム化合物（Ｄ）と、を含有する光拡散性粘着剤組成物。 - 特許庁

The adhesive contains (A) a polyvinyl alcohol resin modified by a reactive group having an active hydrogen, water emulsion as the main component (B), and a hardener containing (C) a polyvalent isocyanate compound.例文帳に追加

活性水素を有する反応性基で変性されたポリビニルアルコール系樹脂（Ａ）及び水性エマルジョン（Ｂ）を含有する水性液の主剤及び多価イソシアネート化合物（Ｂ）を含有する硬化剤からなり、かつ下記（１）式の条件を満足してなる。 - 特許庁

The adhesive composition contains the highly-saturated nitrile rubber latex which is obtained by hydrogenating the latex of the nitrile rubber obtained by emulsion polymerization and has 10-55 wt.% content of nitrile monomer units and ≤12 iodine value.例文帳に追加

乳化重合で得られたニトリルゴムのラテックスを水素化処理に付することによって得られた、ニトリル単量体単位含有量が１０〜５５重量％であり、ヨウ素価が１２以下である高飽和ニトリルゴムラテックスを含有して成る接着剤組成物。 - 特許庁

The water-borne adhesive composition is characterized by comprising (A) an ethylene-vinyl acetate copolymer emulsion and (B) at least one or more kinds selected from propylene glycol monobutyl ether, dipropylene glycol monobutyl ether, tripropylene glycol monobutyl ether and ethylene glycol mono-2-ethylhexyl ether.例文帳に追加

（Ａ）エチレン酢酸ビニル系共重合体エマルジョンと、（Ｂ）プロピレングリコールモノブチルエーテル、ジプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノブチルエーテルおよびエチレングリコールモノ２−エチルヘキシルエーテルから選ばれた少なくとも１種以上を含有する水性接着剤組成物。 - 特許庁

The water-based adhesive composition comprises a urethane polymer containing carboxy and blocked isocyanate and having ≤0°C glass-transition temperature, a crosslinking agent having reactivity to the carboxy, and water, wherein the urethane polymer forms emulsion in water.例文帳に追加

カルボキシ基とブロックイソシアネート基とを有しガラス転移温度が０℃以下であるウレタンプレポリマーと、前記カルボキシ基に対して反応性を有する架橋剤と、水とを含有し、前記ウレタンプレポリマーが水中でエマルジョンとなっている水系接着剤組成物。 - 特許庁

This aqueous adhesive composition is obtained by emulsion copolymerization of ethylene with vinyl acetate monomer seeded by a urethane resin emulsion.Thus conventional problems such as adhesiveness to polyolefin-based resin, thermal creep resistance and low temperature adhesiveness are cleared.例文帳に追加

ウレタン樹脂エマルジョンをシードとして、エチレン、酢酸ビニルモノマーを乳化共重合して調製された水性接着剤組成物により、ポリオレフィン系樹脂に対する接着性、耐熱クリープ性、低温接着性など従来の課題を解決できた。 - 特許庁

To obtain an adhesive composition maintaining characteristics of excellent bond strength, water resistance, stability, or the like, of an ethylene- vinyl acetate copolymer emulsion, further excellent heat resistance, suitable for adhesion substrate a wood member and a synthetic resin-based member.例文帳に追加

エチレン−酢酸ビニル共重合体エマルジョンの有する優れた接着力、耐水性、安定性などの特性を維持しつつ、さらに耐熱性においても優れ、木質部材と合成樹脂系部材の接着に適した接着剤組成物を提供する。 - 特許庁

This information-recording paper is characterized by laminating an aqueous emulsion pressure-sensitive adhesive layer 2 not sticking in an usual state but showing a peelable sticking property by compression on at least one side of a paper substrate 1 having temperature dependent water absorbing property.例文帳に追加

この情報記録用紙は、吸水温度依存性を有する紙基材１の少なくとも片面に、通常の状態では接着せず加圧により剥離可能な接着性を示す水性エマルジョン感圧接着剤層２が積層されていることを特徴とする。 - 特許庁

To provide an emulsion coating composition which has excellent hydrophilic nature, adhesive properties and a film appearance, can reduce the problem of environmental pollution caused by using organic solvents and is highly safe, to provide coated articles thereof, and a method for manufacturing the same.例文帳に追加

優れた親水性、密着性及び塗膜外観が発現されると共に、有機溶剤から生じる塗装作業環境の問題を低減させ得る、より安全性が高いエマルション塗料組成物とその塗装物品及びその製造方法を提供する。 - 特許庁

To provide an emulsion type adhesive composition of the two-pack mixing type which exhibits bonding performances such as excellent adhesion to various adherends and excellent bonding power, heat resistance, water resistance and the like and, at the same time, excels in workability, storage stability and the like.例文帳に追加

各種被着体に対する優れた密着性や優れた接着力、耐熱性、耐水性等の接着性能を発揮し、且つ、作業性や貯蔵安定性等にも優れる２液混合型のエマルジョン型接着剤組成物を提供することを課題とする。 - 特許庁

This adhesive composition is characterized by compounding (B) 5 to 200 pts.wt. of an oligo acrylate having one or more (meth)acryloyl groups in the molecule into (A) 100 pts.wt. of the solid content of the emulsion of polyvinyl acetate and/or a vinyl acetate-copolymerizable monomer copolymer.例文帳に追加

（A）ポリ酢酸ビニル及び／又は酢酸ビニルと共重合可能なモノマーとの共重合ポリマーのエマルジョンの固型分100重量部に、（B）1分子中に1個以上の（メタ）アクリロイル基を有するオリゴ・アクリレート５重量部以上200重量部以下を配合する接着剤組成物 - 特許庁

This adhesive composition contains a water soluble polymer or a polymer emulsion, a penetrant and one or more species of antisensitive compounds selected from a group consisting of a polyoxyethylene oleyl ether, a polyoxyethylene oleyl phenyl ether, a polyoxyethylene monooleate and a polyoxyethylene sorbitan monooleate.例文帳に追加

接着剤組成物が、水溶性高分子又は高分子エマルジョン、浸透剤及びポリオキシエチレンオレイルエーテル、ポリオキシエチレンオレイルフェニルエーテル、ポリオキシエチレンモノオレエート、ポリオキシエチレンソルビタンモノオレエートの群から選ばれる１種或いは２種以上の減感性化合物を含有する。 - 特許庁

The polarizer protecting film containing thermoplastic resin (A) (for example, olefin-maleimide copolymer) having at least a substitutional or non-substitutional imide radical on a side chain is stuck on at least one side of a polarizer with water urethane-based adhesive constituted of water resin emulsion (for example, anion water polyester emulsion) and water-dispersion polyisocyanate compound (for example, aliphatic diisocyanate), then, the polarizing plate is obtained.例文帳に追加

少なくとも側鎖に置換または非置換イミド基を有する熱可塑性樹脂（Ａ）（例えばオレフィン−マレイミド共重合体）を含む偏光子保護フィルムを、偏光子の少なくとも片面に、水性樹脂エマルジョン（例えばアニオン性水性ポリエステルエマルジョン）と水分散性ポリイソシアネート組成物（例えば脂肪族ジイソシアネート）からなる水性ウレタン系接着剤により貼り合わせて、目的の偏光板を得る。 - 特許庁

This adhesive composition of the aqueous emulsion of the one-pack type is obtained by blending the aqueous dispersion-type crosslinking agent containing the oxazoline group to an aqueous dispersion-type copolymer of an acrylic adhesive composition having a weight-average molecular weight of at least 1,000,000 obtained by copolymerizing a 4-18C alkyl ester of (meth)acrylic acid as a main component and a carboxyl group-containing monomer.例文帳に追加

アルキル基の炭素数が４〜１８の（メタ）アクリル酸アルキルエステルを主成分とし、カルボキシル基含有モノマーを共重合した重量平均分子量が少なくとも１００万のアクリル系粘着剤組成の水分散系共重合体に、オキサゾリン基を含有する水分散系架橋剤を配合した一液タイプの水性エマルション型粘着剤組成物である。 - 特許庁

To provide an adhesive composition that shows excellent adhesion property to lumber not only of broadleaf tree but also of needleleaf tree causing adhesion trouble, has reduced smell and minimized environmental contamination, does not diffuse formaldehyde because the composition is an aqueous emulsion but includes no organic solvent, and has excellent workability, long-term adhesive properties, adhesion properties, resistance to water and resistance to boiling water.例文帳に追加

広葉樹のみならず接着性に問題のある針葉樹等の難接着合板に対し優れた接着性を有し、水性エマルジョンであって有機溶剤を含まないため、臭気及び環境汚染が少なく、全くホルムアルデヒドを放散せず、作業性に優れ、可使時間が長い密着性、接着性、耐水性、耐煮沸性のある接着剤組成物の提供。 - 特許庁

In the false adhesive paper, air permeability defined by JIS P-8117 is ≤1,500 sec and the adhesive base contains an acrylic acid ester copolymer resin emulsion obtained by emulsifying an acrylic acid ester copolymer resin containing 50-90 mass % butyl acrylate monomer and 5-45 mass % ethyl acrylate monomer in a monomer raw material and does not contain a natural rubber latex.例文帳に追加

ＪＩＳ Ｐ ８１１７に規定される透気度が１５００秒以下であり、かつ、接着基剤が、モノマー原料中にブチルアクリレートモノマーを５０〜９０質量％、エチルアクリレートモノマーを５〜４５質量％含むアクリル酸エステル共重合体樹脂を乳化したアクリル酸エステル共重合体樹脂エマルジョンを含み天然ゴムラテックスを含まない疑似接着用紙により解決される。 - 特許庁

The pressure sensitive adhesive composition of an aqueous emulsion type contains a liquid toner-receptive resin, is applied on the stacked surfaces of sheets and forms an adhesive layer 6 which does not adhere under an ordinary condition by drying and peelably adheres the stacked surfaces by putting them face-to-face and applying specific pressure on them.例文帳に追加

シートの重ね合わせ面に塗布され、乾燥処理により通常状態では接着しない接着層６を形成し、重ね合わせ面同士を対接させ所定の圧力を付与することにより、その重ね合わせ面同士を剥離可能に接着させる水系エマルジョンタイプの感圧接着剤組成物であって、液体トナー受容性樹脂を含む感圧接着剤組成物を用いる。 - 特許庁

Two tackifier resins are brought to be compartively coexist in one emulsion particle and dispersed in water in the same state by mixing and melting in advance the rosin derivative having higher softening point with the terpene-based resin having lower softening point and collectively emulsifying the mixed resin, so the balance of two or more physical adhesive properties between the adhesive power to olefins and tackiness at low temperatures is improved.例文帳に追加

高軟化点の重合ロジン誘導体と低軟化点のテルペン系樹脂とを予め溶融混合し、この混合樹脂をまとめて乳化することにより、一つのエマルション粒子内に複数の粘着付与剤樹脂が相溶して存在させた状態で水中に分散させるため、対オレフィン粘着力と低温タック性の複数の粘着物性バランスが良好になる。 - 特許庁

To obtain an aqueous emulsion-type adhesive of one package-type (1) excellent in water resistance and hot water resistance, (2) small in the increase in viscosity at a low temperature and excellent in workability, and (3) having improved preservability even without using a stabilizer such as an acidic sulfite salt.例文帳に追加

耐水性及び耐温水性に優れ、 低温時の粘度上昇が小さく、低温作業性が良く、且つ 酸性亜硫酸塩等の安定剤を用いなくとも、改善された保存性を有する、一液タイプの水性エマルジョン型接着剤を提供することを目的とする。 - 特許庁

To provide a urethane emulsion having excellent film-forming property while keeping good strength (breaking strength and yield strength), elastic modulus, scratch resistance and surface hardness in the case of using as a coating film or an adhesive, having excellent adhesiveness to a leather and exhibiting excellent water resistance and workability.例文帳に追加

塗膜や接着剤として用いた場合に、強度（破断強度、降伏強度）、弾性率、耐傷付き性および表面硬さを良好に維持しつつ造膜性に優れ、皮革への密着性を良好に維持しつつ耐水性に優れ、作業性にも優れるウレタンエマルジョンの提供。 - 特許庁

The curable aqueous adhesive is composed of (A) a first liquid containing an aqueous emulsion containing a saponified product of a diacetoneacrylamide-fatty acid vinyl ester copolymer as an emulsifying and dispersing agent and containing a polymer of an ethylenic unsaturated monomer as a dispersoid and (B) a second liquid composed of an aqueous liquid containing a trifunctional hydrazide compound.例文帳に追加

ジアセトンアクリルアミド−脂肪酸ビニルエステルの共重合体のケン化物を乳化・分散剤とし、エチレン性不飽和単量体の重合体を分散質とする水性エマルジョンを含有する第１液（Ａ）と、３官能ヒドラジド化合物を含有する水性液からなる第２液（Ｂ）からなる。 - 特許庁

To provide an O/W emulsion composition containing an antifungal agent that is less irritating to the skin owing to substantially no incorporation of surfactants and is assumed to retain manifestation of medicinal effects of the antifungal agent owing to high adhesive retention of the antifungal agent such as miconazol nitrate or the like.例文帳に追加

実質的に界面活性剤を配合していないため皮膚への刺激がより少なく、硝酸ミコナゾール等の抗真菌剤の付着滞留性が高いため、抗真菌剤の薬効の発現が持続すると考えられる抗真菌剤含有Ｏ／Ｗエマルション組成物を提供する。 - 特許庁

The interlayer adhesive contains a resin composition obtained by reacting (a) a base agent made of an emulsion of a main resin that comprises one or more resins selected from an acrylic resin, an ethylene-vinyl acetate resin and an epoxy-based resin, with (b) an isocyanate compound having an isocyanate group.例文帳に追加

この層間接着剤は、（ａ）アクリル系樹脂、エチレン−酢酸ビニル系樹脂、およびエポキシ系樹脂から選ばれた１または２種以上からなる主樹脂のエマルションからなる主剤と、（ｂ）イソシアネート基を有するイソシアネート化合物と、を反応させて得られた樹脂組成物が含有されている。 - 特許庁

This synthetic leather is given by forming a foamed acrylic resin emulsion layer 2 on the raised surface 11 of a single-sided raised fabric 1, forming a foamed polyurethane layer 3 on the non-raised surface 12 of the raised fabric through an adhesive layer 31, and further forming a polyurethane top layer 4 on the foamed polyurethane layer 3.例文帳に追加

片面起毛布１の起毛面１１に発泡アクリル系樹脂エマルジョン層２が設けられ、該起毛布の非起毛面１２に発泡ポリウレタン層３が接着剤層３１を介して設けられ、該発泡ポリウレタン層３上にポリウレタン表皮層４が設けられている。 - 特許庁

The emulsion self-adhesive contains 100 parts by mass of a rubber mixture prepared by mixing natural rubber and synthetic rubber in ratios of 10:90 to 90:10, 50 to 150 parts by mass of a tackifier resin, and 0.1 to 5 parts by mass of a water-soluble polymer thickener, in total by 30 to 60 mass% calculated as a solid content.例文帳に追加

天然ゴムと合成ゴムを１０：９０〜９０：１０の割合で混合したゴム混合物１００質量部と、粘着付与樹脂５０〜１５０質量部と、水溶性高分子増粘剤０．１〜５質量部とを、固形分換算で３０〜６０質量％有するエマルジョン型粘着剤。 - 特許庁

In a method of manufacturing a polishing sheet, after the planarity is improved by surface processing the reverse surface of the hook-and-loop fastener, emulsion liquid obtained by mixing a fine-powder abrasive, adhesive, and water is applied on the reverse surface that has been surface processed.例文帳に追加

この発明は、面ファスナーの裏面を表面処理して平面性を向上させた後、前記表面処理した裏面に、微粉研磨材と接着剤と水とを混合して得たエマルジョン液を塗布することを特徴とした研磨シートの製造方法により目的を達成した。 - 特許庁

To provide an aqueous emulsion adhesive for an information-supporting seat capable of laminating with such a force as a folding force without applying any heat or high pressure, being excellent in re-peeling property, and capable of being peeled without a set-off of printed matters.例文帳に追加

情報担持シート用の水性エマルション接着剤であって、熱や大きな圧力を加えることなく、折り畳む程度の力での貼り合わせが可能であり、さらに、再剥離性にも優れ、剥離の際に印刷物が裏写りしない情報担持シート用の水性エマルション接着剤を提供すること。 - 特許庁

To provide an adhesive composition comprising one or more polymerizable surfactant monomers as a part of an emulsion polymer, well adhering to a wide spectrum of substrates that conventional adhesives have difficulty adhering thereto and having improved low temperature and high temperature performances when compared to conventional PSAs.例文帳に追加

エマルジョンポリマーの一部として１以上の重合性界面活性剤モノマーを含む接着剤組成物は、従来の接着剤が接着困難性を有する広範なスペクトルの基体に良好に結合し、従来のＰＳＡと比較して改良された低温および高温性能を有する。 - 特許庁

The pressure-sensitive adhesive composition comprises an emulsion of a copolymer, and in the copolymer 10-50 wt.%, based on the whole copolymer, of 2-ethylhexyl methacrylate (A) is copolymerized, the copolymer having a glass transition temperature of -25°C or below.例文帳に追加

共重合体エマルジョンを含む感圧接着剤組成物であって、前記共重合体が、共重合体全体に対して１０〜５０重量％の（Ａ）メタクリル酸２−エチルヘキシルが共重合されており、かつ、前記共重合体のガラス転移温度が−２５℃以下である感圧性接着剤組成物。 - 特許庁

A water color ink accepting layer forming agent is formed by dissolving a water soluble polycation in a water-based medium of a weakly acidic water emulsion type acrylic self-adhesive obtained through a copolymerization between one or more kinds of (meth)acrylates with a 4-12C alkyl group and a vinyl base monomer.例文帳に追加

水性インク受容層形成剤は、炭素数４〜１２のアルキル基を有する１種又は2種以上の（メタ）アクリル酸エステルとビニル系モノマーとを共重合させて得られる弱酸性の水性エマルジョン型アクリル系粘着剤の水性媒体中に水溶性ポリカチオンを溶解させたものである。 - 特許庁